The Influence of Various Ag Additions on the Nucleation and Thermal Stability of Ω Phase in Al–Cu–Mg Alloys

Xuanwei Zhou,Zhiyi Liu,Song Bai,Meng Liu,Puyou Ying

DOI: https://doi.org/10.1016/j.msea.2012.11.081

2013-01-01

Abstract:The effect of the bulk Ag content ranging from 0.14 to 0.57wt% on the aging hardening response and microstructures of Al–Cu–Mg alloys was investigated in the present study. The strong dependence of the hardening response on the bulk Ag content was obtained as the hardening response at 165°C was accelerated by increasing Ag content. The highest hardening response was observed in the alloy containing 0.57wt% Ag, whereas the least one was obtained in the alloy containing 0.14wt% Ag. The tensile testing at various temperatures also revealed a similar trend. Based on the TEM study on peak aging conditions at 165°C, it was found that the competitive precipitation kinetics between Ω and θ′ phases was sensitive to the variation of Ag content. The dense precipitation of the Ω plates promoted by increasing Ag content was responsible for the increasing hardening response. Meanwhile, the formation of θ′ phase was greatly suppressed. Subsequent long term aging at 200°C for 500h following the peak aging treatment further suggested that the thermal stability of the Ω plates was enhanced with increasing Ag as the presence of the Ω plates could be clearly confirmed in 0.57wt% Ag alloy but was hard to distinguish in the alloy containing 0.14wt% Ag.