Tribological Properties of Self-Lubricating Polymer–Steel Laminated Composites

Dong-Ya Zhang,Peng-Bo Zhang,Ping Lin,Guang-Neng Dong,Qun-Feng Zeng

DOI: https://doi.org/10.1080/10402004.2013.805348

IF: 2.056

2013-01-01

Tribology Transactions

Abstract:Self-lubricating polymer-steel laminated composites (SLC) consisting of matrix zones and filled zones were fabricated by a laminating-bonding process. The matrix zones were silicon steel sheets and the filled zones were polymer matrix filled with MoS2 and graphite, respectively. The control specimen was prepared by spraying a polymer composite coating on a GCr15 disc. The tribological properties of SLC were investigated using a ball-on-disc tribometer under different loads and frequencies. Compared to the control specimen, the friction coefficient and wear rate of SLC was reduced by 57% and threefold at 4N and 6Hz, respectively. In addition, the friction coefficient of SLC was low and stable under low reciprocating frequency, and it was high and fluctuating under high reciprocating frequency. In addition, the wear rate increased with increasing applied load and reciprocating frequency. Scanning electron microscopy (SEM) images show that the lubricating mechanism of SLC was that solid lubricants embedded in filled zones expanded and smeared a layer of transfer film on the sliding path to lubricate the surface. The thermal expansion of solid lubricants was simulated using ANSYS software with thermal-stress coupling. The simulation results showed the maximum temperature of the filled zones was 130 degrees C, and the maximum normal displacement of solid lubricants was approximately 10m. This confirmed that the solid lubricants expanded effectively by the aid of frictional heat.