Abstract:Carbon fiber reinforced silicon carbide matrix composites (C/SiC) have emerged as key materials for thermal protection systems owing to their high strength-to-weight ratio, high-temperature durability, resistance to oxidation, and outstanding reliability. However, manufacturing defects deteriorate the mechanical response of these composites under extreme thermal-force coupling conditions, prompting significant research attention. This study demonstrates a customized in situ loading device compatible with synchrotron radiation facilities, enabling high spatial and temporal resolution recording of internal material damage evolution and failure behavior under thermal-force coupling conditions. Infrared thermal radiation units in a confocal configuration were used to create ultra-high-temperature environments, offering advantages of compactness, rapid heating, and versatility. In situ tensile tests were conducted on C/SiC samples in a nitrogen atmosphere at both room temperature and 1200 °C. The high-resolution image data demonstrate various failure phenomena, such as matrix cracking and pore linkage. Image-based finite element simulations indicate that the temperature-dependent variation of the failure mechanism is attributable to thermal residual stresses and defect-induced stress concentrations. This work seamlessly integrates extreme mechanical testing methods with in situ observation techniques, providing a comprehensive solution for accurately quantifying crack initiation, pore connection, and failure behavior of C/SiC composites.

Inspection on SiC coated carbon–carbon composite with subsurface defects using pulsed thermography

Experimental Study of Inspection on SiC Coated High-Temperature Alloy Plates with Defects Using Pulsed Thermographic Technique

The study of inspection on SiC coated carbon-carbon composite with subsurface defects by lock-in thermography

Investigation on Coating Uniformity of High-Temperature Alloy with SiC Thermal Barrier Coating Using Pulsed Infrared Thermographic Technique

Detection on the Coating Peeling of SiC Coated C/C Composites Using Infrared Thermal-Wave Tomography

Inspection on CFRP Sheet with Subsurface Defects Using Pulsed Thermographic Technique

Investigation of the bulging mechanism of C/SiC coating through in situ optical observation and numerical simulation

Detecting of defects in heat-resistant alloy coating structure plates using pulsed infrared thermography

In Situ X-ray Imaging and Numerical Modeling of Damage Accumulation in C/SiC Composites at Temperatures Up to 1200 ℃

Evaluation of subsurface defect based on pulsed eddy current thermography

Numerical Analysis of Heat Transfer Process in Pulsed Thermography Detection on Electrical Ceramic Materials

In Situ Detection of Damage in the SiC<sub>f</sub>/Ti6242 Composite During the Thermomechanical Fatigue Test

Pulsed Infrared Thermography to Inspect the Internal Defects of Composite Insulators

Finite Element Simulation Analysis of Infrared Thermal Wave Detection on Composite Insulators

Synthesis of SiC Coatings and Evaluation of Their Emissivity

Experimental study on active infrared thermography as a NDI tool for carbon-carbon composites

Quantitative Characterization of Interfacial Defects in Thermal Barrier Coatings by Long Pulse Thermography

A new method to evaluate the subsurface defect by thermal nondestructive testing

Synchronous Full-Field Measurement of Temperature and Deformation of C/SiC Composite Subjected to Flame Heating at High Temperature

Experimental research on surface defect based on pulsed eddy current thermography

Experimental study on infrared phase-locked thermal imaging inspection of carbon fiber reinforced polymer laminates