NdFeB magnets prepared by spark plasma sintering and hot deformation

Xiaoqiang Li,Zhicheng Chen,Chao Yang,Shengguan Qu

DOI: https://doi.org/10.3969/j.issn.1002-185X.2013.01.040

2013-01-01

Rare Metal Materials and Engineering

Abstract:The effects of sintering temperature (T-sps) on the magnetic properties and density of NdFeB magnets prepared by spark plasma sintering (SPS) from HDDR powders were studied. With increasing the sintering temperature in the range of 650-900 degrees C, the remanence (B-r), intrinsic coercivity (H-cj) and maximum energy product ((BH)(max)) all increased first and then decreased. The optimum magnetic properties of B-r = 0.78 T, H-cj = 577 kA/m and (BH)(max) = 78 kJ/m(3) were obtained in the samples SPSed at 800 degrees C and the density reached 99% of the theoretical. The microstructure, XRD patterns and magnetic properties indicated that the sample (T-sps = 800 degrees C) was anisotropic to a certain degree. But the grain growth was obvious when the T-sps reached 900 degrees C. The SPSed magnet with optimal magnetic properties was subjected to hot deformation at 800 degrees C and an anisotropic magnet was obtained. The hot deformation made the Nd2Fe14B grain orient in such a way that the c-axis of the Nd2Fe14B grain was parallel to the pressing direction. However, the alignment of grains was disrupted by a small amount of abnormal large grains. The magnetic properties parallel to the c-axis of the SPSed + HDed magnet were as follows: B-r = 1.09 T, H-cj = 384 kA/m, and (BH)(max) = 114 kJ/m(3).