Abstract:Two novel low-firing microwave dielectric ceramics ACa(2)Mg(2)V(3)O(12) (A=Li, K) were prepared using the solid state reaction method. The phase composition, sintering behavior, and microwave dielectric properties were investigated. X-ray diffraction (XRD) analysis showed that both ceramics crystallized into a cubic garnet structure. Both ceramics were well densified at temperatures lower than 960 degrees C. LiCa2Mg2V3O12 ceramic sintered at 940 degrees C with relative density of similar to 96.3% obtained the optimum microwave dielectric properties with epsilon(r) similar to 9.8, Qxf similar to 24,900 GHz (at 11.0 GHz), tau(f) similar to+259.2 ppm/degrees C. For KCa2Mg2V3O12, the ceramic sintered at 900 degrees C had a relative density of similar to 96.1%, a relative permittivity (epsilon(r)) similar to 10, a quality factor (Qxf) similar to 30,330 GHz and a large positive temperature coefficient of resonance frequency tau(f) similar to+190.9 ppm/degrees C. Both ACa(2)Mg(2)V(3)O(12) (A=Li, K) ceramics were chemically compatible with Ag electrodes. The large positive tau(f) of LiCa2Mg2V3O12 ceramic could be compensated by forming sold solution with NaCa2Mg2V3O12, and improved properties with a near-zero tau(f)= +2 ppm/degrees C, epsilon(r)=9.9, Qxf=45,500 GHz was obtained for 0.16Lica(2)Mg(2)V(3)O(12)-0.84NaCa(2)Mg(2)V(3)O(12) ceramic sintered at 920 degrees C for 4 h. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Novel Low‐Firing Microwave Dielectric Ceramic LiCa3MgV3O12 with Low Dielectric Loss

LiCa3ZnV3O12: A Novel Low-Firing, High Q Microwave Dielectric Ceramic

Low-Temperature Firing And Microwave Dielectric Properties Of Ca[(Li0.33nb0.67)(0.9)Ti-0.1]O3-Delta Ceramics With Lif Addition

A novel low firing microwave dielectric ceramic NaCa2Mg 2V3O12

A Novel Thermally Stable Low-Firing Limg4v3o12 Ceramic: Sintering Characteristic, Crystal Structure and Microwave Dielectric Properties

Microwave dielectric properties of novel glass-free low temperature firing ACa2Mg2V3O12 (A=Li, K) ceramics

A Novel Low‐Firing and Low Loss Microwave Dielectric Ceramic Li2Mg2W2O9 with Corundum Structure

A New Microwave Ceramic with Low-Permittivity for Ltcc Applications

A low-firing Ca5Ni4(VO4)6 ceramic with tunable microwave dielectric properties and chemical compatibility with Ag

A Novel Low-Firing Microwave Dielectric Ceramic Li 2 ZnGe 3 O 8 with Cubic Spinel Structure

Microwave Dielectric Properties of Low-Fired Li2TiO3–MgO Ceramics for LTCC Applications

A new low-loss microwave dielectric ceramic for low temperature cofired ceramic applications

Li4Mg3Ti2O9: A novel low-loss microwave dielectric ceramic for LTCC applications

A novel high-Q oxyfluoride Li4Mg2NbO6F microwave dielectric ceramic with low sintering temperature

Ultra-Low Loss Microwave Dielectric Ceramic Li 2 Mg 2 TiO 5 and Low-Temperature Firing Via B 2 O 3 Addition

Microwave Dielectric Properties of Na+-substituted CaMg0.9Li0.2Si2O6 Ceramics

Series of Thermally Stable Li1+2xMg4−xV3O12 Ceramics: Low Temperature Sintering Characteristic, Crystal Structure and Microwave Dielectric Properties

Microwave Dielectric Properties of the Low-Temperature-fired Li2ZnTi3O8–Li2TiO3 Ceramics for LTCC Applications

Temperature Stable and High-Q Microwave Dielectric Ceramics in the Li2Mg3−Ca TiO6 System (X=0.00–0.18)

Temperature Stable Microwave Dielectric Ceramics in LiCa 3− X Sr X MgV 3 O 12 Ceramics

A Novel Tungstate Li3Nd3W2O12 with Garnet Structure for Low-Temperature Cofired Ceramic Technology