Microstructural Evolution And Precipitation Mechanism Of Alpha-Phase In Ti-55531 Alloy Aged At High Temperature

Xue Zhang,Yi Chen,Fengshou Zhang,Junting Yang,Yunjin Lai,Hongchao Kou,Jinshan Li,Lian Zhou

DOI: https://doi.org/10.4028/www.scientific.net/MSF.747-748.912

2013-01-01

Materials Science Forum

Abstract:After two-stage annealing heat treatment process, the near beta-Titanium alloys reveal a mixed microstructure containing lath-like alpha phase and finer acicular alpha phase in beta matrix, leading to the improvement of strength-ductility balance. In this paper, the microstructural evolution and the behaviour of alpha precipitate during high temperature ageing process were investigated by SEM in a near beta-Titanium alloy called Ti-55531. The relationship between alpha precipitates and the beta grain orientation in high temperature was investigated by EBSD. The results show that the alpha-phase precipitated only at some places of the beta grain boundaries at higher ageing temperature (similar to 780 degrees C); the amount of grain boundary alpha increased with the decreased of the ageing temperature; after ageing at 720 degrees C for 45 min, we found that the alpha-phase precipitated not only at grain boundaries but also within the grains. It seems that the precipitation of grain boundary alpha is strongly influenced by beta grain boundary energy which means that grain boundary alpha tends to form preferentially at high energy grain boundaries (high-angle grain boundaries); The alpha-phase precipitates more easily at the grain boundaries where the {110} plane of adjacent beta grains have the same orientation.