Abstract:Four carbon/carbon composites with densities of 1.75–1.81 g/cm3were produced with matrix carbons derived from (a)coal tar pitch and furfural acetone resin by impregnation-carbonization, (b) natural gas by isothermal chemical vapor infiltration and (c) xylene by film-boiling chemical vapor infiltration. Theirmechanical properties and thermal conductivities (TC) were compared and correlated to the matrix carbon microstructures. Results showed that the strength of the composites decreased as thecarbon matrix changed from natural gas pyrocarbon (PyCN), to resin-derived carbon, to xylene PyC (PyCX), and to pitch-derived carbon. The highest flexural and interlaminar shear strengths of 208.7 and 26.4MPa, respectively, were obtained for the PyCN matrix. The large amount of fiber pull-out and step-like matrix fracture contributed to a high toughness of composites with PyCN and PyCX matrices. Relatively low strength and toughness were obtained for the pitch-derived carbon. The change of TC with the matrix type was consistent with the graphitization degree and apparent crystallite height. The highest in-plane and out-of-plane TC reached 148.2 and 75.4 W/(m·K), respectively, for the PyCX matrix, which was due to its carbon layers having the highest preferred orientation. The chaotic structure and large number of defects of the resin-derived carbon produced a relatively low TC. PyCN was the most suitable matrix for composites with excellent mechanical properties. PyCXshould be used to improve the TC and toughness of the low-cost composites.

Microstructure characterization from X-ray micro-tomography and equivalent mechanical properties of carbon matrix of 4D in-plane carbon/carbon composites

Microstructures and Mechanical Properties of 3D 4-Directional Carbon/Carbon Composite

X-ray microtomography analysis of the damage mechanisms in 3D circular braided carbon fiber/epoxy resin composite tubes under axial impact compression

Investigation on Mechanical Properties of Porous Fiber Bundle-Matrix Interlayers in Three-Dimensional Carbon/Carbon Composite

Relations Between Microstructure and Mechanical Properties of Fiber-Matrix Interfaces in C/C Composite

Micro-CT Characterization on the Meso-Structure of Three-Dimensional Full Five-Directional Braided Composite

In Situ Tensile Damage Characterization of C/C Composites Through X-ray Computed Tomography and Digital Volume Correlation

Mechanical Properties of 3D Carbon/carbon Composites by Nanoindentation Technique

Real internal microstructure based key mechanism analysis on the micro-damage process of short fibre-reinforced composites

Finite Element Modeling of 3D Orthogonal Woven C/C Composite Based on Micro-Computed Tomography Experiment

Mechanical and thermal conduction properties of carbon/carbon composites with different carbon matrix microstructures

Microstructure-based Modeling on Structure-Mechanical Property Relationships in Carbon Nanotube/aluminum Composites

Microstructural Characterization of Non-Equilibrated 4d Carbon/Carbon Composites in Ultrahigh Temperature Environment

Microstructure Characterization by X-Ray Computed Tomography of C/C-SiC Ceramic Composites Fabricated with Different Carbon Fiber Architectures

Micro-CT characterization on porosity structure of 3D Cf/ SiCm composite

In-situ Micro-Ct Damage Analysis of Carbon and Carbon/glass Hybrid Laminates under Tensile Loading by Image Reconstruction and DVC Technology

Deformation Behavior and Damage in B4Cp/6061Al Composites: an Actual 3D Microstructure-Based Modeling

Microstructure and Mechanical Properties of Three-Dimensional Five-Directional Braided Composites

Microstructure and Mechanical Properties of Dual-Matrix Carbon/Carbon Composites

The Relationship Between the Mechanical Properties and Microstructures of Carbon Fibers

Micro-CT image-based computation of effective thermal and mechanical properties of fibrous porous materials