Abstract:Nanocrystalline zinc oxide (ZnO) samples are synthesized through a facile hydrothermal route at different temperatures. Sample synthesized at 80 °C (sample code HT80) has average crystallite size of 32 ± 2 nm and the morphology is not unform with the presence of rods, wires and discs. Sample prepared at 160 °C (sample code HT160) has rod-like morphology with an average crystallite size of 130 ± 5 nm. X-ray photoelectron spectra reveal the presence of hydroxyl groups bonded to Zn 2+ , oxygen vacancies and adsorbed oxygen species in both the samples. Atomic percentage of the bonded/adsorbed hydroxides and oxygen containing species is higher in HT80. Band gaps values are lower in comparison with bulk ZnO due to band bending. Photoluminescence spectra has a UV peak at ∼381 nm (3.25 eV) and a broad emission band in the visible region centred at ∼550 nm (2.25 eV) respectively corresponding to the band edge emission and defect mediated emission. The emission profile of both samples is similar indicating the presence of similar type of native point defects viz., Zn vacancies, Zn interstitials and oxygen vacancies in different charge states. Sample HT160 has more intense emission due to the better photonic absorption. The photocurrent response under wide light irradiation is also larger for HT160 with a sensitivity of 37 due to the better photonic absorption and larger crystallite size. Wavelength dependent photocurrent response for this sample shows highest sensitivity at 380 nm with a sensitivity of 152 corresponding to the band-to-band excitation. A weak photoresponse for visible light irradiation (∼600 nm) due to the desorption of adsorbed O 2 or hydroxide species caused by the direct photoexcitation of the captured electron to the conduction band is also noted. Photocatalytic efficiency of both the samples are comparable with rate constants 3.1 × 10 −2 min −1 and 3.7 × 10 −2 min −1 respectively for HT80 and HT160. The reusability is much better for sample HT160 which is attribute to larger average crystallite size and uniform morphology.

Defect-Related Photoluminescence and Photocatalytic Properties of Porous Zno Nanosheets

Synthetic and Effect of Annealing on the Luminescent Properties of Zno Nanowire

Nanoplate-Built Zno Hollow Microspheres Decorated with Gold Nanoparticles and Their Enhanced Photocatalytic and Gas-Sensing Properties

Enhanced Visible Light Response of ZnO Porous Thin Film by Post-Annealing Treatment

Annealing-Induced Change of Hydrogen Behavior in Zno Nanorods Revealed by Photoluminescence

Oxygen Deficient Zno1-X Nanosheets with High Visible Light Photocatalytic Activity

Disordered ZnO nanoparticles with extremely intense deep-level emission and enhanced photocatalytic activity

Luminescence and Photocatalytic Activity of ZnO Nanocrystals: Correlation between Structure and Property

Identification of Defect-Related Emissions in ZnO Hybrid Materials

Photoluminescence, photocurrent response and photocatalytic activity of hydrothermally derived nanocrystalline ZnO with native point defects

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Thermal Annealing Induced Controllable Porosity and Photoactive Performance of 2D ZnO Sheets

Influence of Defects on the Photocatalytic Activity of ZnO

Rendering Visible-Light Photocatalytic Activity to Undoped ZnO via Intrinsic Defects Engineering

Enhanced Photocurrent and Photocatalytic Properties of Porous ZnO Thin Film by Ag Nanoparticles

Annealing Effects on the Microstructure and Photoluminescence Properties of Ni-Doped Zno Films

Defect-rich ZnO Nanosheets of High Surface Area As an Efficient Visible-Light Photocatalyst

Defect Emissions in ZnO Nanostructures

Superior Photocatalytic Activity of Porous Wurtzite ZnO Nanosheets with Exposed {0 0 1} Facets and a Charge Separation Model Between Polar (0 0 1) and (001¯) Surfaces

Probing size-dependent defects in zinc oxide using synchrotron techniques: impact on photocatalytic efficiency

Revealing the Dependency of Dye Adsorption and Photocatalytic Activity of ZnO Nanoparticles on Their Morphology and Defect States