Effects of Li2co3 and Sm2o3 Additives on Low-Temperature Sintering and Piezoelectric Properties of Pzn-Pzt Ceramics

G. F. Fan,M. B. Shi,W. Z. Lu,Y. Q. Wang,Fei Liang
DOI: https://doi.org/10.1016/j.jeurceramsoc.2013.07.028
IF: 5.7
2014-01-01
Journal of the European Ceramic Society
Abstract:To assist the development of applications for multilayer piezoelectric devices, the low-temperature sintering piezoelectric ceramics of 0.3Pb(Zn1/3Nb2/3)O3-0.7Pb(Zr0.49Ti0.51)O3 with Li2CO3 and Sm2O3 additives were fabricated by a conventional solid-state reaction, and their structural and piezoelectric properties were studied. With the addition of Li2CO3, the minimum sintering temperature of 0.3Pb(Zn1/3Nb2/3)O3-0.7Pb(Zr0.49Ti0.51)O3 piezoelectric ceramics was reduced from 1125°C to 950°C through the formation of a liquid phase and its piezoelectric properties showed almost no degradation. When the sintering temperature was below 950°C, however, the piezoelectric properties degraded obviously. The additional Sm2O3 resulted in a significant improvement in the piezoelectric properties of 0.3Pb(Zn1/3Nb2/3)O3-0.7Pb(Zr0.49Ti0.51)O3 ceramic with added Li2CO3. When sintered at 900°C, the optimized properties of the 0.3Pb(Zn1/3Nb2/3)O3-0.7Pb(Zr0.49Ti0.51)O3 piezoelectric ceramic with 0.3wt% Li2CO3 and 0.3wt% Sm2O3 were obtained as d33=483pC/N, k31=0.376, Qm=73, ɛr=2524, tanδ=0.0178.
What problem does this paper attempt to address?