Facile fabrication of cordierite-based porous ceramics with magnetic properties
Hao Li,Cuiwei Li,Huaiming Jia,Guangjin Chen,Siyuan Li,Kepi Chen,Chang-An Wang,Liang Qiao
DOI: https://doi.org/10.1007/s40145-022-0631-1
IF: 11.534
2022-09-03
Journal of Advanced Ceramics
Abstract:In this paper, cordierite-based porous ceramics with magnetic properties have been firstly in-situ synthesized by using MgO, Al 2 O 3 , and SiO 2 powders as raw materials and Fe 3 O 4 as a functional additive. Combining with the foam freeze casting method, near net size fabrication (total linear shrinkage < 2.86%) of the magnetic porous materials was realized by adjusting the amount of Fe 3 O 4 . The porosity, compressive strength, and saturation magnetization of the prepared materials were 83.9%–87.8%, 1.51–2.65 MPa, and 1.2–5.8 emu/g, respectively. The phase composition and microstructure evolutions during sintering were investigated briefly. The results showed that the synthesis temperature of cordierite was lowered about 100 °C due to the addition of Fe 3 O 4 . Except for the main phase-cordierite, Mg—Al—Fe spinel and α-Fe 2 O 3 also existed in the final materials. The lattice parameters of the Mg—Al—Fe spinel and the amount of α-Fe 2 O 3 changed obviously with the change in the sintering temperature and Fe 3 O 4 amount, which mainly influenced the magnetic properties of the prepared materials. Thus, a facile fabrication method of the cordierite-based porous ceramics with the magnetic properties has been put forward in this paper.
materials science, ceramics