Abstract:• Ultra‐light NbC nanowires with a density of 0.23 g/cm3 were prepared using natural bamboo powder as a carbon source, assisted by F ions and catalyzed by iron nickel. • By controlling carbon defects through high‐temperature sintering, the electromagnetic performance optimization has been achieved. • After sintering at 1500°C, the minimum reflection loss at 5.92 GHz is as high as −43.03 dB, with a matching thickness of only 3.7 mm, demonstrating the excellent electromagnetic wave absorption performance. Transition metal carbides (TMCs) are a class of materials with excellent dielectric properties and thermal stability, which exhibit enormous potential in high temperature electromagnetic wave absorption (EWA). However, the high dielectric constant and electrical conductivity of TMCs usually cause impedance mismatch, and their high density also prevents further practical applications. To solve these problems, the lightweight and impedance matching NbC nanowires (NbCnws) were prepared by using bamboo powder as a carbon source and subsequent carbothermal reduction reaction process. The as‐synthesized NbCnws all exhibit a low density of 0.23 g/cm3 and superior EMA performance. It is worth noting that the minimum reflection loss (RLmin) of the sample is −43.03 dB at 5.92 GHz and the corresponding matching thickness is only 3.7 mm when sintering temperature is 1500°C. The excellent electromagnetic wave absorption (EWA) performance is attributed to good impedance matching and strong dielectric loss. This research work provides a prospect for the development and utilization of one‐dimensional TMC materials in the field of microwave absorption materials.

Biotemplating fabrication, mechanical and electrical characterizations of NbC nanowire arrays from the bamboo substrate

TaC nanowire/activated carbon microfiber hybrid structures from bamboo fibers

Carbon-nanotube-templated Carbon Nanofibers with Improved Mechanical Performance

Synthesis of Boron and Boride Compounds Nanowire Arrays by Chemical Vapor Deposition

G030084 Fabrication of High Density Cu Nanowire Array by Template Method and Its Evaluation

Experimental studies of the formation process and morphologies of carbon nanotubes with bamboo mode structures

Growth and Characterization of Bamboo-Like Multiwalled Carbon Nanotubes over Cu/Al2o3 Catalyst

Synthesis of boron carbide nanoflakes via a bamboo-based carbon thermal reduction method

Coaxial Carbon@boron Nitride Nanotube Arrays with Enhanced Thermal Stability and Compressive Mechanical Properties.

J212025 Fabrication of Nanowire Surface Fastener on Flexible Substrate and Its Electrical and Mechanical Properties

A Generic Bamboo-Based Carbothermal Method For Preparing Carbide (Sic, B4c, Tic, Tac, Nbc, Tixnb1-Xc, And Taxnb1-Xc) Nanowires

Natural bamboo‐derived NbC nanowires for efficient electromagnetic wave absorption

Fabrication and Morphology of NbC X -C Composite Three-Dimensinal Netted Fibers

Fabrication of Large-Area Single Crystal Bismuth Nanowire Arrays

Synthesis and Characterization of Superconducting NbC Nanotubes

The Fabrication And Characterization Of N-Doped Aligned Carbon Nanotube Arrays In Large Area

Nanoscale characterisation and magnetic properties of Co81Cu19/Cu multilayer nanowires

Tailoring mechanical properties and electrical conductivity of flexible niobium carbide nanocomposite thin films

Template synthesis, characterization and magnetic property of Fe nanowires-filled amorphous carbon nanotubes array

Fabrication of patterned boron carbide nanowires and their electrical, field emission, and flexibility properties

Synthesis, Analysis, and Electrical Property Measurements of Compound Nanotubes in the B-C-N Ceramic System