Effects of Aging Temperature on the Mechanical Properties and Precipitation Behavior of a Pre-strained Al–Cu–Mg–Ag Alloy
Jian Wang,Jingpei Xie,Zhiyi Liu,Aiqin Wang,Wenyan Wang
DOI: https://doi.org/10.1007/s12540-022-01229-1
IF: 3.451
2022-06-09
Metals and Materials International
Abstract:In this work, effects of artificial aging temperature on the mechanical properties and precipitation behavior of a pre-strained Al–Cu–Mg–Ag alloy were investigated by hardness and tensile tests, and quantitative transmission electron microscope analysis. Three aging conditions, a single aging at a high temperature (T8H), a single aging at a low temperature (T8L) and an interrupted aging at low temperature following under-aging at a higher temperature (T8I4), were compared. Based on the quantitative analysis of the strengthening phases, the evolution law of the average diameter, thickness and volume fraction of Ω plates with the aging time for a pre-stretched Al–Cu–Mg–Ag alloy aged at 190 °C/160 °C may be predicted by the modified equations. The precipitation behavior of Ω precipitates was confirmed by considering the coarsening kinetics of them. Results show that a higher aging temperature can increase the precipitation kinetics of Ω phase and inhibit the precipitation of θ′ phase. Thus, a new type of interrupted aging treatment, T8I4 (3.2% pre-stretch + 190 °C/1 h + 160 °C/10 h), was proposed to enhance the strength of the pre-stretched Al–Cu–Mg–Ag alloy. Graphical
materials science, multidisciplinary,metallurgy & metallurgical engineering