Abstract:The Mg-4Zn-0.5Y-0.5Nd alloy was designed and fabricated by conventional casting with subsequent heat treatment to regulate the microstructure and mechanical properties. The microstructure, secondary phase, mechanical properties, and fracture behavior were analyzed to elucidate the influencing mechanism. The results reveal that the as-cast alloy is composed of equiaxed grains with large sizes and discontinuously distributed secondary phases. Moreover, the secondary phase is mainly W-Mg 3 Zn 3 Y 2 , which partly forms the eutectic structure. The solid solution treatment coarsens the equiaxed grains and transforms the secondary phase into near continuous distribution. The Mg 41 Nd 5 phase appears and volume fraction of secondary phase decreases a little. The combining of solid solution and aging treatment increases grain size and volume fraction of secondary phase more or less. Furthermore, the Mg 24 Y 5 phase appears and secondary phases have been changed into semi-continuous distribution. After heat treatment, the average grain size reaches its maximum value of 107.18 μm, and the volume fraction of secondary phase climbs up to 2.73 %. Moreover, the solid solution treatment weakens the crystallographic orientation preference along {0001} but induces diversified crystallographic orientation preference. The heat treatment increases microhardness from 57.2 HV 0.1 of the as-cast state to 70.5 HV 0.1 of the heat-treated state. Comparatively, the solid solution treatment decreases mechanical properties, while the solid solution and aging treatment increase strength and ductility simultaneously. Especially for the ductility, it has been improved by more than 80 %, which is beneficial to the subsequent thermalmechanical processing greatly.

High temperature mechanical properties of Sand-cast Mg-Gd-Y magnesium alloy

High temperature mechanical behavior of low-pressure sand-cast Mg–Gd–Y–Zr magnesium alloy

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Effect of Heat Treatment on Microstructure and Mechanical Properties of Alloy Mg – 10% Gd – 3% Y – 0.6% Zr

Effect of heat treatment on mechanical properties and microstructure evolution of Mg-9.5Gd-4Y-2.2Zn-0.5Zr alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Microstructure and Mechanical Properties of As-Cast and Heat Treated Mg-15Gd-3Y Alloy

Effect of heat treatment on microstructure and mechanical properties of Mg-4Y-1.6Nd-1Sm-0.5Zr alloy

Study on Tensile Behavior at Various Temperatures of the Mg-7Gd-5Y-1Nd-2Zn-0.5Zr Alloy

Homogenization Heat Treatment of Mg-7.68Gd-4.88Y-1.32Nd-0.63Al-0.05Zr Alloy

Effect of Heat Treatment on the Structure and Properties of EW75 Magnesium Alloy Plate

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Microstructure and Elevated-Temperature Tensile Properties of Differential Pressure Sand Cast Mg-4Y-3Nd-0.5Zr Alloy

Regulating microstructure and mechanical properties of the as-cast Mg-4Zn-0.5Y-0.5Nd alloy by heat treatment

Hot Deformation and Processing Map of As-Homogenized Mg–9Gd–3Y–2Zn–0.5Zr Alloy

Effects of heat treatment on mechanical properties of an extruded Mg-4.3Gd-3.2Y-1.2Zn-0.5Zr alloy and establishment of its Hall–Petch relation

A Preliminary Study on the Effects of Aging Temperature on the Microstructure and Mechanical Properties of As-Extruded Mg-12Gd-4Y-1Zn Magnesium Alloy

The effect of T4 and T6 heat treatments for dynamic impact behavior of casting Mg-Gd-based alloys

Effect of the precipitation state on high temperature tensile and creep behaviors of Mg-15Gd alloy

Effect of heat treatments on microstructure and mechanical properties of sand cast Al–2Li–2Cu–0.5Mg–0.2Sc–0.2Zr alloy

Fabrication of magnesium alloy with high strength and heat-resistance by hot extrusion and ageing