Tb4o7-Tio2 Mixture Powders Prepared by High Energy Ball Milling
Wang Ke,Liu Tengjiao,Ran Guang,Luo Yong,Lu Junqiang,Li Ning,Wang Lumin
2016-01-01
Rare Metal Materials and Engineering
Abstract:The nanocrystalline powders of Tb4O7-18wt%TiO2 were prepared by high energy ball milling. Systematical investigations were carried out on microstructure, particle and grain size, lattice distortion and morphology of the Tb4O7-18wt%TiO2 milled powders using laser particle analyzer, X-ray diffraction, transmission electron microscopy and scanning electron microscopy. The results show that the nanocrystalline and nanoparticle powders are synthesized and microstructure is homogeneous after high energy ball milling. With the increase of ball milling time, the diffraction peaks of Tb4O7 phase are broadened gradually and move to large angles. Meanwhile, the diffraction peaks of TiO2 phase weaken gradually and disappear after 4 h milling. At the initial stage of ball milling, both particle size and crystalline size decrease significantly, then the sizes decline slowly and tend to be stable at the late stage of ball milling. After 96 h milling, the average particle size and crystalline size are 200 nm and 95 nm, respectively. The lattice distortion is up to 1.35%. The reason of solid solution of TiO2 and nanocrystalline formation and the mechanism of microstructure evolution were also discussed.