Effect of MgO/La2O3 Co-Doping on the Microstructure, Transmittance and Microwave Dielectric Properties of Translucent Polycrystalline Alumina

Liu Yuan,Huijun Wang,Huixing Lin,Wei Li,Xiaowei Li,Jianlin Shi

DOI: https://doi.org/10.1016/j.ceramint.2013.07.125

IF: 5.532

2014-01-01

Ceramics International

Abstract:In this paper, a systematic experimental design is used to study the influence of different content ratios of MgO/La2O3 co-doping on the microstructure, real inline transmittance (RIT) and microwave dielectric properties of translucent polycrystalline alumina (PCA). Compared with those doped only with MgO, translucent PCA co-doped with different ratios of MgO/La2O3 demonstrates a higher and more stable Q×f value. The increased solubility of La in alumina and the elimination of the second phase are possible reasons for the decrease in dielectric loss. An optimized Q×f value of~300,000GHz could be attained for samples co-doped with 1500ppm MgO/300ppm La2O3. Besides, a high RIT of~30% at a wavelength of 600nm could be achieved when 500ppm MgO/500ppm La2O3 was co-doped, the reasons for these phenomena are also discussed in the paper.