Abstract:Investment and suction casting (ISC) represents an economic and promising process route to fabricate automotive exhaust valves of γ-TiAl based alloys, but information available on the metal flow and the temperature changes during mould filling and solidification process for the ISC process is meager. A sequentially coupled mathematical flow-thermal model, based on the commercial finite-volume/finite-difference code FLOW-3D and the finite-element code PROCAST, has been developed to investigate the ISC process. In term of calculating the flow and temperature fields during the filling and solidification stages, potential defects including the gas bubbles and the surface air entrainment occurred in the mould filling process and the shrinkage porosities formed in the solidification process are predicted and the reasons for the formation of these defects are also analyzed. The effects of filling pressure difference control methods and moulds on gas bubble and surface air entrainment behavior are presented. It is found that by changing the filling pressure difference control methods from general suction casting to “air leakage” suction casting and reducing air leakage flow rates, the gas bubbles are eliminated effectively, and the surface air entrainment attenuate dramatically. With resort to a mould with a tetragonal runner, the surface air entrainment decrease to the lowest level. Finally, the water analogue and suction casting experiments of exhaust valves are implemented for further validation of the simulation results.

Water Analogue Experimental Study on the Filling Process of A Steam Turbine Housing Casting

Simulation and Experimental Analysis on Non-circular Cross-section Parts Residual Wall Thickness of Water-assisted Injection Molding

Observation of the Mold-Filling Process of a Large Hydro-Turbine Guide Vane Casting

ANALYSIS OF LOAD CHARACTERISTICS AND CONTROL OF WATER HYDRAULIC SYSTEM FOR WAIM

Water Analogue Validation of Numerical Model for Fluid Flow During Slow Shot Phase in Die Casting Process

Effect on Residual Wall Thickness of Parts with Floating Core Injection of Water-Assisted Injection Molding

Measurement and observation of the filling process of steel castings

Application of Transparent Casting Moulds Prepared by Additive Manufacturing Technology in Hydraulic Simulation

Study and Application of Mold Filling Simulation of Shaped Castings

Direct Observation of Filling Process and Porosity Prediction in High Pressure Die Casting

Study on Numerical Simulation of Mold Filling and Heat Transfer in Die Casting Process

Research on Casting Process for Embedded Internal Flow Passage Mould

Determination of casting parameters of thick wall die-casting of magnesium alloy and simulation of its processing

An Improved Mathematical Model to Simulate Mold Filling Process in High Pressure Die Casting Using CLSVOF Method and CSF Model

Experimental Study on the Filling Process of the Lost Foam Casting Process of a Cast Iron Plate

Study and Application of Cae Simulation in Die-Casting Die Design

Study of Mold Filling Simulation on Low Pressure Die Casting for Automobile Wheel Casting

Studies on formation of shrinkage cavity and porosity of steel castings by taking filling process into account

Numerical simulation and experimental verification of the initial temperature distribution of castings during mold filling process

Numerical Simulation of Fluid Flow and Heat Transfer During Mold Filling for Die Casting

Modeling of filling and solidification process for TiAl exhaust valves during suction casting