Abstract:In this paper, the main purpose was to investigate the effects of laser peening (LP) on the microstructural evolution and frictional wear resistance of TC6 titanium alloy. The surface topographic features, microhardness and residual stress distribution in the depth direction of differently treated specimens were measured using three-dimensional topography instrument, digital microhardness tester and residual stress instrument. The frictional wear test was carried out using a multifunctional friction wear tester. Meanwhile, X-ray diffraction (XRD), optical microscope (OM) and transmission electron microscopy (TEM) were utilized to investigate the effects of LP on the microstructural response of TC6 titanium alloy. The results indicated that the micro-pits induced by LP increased the surface roughness to a maximum of 6.94 μm. LP technique effectively improved the microhardness and frictional wear resistance of TC6 titanium alloy, and the wear form changed from abrasive wear, adhesive wear and fatigue spalling wear to abrasive wear at the laser energy of 8 J. Compared to the untreated specimens, the surface microhardness of the specimens treated by LP with 8 J increased from 356 HV to 442 HV, and the affected layer depth was approximately 500 μm. Moreover, the friction coefficient decreased from 1.2 to 0.5, the abrasion depth of the abrasion track was reduced by approximately 32 % compared to the untreated specimen. Additionally, the surface compressive residual stress induced by LP with 8 J reached about −510 MPa. The microstructural evolution of the specimens processed by LP was dominated by twin formation and dislocation slip, while the intercalation between multidirectional twins and the formation of sub-grain boundaries promoted grain refinement of TC6 titanium alloy. Refined grains, high density of dislocations, mechanical twins and the implantation of compressive residual stresses effectively improved the friction and wear resistance of TC6 titanium alloy.

Effects on structure and mechanical properties of TC11 titanium alloy by laser shock peening

Microstructure evolution and mechanical properties of a lamellar near-α titanium alloy treated by laser shock peening

Microstructural response and surface mechanical properties of TC6 titanium alloy subjected to laser peening with different laser energy

On the Microstructure, Residual Stress and Fatigue Performance of Laser Metal Deposited TC17 Alloy Subjected to Laser Shock Peening

Plastic deformation behavior of titanium alloy by warm laser shock peening: Microstructure evolution and mechanical properties

Laser shock peened Ti-6Al-4 V alloy: Experiments and modeling

Effects of Laser Shock Peening on Microstructure and Properties of Ti–6Al–4V Titanium Alloy Fabricated via Selective Laser Melting

Molecular dynamics simulation of microstructural evolution and mechanical behavior of titanium alloy subjected to laser shock peening

Surface residual stress, micro-hardness and geometry of TC6 titanium alloy thin-wall parts processed by multiple oblique laser shock peening

Effect of Laser Shock Peening on Residual Stress, Microstructure and Hot Corrosion Behavior of Damage-Tolerant TC21 Titanium Alloy

Experimental and Numerical Studies of Fatigue Behavior of Ti6Al4V Alloy Treated by Laser Shock Peening

Effect of laser shock peening without protective coating on surface integrity of titanium-based carbon-fibre/epoxy laminates

Mechanical properties and strengthening mechanisms of Ti-6Al-4V treated by electro-pulsing assisted laser shock peening

Microstructural evolution and mechanical behaviors of Al-Cu-Li alloy processed by laser shock peening

High temperature wear performance of Ti–6.5Al–3.5Mo–1.5Zr–0.3Si alloy subjected to laser shock peening

Gradient microstructure and foreign-object-damaged fatigue properties of Ti6Al4V titanium alloy processed by the laser shock peening and subsequent shot peening

Effects of laser shock peening on the hot corrosion behaviour of the selective laser melted Ti6Al4V titanium alloy

Effects of Ultrasonic Shot Peening on Fatigue Behavior of TA15 Titanium Alloy Fabricated by Laser Melting Deposition

Strain rate dependence of tensile properties and strengthening mechanism of Ti6Al4V alloy undergoing different coverage layers of laser shock peening

Achieving high strength and ductility in selective laser melting Ti-6Al-4V alloy by laser shock peening

Laser shock peening induced mechanical properties enhancement of 50CrVA alloy