Effect of adding method of Cr on microstructure and properties of WC-9Ni-2Cr cemented carbides

Kaihua Shi,Kechao Zhou,Zhiyou Li,Xiuqi Zan,ShangZhi Xu,ZhaoYu Min
DOI: https://doi.org/10.1016/j.ijrmhm.2012.11.010
IF: 4.804
2013-01-01
International Journal of Refractory Metals and Hard Materials
Abstract:The WC–9Ni–2Cr cemented carbides were prepared by ball milling method and low pressure sintering. The microstructure and properties of the cemented carbides were then investigated using scanning electron microscopy, mechanical property tester and immersion corrosion tests. The results showed that the adding method of Cr significantly influenced the microstructure and properties of the WC–9Ni–2Cr cemented carbides. Cemented carbides with Cr added in the form of chromium carbide (Cr3C2) were characterized by carburizing and showed a relative lower density, while the addition of metallic chromium and nichrome (Ni–18Cr) resulted in the formation of (W,Cr)C phase and a decrease in the bending strength. However, no defects were found in the microstructure of the cemented carbides in which Cr was added via Cr–Cr3C2 composite powder. Furthermore, cemented carbides prepared with nichrome powder and metallic Cr powder exhibited a higher immersion corrosion resistance in neutral tap water after soaking six times according to BS:6920:2000.
What problem does this paper attempt to address?