Relation Between Reactivity and Electronic Structure for Α′l-, Β- and Γ-Dicalcium Silicate: A First-Principles Study

Qianqian Wang,Feng Li,Xiaodong Shen,Wujun Shi,Xuerun Li,Yanhua Guo,Shijie Xiong,Qing Zhu

DOI: https://doi.org/10.1016/j.cemconres.2013.12.004

IF: 11.958

2014-01-01

Cement and Concrete Research

Abstract:The effect of the electronic structures of α′L-, β-, and γ-dicalcium silicate (α′L-, β- and γ-C2S, C=CaO, S=SiO2) on hydration reactivity have been investigated by first-principles calculations. Active O atoms with larger charge densities are found in α′L- and β-C2S, while they are absent in γ-C2S. The local density of states of valence band maximum in α′L- and β-C2S is highly localized around active O atoms, whereas that in γ-C2S is homogeneously dispersed. For the active O-2p orbital in α′L- and β-C2S, the highest orbital energy in the partial density of states is about 0.31eV higher than that of the inactive O in γ-C2S. These differences make the active O atoms of α′L- and β-C2S more susceptible to electrophilic attack and result in higher hydration reactivity for α′L- and β-C2S.