Abstract:The structural stability of non-stoichiometric TiB 1.5 was assessed using first principles calculations, followed by synthesis through the mechanical alloying method. Subsequently, TiB 1.5 was combined with other transition metal borides to fabricate high-entropy ceramics (HEB 1.9 ) consisting of multi-component transition metal borides (Ti, Cr, V, Nb, Ta)B 1.9 via spark plasma sintering (SPS). The sintered bodies were prepared at various temperatures ranging from 1700Ā Ā°C to 1900Ā Ā°C and were subjected to characterization. Simulation results indicate that TiB 1.5 exhibits a negative formation energy, signifying its stability. Experimental findings reveal that at relatively low sintering temperatures, the combined influence of temperature and pressure facilitates the diffusion of several other compounds into the TiB 1.5 phase, resulting in the synthesis of a single-phase high-entropy diboride ceramic (HEDC) at 1700Ā Ā°C. As the sintering temperature increases, the Vickers hardness and flexural strength of the sintered body initially increase and subsequently decrease, a trend influenced by both porosity and grain size. Concurrently, fracture toughness exhibits a pattern of decreasing, increasing, and then decreasing again. At a temperature of 1850Ā Ā°C, the single-phase HEDC demonstrates peak values in Vickers hardness (23.28Ā GPa), fracture toughness (5.33Ā MPaĀ m 1/2 ), and flexural strength (681.39Ā MPa).

Synthesis Route and Mechanical Properties of Reactive Hot Pressed TiN–TiB2 Ceramics

In Situ TiBw/Ti–6Al–4V Composites with Novel Reinforcement Architecture Fabricated by Reaction Hot Pressing

Microstructure and Mechanical Properties of TiN–TiB2–hBN Composites Fabricated by Reactive Hot Pressing Using TiN–B Mixture

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

Reactive hot-pressing TiB2/AlN ceramic composites

Reaction Sintering of Machinable TiB2-BN-C Ceramics with In-Situ Formed h-BN Nanostructure

Synthesis and Mechanical Properties of TiB2/Ti2AlN Composites Fabricated by Hot Pressing Sintering

Fabrication of BN-AlN-TiB2 Compound Conductive Ceramics by Self-Propagating High Temperature Synthesis and Hot Isostatic Pressing

Novel (Zr, Ti)B2-(Zr, Ti)C-SiC ceramics via reactive hot pressing

Low-temperature synthesis and mechanical performance analysis of single-phase high-entropy (Ti,Cr,V,Nb,Ta)B 1.9 ceramics

Synthesis and Properties of AlN-SiC-TiB2 Ceramics by SHS-HIP

Microstructural characterization of TiB2–SiC–BN ceramics prepared by hot pressing

Fabrication of AlN-SiC-TiB2 Ceramics by Self-Propagating High Temperature Synthesis and Hot Isostatic Pressing

Reactive sintering behavior and enhanced densification of (Ti,Zr)B2–(Zr,Ti)C composites

Microstructure, Mechanical Properties and Oxidation Behavior of Reactive Hot-Pressed (Zr,Ti)B2-SiC-ZrC Composites

Novel TiC-based ceramic with enhanced mechanical properties by reaction hot-pressing at low temperature

Microstructure and mechanical properties of TiB2–B4C ceramics fabricated by hot-pressing

Influence of TiN addition on densification behavior and mechanical properties of ZrB2 ceramics

Enhanced Mechanical/electrical Properties of in Situ Synthesized SiC-TiB2 Ceramic Composites by Reactive Hot-Pressing Sintering

Hot pressing and microstructural characterization of SiC and TiN added TiB2 ceramics

In situ reaction and solid solution induced hardening in (Ti,Zr)B 2 ‐(Zr,Ti)C composites