Abstract:The Mg-4Zn-0.5Y-0.5Nd alloy was designed and fabricated by conventional casting with subsequent heat treatment to regulate the microstructure and mechanical properties. The microstructure, secondary phase, mechanical properties, and fracture behavior were analyzed to elucidate the influencing mechanism. The results reveal that the as-cast alloy is composed of equiaxed grains with large sizes and discontinuously distributed secondary phases. Moreover, the secondary phase is mainly W-Mg 3 Zn 3 Y 2 , which partly forms the eutectic structure. The solid solution treatment coarsens the equiaxed grains and transforms the secondary phase into near continuous distribution. The Mg 41 Nd 5 phase appears and volume fraction of secondary phase decreases a little. The combining of solid solution and aging treatment increases grain size and volume fraction of secondary phase more or less. Furthermore, the Mg 24 Y 5 phase appears and secondary phases have been changed into semi-continuous distribution. After heat treatment, the average grain size reaches its maximum value of 107.18 μm, and the volume fraction of secondary phase climbs up to 2.73 %. Moreover, the solid solution treatment weakens the crystallographic orientation preference along {0001} but induces diversified crystallographic orientation preference. The heat treatment increases microhardness from 57.2 HV 0.1 of the as-cast state to 70.5 HV 0.1 of the heat-treated state. Comparatively, the solid solution treatment decreases mechanical properties, while the solid solution and aging treatment increase strength and ductility simultaneously. Especially for the ductility, it has been improved by more than 80 %, which is beneficial to the subsequent thermalmechanical processing greatly.

Thermal Characteristics of Mg–Zn–Mn Alloys with High Specific Strength and High Thermal Conductivity

Effect of Zn content on microstructure, mechanical properties and thermal conductivity of extruded Mg-Zn-Ca-Mn alloys

Microstructure and thermophysical properties of Mg-2Zn-xCu alloys

Anisotropy of thermal conductivity and mechanical properties in Mg-5Zn-1Mn alloy

Microstructure, Mechanical and Thermal Properties of Mg-0.5Ca-xZr Alloys

Quantitative Study of Microstructure-Dependent Thermal Conductivity in Mg-4Ce-xAl-0.5Mn Alloys

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

The development of low-temperature heat-treatable high-pressure die-cast Al–Mg–Fe–Mn alloys with Zn

Microstructure and Thermal Conductivity of As-Cast and As-Extruded Binary Mg–Mn Alloys

Thermal and electrical conductivity of binary magnesium alloys

Microstructure and Mechanical Properties of Mg–4.5Zn–xNd (x=0, 1 and 2, Wt%) Alloys

The Microstructure, and Mechanical and Corrosion Properties of As-Cast and As-Extruded Mg-2%Zn-x%Cu Alloys After Solution and Aging Heat Treatments

Alloying effect of Mg on microstructure and mechanical properties at 300 °C of Al–5Cu–1Mn–0.5Ni heat-resistant alloy

Recent advancements in thermal conductivity of magnesium alloys

A review on thermal conductivity of magnesium and its alloys

Improving the stretch formability of a heat-treatable magnesium–aluminum–calcium–manganese alloy by copper addition at the parts-per-million-level

Regulating microstructure and mechanical properties of the as-cast Mg-4Zn-0.5Y-0.5Nd alloy by heat treatment

Effect of Extrusion Temperature on the Microstructure and Thermal Conductivity of Mg–2.0Zn–1.0Mn–0.2Ce Alloys

Microstructure and Mechanical Properties of As-Aged Mg-Zn-Sn-Mn-Al Alloys

Effect of Mn Element Addition on the Microstructure, Mechanical Properties, and Corrosion Properties of Mg-3Zn-0.2Ca Alloy