Tensile Yield Behavior and Precipitation Strengthening Mechanism in Super304H Steel

P. Ou,H. Xing,X. L. Wang,J. Sun
DOI: https://doi.org/10.1016/j.msea.2014.01.085
IF: 6.044
2014-01-01
Materials Science and Engineering A
Abstract:Tensile yield behaviors of the solution- and aging-treated Super304H austenitic steel have been investigated at temperatures from 300 to 923 K. The results showed that the contribution to yield stress from precipitation strengthening of Cu-rich phases is 17–23%. The higher thermal activation volume and energy imply an interaction between dislocation and Cu-rich precipitates. The precipitation strengthening mainly arises from coherency strain and partially from stacking fault strengthening. The calculated shear stress from precipitation strengthening agrees reasonably with the experimental result.