Beneficial Reuse of Stainless Steel Slag and Its Heavy Metals Pollution Risk
Xiang-yu ZHANG,Hua ZHANG,Pin-jing HE,Li-ming SHAO,Ru-yi WANG,Rong-huan CHEN
DOI: https://doi.org/10.13198/j.res.2008.04.35.zhangxy.010
2008-01-01
The Research of Environmental Sciences
Abstract:The feasibility of beneficial reuse of two kinds of stainless steel slag,electric arc furnace(EAF) slag and argon oxygen decarburization furnace(AOD) slag,and their pollution properties of heavy metals were studied.The results indicate that the majority of the slags were sized 5 mm.The main elements(mass content1%) in the EAF slag were Ca,Si,Mg,Al,Fe,O,and Cr,existing as Ca_2SiO_4 and Ca_3Mg(SiO_4)_2,while the AOD slag was mainly composed of Ca,Si,Mg, C,and O,and the main minerals were Ca_2SiO_4.The slags were suitable for beneficial reuse.The leaching mass concentrations of all heavy metals except Cr by the leaching test were lower than or close to the detection limit.The leaching mass concentration of Cr was 0.2(mg/L),far lower than the limit values of Identification Standards for Hazardous Wastes(GB5085.3-1996).Most of the heavy metals existed as stable speciation.The availability leaching test results show that Cr could be leached out at the worst scenario,but mainly as the less hazardous Cr(Ⅲ),which was confirmed by the XRD analysis results.Therefore,the pollution risks of the heavy metals in the stainless steel slags were low.