Eu 2+ -activated hexagonal aluminate solid solution phosphors with high quantum efficiency and anti-thermal quenching for pc-LEDs
Yue Han,Mengfang Chen,Xiaochen Hu,Shuzhen Liao,Jiali Tang,Jiayuan Lin,Shixun Lian,Jilin Zhang
DOI: https://doi.org/10.1016/j.cej.2024.157274
IF: 15.1
2024-11-04
Chemical Engineering Journal
Abstract:The luminescence quantum efficiency and thermal stability are important parameters for phosphors when applied in phosphor-converted white light-emitting diodes (pc-LEDs). A facile solid solution strategy was applied to improve the quantum efficiency and thermal stability based on Na-β-Al 2 O 3 :Eu 2+ . Ba 2+ , Mg 2+ , and Ge 4+ are introduced to replace Na + and Al 3+ simultaneously, besides the substitution of Na + by Eu 2+ . X-ray powder diffraction, scanning electron microscopy combining elemental mapping indicate the formation of solid solution from Na-β-Al 2 O 3 :Eu 2+ and BaMgAl 10 O 17 :Eu 2+ . The internal and external quantum efficiencies (IQE, EQE) both increase through solid solution with nearly unchanged blue emission at 468 nm. The IQE and EQE values of nominal Na 1.6- x Ba x Al 11-3 x Mg 2 x Ge x O 17+δ :0.2Eu 2+ ( x = 0.3) are as high as 90.4 % and 68.1 %, respectively. Furthermore, the thermoluminescent curves suggest that the defects decrease by introducing Ba 2+ , Mg 2+ , and Ge 4+ ions. Therefore, the anti-thermal quenching degree decreases, resulting in better thermal stability. The proto-type white pc-LED based on the as-synthesized blue phosphor has a color-rendering index of 87, and nearly unchanged emission profile versus driving currents. The solid-solution phosphors show their potential as blue-emitting component for white pc-LEDs.
engineering, chemical, environmental