Abstract:BACKGROUND Zirconia is one of the most widely used ceramic materials for transplanting and treating caries. This study aimed to synthesize zirconium oxide (ZrO₂) nanotubes and evaluated their characteristics. MATERIAL AND METHODS Zr film was prepared using an ion plating method. Nanoarray film was constructed with anodizing. Photocatalytic properties of nnanotubes were assessed by evaluating decolorization of methyl orange. Elemental analysis and structural morphology for coatings were evaluated using x-ray analysis and scanning electron microscopy (SEM). Dimensions for layers were measured with SEM imaging. X-ray diffraction (XRD) was measured using Empyrean x-ray diffractometry. RESULTS There were irregular cavities on the surface of ZrO₂ nanotubes undergoing anodizing of 30V. Anodizing voltage of 45 V (with regular nano-pore arrays and smooth nanotube walls) and anodic oxidation duration of 60 min (ZrO₂ nanotubes clearly formed atop ZrO₂-coated substrate surface) were the optimal condition for ZrO₂ nanotube formation. TEM illustrated tube length of ZrO₂ nanotubes was approximately 2.01 μm. Nanotube diameter was 51.06 nm, and wall thickness was 13 to 14 nm. Annealed nanotubes showed an obvious crystal diffraction pattern. TEM diffraction ring showed nanotube array without obvious transistor structure before annealing, but with good crystallinity post-annealing. Increased annealing temperatures result in enhanced intensity for the monoclinic phase (400-800°C). After annealing at 600°C, the decolorization effect of ZrO₂ nanotubes on methyl orange was better than that post-annealing at 400 and 800°C. ZrO₂ nanotubes demonstrated higher microshear bond strength. CONCLUSIONS Zirconium nanotubes were successfully synthesized and demonstrated good structural characteristics, which can be applied to transplanting and treating caries.

Photoluminescence Properties and Photocatalytic Activities of Zirconia Nanotube Arrays Fabricated by Anodization

Synthetic and Effect of Annealing on the Luminescent Properties of Zno Nanowire

Temperature-dependent differences in wettability and photocatalysis of TiO 2 nanotube arrays thin films

Effects of Hydrothermal Time on the Morphologies of Rutile TiO2 Hierarchical Nanoarrays and Their Optical and Photocatalytic Properties

Effect of UV irradiation on the properties of ZnO nanorod arrays prepared by hydrothermal method

Photoluminescence of ZrO2-ZnO Hybrid Nanotube Arrays Produced by Electrodeposition

Preparation of a Novel Transplant Material, Zirconium Oxide (ZrO₂) Nanotubes, and Characterizations Research

Fabrication and correlation between photoluminescence and photoelectrochemical properties of vertically aligned ZnO coated TiO2 nanotube arrays

Thermally stimulated luminescence of oxygen-deficient zirconia nanotubes

Crystal phase transition and properties of titanium oxide nanotube arrays prepared by anodization

Industrial and environmental significance of photonic zirconia nanoflakes: Influence of boron doping on structure and band states

Photoluminescence Properties of Zirconia Nanobelts with Trace Sm3+ Ions

Photoluminescence of nanometer zirconia powders

Tunable Luminescence In Monodisperse Zirconia Spheres

Photoluminescence enhancement of ZnO nanowire arrays by atomic layer deposition of ZrO2 layers and thermal annealing.

Photoluminescence of ZnO Nanorod-Tio2 Nanotube Hybrid Arrays Produced by Electrodeposition

Preparation and photoluminescence properties of Eu3+ -doped BaZrO3 nanotube arrays

Defect-Related Photoluminescence and Photocatalytic Properties of Porous Zno Nanosheets

Preparation and Photoluminescence Properties of ZnO Nanowire/Nanorod Mix Arrays

The growth rate of nanotubes and the quantity of charge during anodization

Double-Walled ZrO2 Nanotube Array: Preparation and Enhanced Photocatalytic Activity