Abstract:The microstructural evolution of a tempered martensitic ferritic steel X20CrMoV12.1 subjected to ultrasonic nanocrystalline surface modification (UNSM) treatment was investigated by electron backscattered diffraction (EBSD) and transmission electron microcopy (TEM). EBSD results clearly show a grain refinement up to a depth of similar to 210 mu m from the treated surface, with the activities of formation of low angle grain boundary transforming to high angle grain boundary with misorientation. The mechanism of grain refinement involves the formation of dislocations within the tempered lath structure, transforming to a dense dislocation wall (DDW) which is always vertical to the lath boundary, dividing the original lath into a block and a subgrain structure, contributing to loss of lath structure. With increasing strain (top layer), the blocks and subgrains were further refined by dislocation slipping, resulting in the formation of nano-sized grains in the top surface. Refinement of second phase precipitation (M23C6) is observed up to a depth of similar to 50 mu m from the treated surface due to the dislocation cutting induced by plastic deformation. In addition, an increase in number density and volume fraction of precipitates is observed with decreasing depth from the matrix, which may be due to compressed microstructure formed as the result of UNSM treatment. Further, no evidence of carbide dissolution was observed. Consequently, a nano-sized grain and dense precipitate layer are produced by UNSM treatment.

EFFECT OF SURFACE NANOCRYSTALLIZATION ONMICROSTRUCTURE AND THERMAL STABILITYOF REDUCED ACTIVATION STEEL

Strain-induced Refinement and Thermal Stability of a Nanocrystalline Steel Produced by Surface Mechanical Attritiontreatment

Microstructure and Thermal Stability of Bulk Nanocrystalline Alloys Produced by Surface Mechanical Attrition Treatment

Nanocrystallization of a Quenched RAFM Steel and Microstructure Evolution During Annealing Heat Treatment

A Coupled EBSD/TEM Analysis of the Microstructure Evolution of a Gradient Nanostructured Ferritic/Martensitic Steel Subjected to Surface Mechanical Attrition Treatment

Effect of N on the Precipitation Behaviours of the Reduced Activation Ferritic/martensitic Steel CLF-1 after Thermal Ageing

Thermal Stability in Nanocrystalline Fe-30 Wt Pct Ni Alloy Induced by Surface Mechanical Attrition Treatment

Nanocrystallization and Magnetic Properties of Fe-30 Weight Percent Ni Alloy by Surface Mechanical Attrition Treatment

Interdiffusion of Alloying Elements in Nanocrystalline Fe–30 Wt.% Ni Alloy During Surface Mechanical Attrition Treatment and Its Effect on Α → Γ Transformation

Characterization of the Nano-Scale Surface Layer of a Tempered Martensitic Steel Synthesized by Ultrasonic Nanocrystalline Surface Modification Treatment

Enhanced Saturation Magnetization of Nanocrystalline Cobalt Produced by Surface Mechanical Attrition Treatment

Measurement of Microstructural Parameters of Nanocrystalline Fe–30 Wt.%ni Alloy Produced by Surface Mechanical Attrition Treatment

Microstructural Characterization of Nanocrystalline Nickel Produced by Surface Mechanical Attrition Treatment

α to γ transformation in the nanostructured surface layer of pearlitic steels near room temperature

Mechanical Nanocrystallization Surface Treatment on the Reheated 400mpa Ultrafine Grained Steel

Thermal stability of nanocrystalline microstructure in P92 heat resisting steels

Nanocrystallization and Martensitic Transformation in Fe–23.4Mn–6.5Si–5.1Cr (wt.%) Alloy by Surface Mechanical Attrition Treatment

Diffusion Phenomenon During SMAT and Its Effect on Magnetic Property in Nanocrystalline Fe-30 Wt%ni Alloy

Thermal Stability and Corrosion Resistance of Nanocrystallized Zirconium Formed by Surface Mechanical Attrition Treatment

Surface Nanocrystallization of Mg-3 Wt.% Li-6 Wt.% Al Alloy by Surface Mechanical Attrition Treatment

Influence of austenitizing temperature on the mechanical properties and microstructure of reduced activation ferritic/martensitic steel