High Temperature Creep Behavior of Mg-12Gd-2Y-0.5Zr Magnesium Alloy

付三玲,李全安,井晓天,周伟

DOI: https://doi.org/10.15980/j.tzzz.2013.12.023

2013-01-01

Abstract:The creep behavior of Mg-12Gd-2Y-0.5Zr magnesium alloy at high temperature was analyzed. The results show that the creep resistance of the experimental alloy is generally superior to that of commercial WE54 alloy, and the stress exponent(n) is in range of 2.5~3.8 at 200°C and 4.2~6.1 at 300°C under a stress of 50~70 MPa. The creep mechanisms of the series alloy mainly are controlled by dislocation climbing towards dislocation cross-slip. The creep activation energy(Qc) is 66 kJ/mol under 50 MPa and 87.2 kJ/mol under 70 MPa at 200~300°C. With the increase of temperature and stress, creep activation energy of Mg-12Gd-2Y-0.5Zr alloy is near to diffusion activation energy (80 kJ/mol) of pure magnesium more and more.