Influence of deposition time on C-AlPO4-mullite coatings prepared by solvothermal electrophoretic deposition process and activation energy

Wei Hao,Jie Fei,Jianfeng Huang,Kaitong Wang,Liyun Cao,Lixiong Yin,Jianpeng Wu,Xinyuan Fu

2013-01-01

Abstract:C-AlPO4-mullite coating was deposited on C/C-SiC composites surface by a noval solvothermal electrophoretic deposition using cristobalite aluminum phosphate crystallites, mullite powder as source materials. Phase compositions and microstructures of the as-prepared multi-coatings were characterized by XRD and SEM. The influence of deposition time on the microstructure was investigated. Results show that the deposition time plays an important role in improving the microstructure of C-AlPO4-mullite coatings. Density and homogeneity of the C-AlPO4-mullite coatings was achieved when the deposition time reaches 15 min. The deposition amount of the multi-coatings also increases with the increase of deposition temperature. The deposition mass of the coatings and the square root of the deposition time at different solvothermal temperatures according to linear relationship, and the deposition activation energy is calculated to be 24.39 kJ/mol. Compared with SiC coatings prepared by pack cementation, the as-prepared coatings exhibit better anti-oxidation property, which could effectively protect C/C composites from oxidation at 1 773 K in air for 300 h with a mass loss of 1.26%.