Abstract:Double‐layer thermal barrier coatings are one of the development directions of thermal barrier coatings technology. LaYbZr2O7 (LYZO) has high toughness and low thermal conductivity, making it promising for use as a high‐temperature thermal barrier coating. However, its relatively poor mechanical properties, especially low fracture toughness, limit its further application. Therefore, we prepared a double‐layer coating of LYZO and Y2O3 partially stabilized ZrO2 (YSZ) using atmospheric plasma spraying, with the inner layer being YSZ and the outer layer being LYZO. The results showed that after spraying, LYZO was in the metastable fluorite phase, while YSZ was in the tetragonal phase. LYZO and YSZ had good chemical compatibility, and an interaction layer formed at the interface between them, with its thickness increasing with the sintering time. Eventually, after 100 h of heat treatment, the thickness reached 12 µm. The hardness of the LYZO/YSZ interface increased with the sintering time, reaching a maximum value after sintering at 1300°C for 10 h. When evaluating the interfacial bonding strength using indentation method, the length of cracks caused by indentation significantly decreased with the increase of sintering time. The increase in bonding strength can be attributed to the formation of a reaction layer and the reduction of thermal residual stresses. Raman spectroscopy was used to measure the thermal residual strain at the LYZO/YSZ interface. Unbalanced distribution of thermal residual stress and M phase was observed near the interface. As the sintering time increased, both thermal residual stress and M phase content decreased. In summary, the double‐layer thermal barrier coating of LYZO/YSZ has good potential for development.

Thermal conductivity and mechanical properties of YSZ/LaPO 4 composites

Microstructure and Thermal Properties of a Promising Thermal Barrier Coating: YTaO4

The Microstructure and Property Evolution of LaYbZr2O7 Thermal Barrier Coatings

Structure-property Relationship and Design of Plasma-Sprayed La2Ce2O7/8YSZ Composite Coatings for Gas Turbine Blades

Effective Blocking of Radiative Thermal Conductivity in La2Zr2O7/LaPO4 Composites for High Temperature Thermal Insulation Applications

Aging Properties of Yttria-Stabilized Zirconia Ceramics

Assessment of the Performance of Y2SiO5-YSZ/YSZ Double-Layered Thermal Barrier Coatings

Investigation on the phase stability, sintering and thermal conductivity of Sc2O3–Y2O3–ZrO2 for thermal barrier coating application

High-Temperature Aging Of Plasma Sprayed Quasi-Eutectoid Laybzr2o7-Part I: Phase Evolution

Thermal Cycling Performance of La2Ce2O7/50 Vol.% YSZ Composite Thermal Barrier Coating with CMAS Corrosion

Influence of Powder States on the Composition and Phase Stability of LZ/YSZ Composite Thermal Barrier Coatings

Oxygen‐vacancy‐mediated microstructure and thermophysical properties in Zr 3 Ln 4 O 12 for high‐temperature applications

Thermochemical compatibility between La2(Ce1-xZrx)2O7 and 4 mol% Y2O3 stabilized zirconia after high temperature heat treatment

High Temperature Mechanical Properties of Zirconia Metastable T '-Phase Degraded Yttria Stabilized Zirconia

High‐temperature thermal conductivity measurement of porous ceramic coatings with a high heat flux CO2 laser rig

Thermal Stability of Plasma-Sprayed La2Ce2O7/YSZ Composite Coating

High‐Temperature Aging of Plasma Sprayed Quasi‐Eutectoid LaYbZr2O7–Part II: Microstructure & Thermal Conductivity

Mechanical Properties Durability of Sc2O3-Y2O3 Co-Stabilized ZrO2 Thermal Barrier Materials for High Temperature Application

Microstructural and Mechanical Property Evolutions of Plasma-Sprayed YSZ Coating During High-Temperature Exposure: Comparison Study Between 8YSZ and 20YSZ

Preparation and Phase Stability of La_2O_3, Y_2O_3 Co-doped ZrO_2 Ceramic Powder Application for Thermal Barrier Coating

Influence of ytterbium- and samarium-oxides codoping on structure and thermal conductivity of zirconate ceramics