Abstract:The failure of composite laminates under cyclic fatigue loads is complex, as multiple failure mechanisms are in play at different scales and interact with each other. Predicting the remaining fatigue life as well as the residual capacities of a composite laminate or component is crucial, particularly for safety-critical applications. A progressive fatigue model is proposed to describe the catastrophic failure of open-hole laminates under tensile cyclic fatigue. To represent both intra-laminar and inter-laminar damage, a combination of a continuum damage mechanics model (CDM) and a discrete cohesive zone model (CZM) is implemented in the finite element (FE) software Abaqus. The CDM combines fibre- and matrix-dominated S-N curves with the Palmgren–Miner accumulation rule and Hashin’s residual strength to form a fatigue failure criterion differentiating between fibre failure (FF) and matrix failure (MF). The CZM implemented in this work is the CF20 model proposed by NASA. Fatigue cycling is simulated using an external cycle-jump scheme, where the stiffness degradation is conducted between the FE simulations outside of the implicit solver [90/0] s. Glass fibre reinforced polymer (GFRP) open-hole specimens were tested in tensile cyclic fatigue at a load ratio of 0.1. The experiments were reproduced numerically and the results compared. After calibration of a set of parameters based on one load level, the model was able to reproduce the experimental S-N curve very well, predicting a slope of −0.10, while the experimental value was −0.11. The failure sequence of the laminate was also successfully reproduced. The growth of the split from the hole, and its interaction with inter-laminar delamination, was successfully captured. The proposed approach was able to describe the fatigue failure of an open-hole laminate with a minimal set of material inputs using a simplified fatigue damage model while avoiding convergence issues.

Progressive damage of an open-hole NCF/epoxy laminate subjected to tensile load

Continuum Damage Modeling and Progressive Failure Analysis of Carbon Fiber/epoxy Composite Pressure Vessel

Progressive failure analysis of 2D woven composites at the meso-micro scale

Open-hole Tensile Progressive Damage and Failure Prediction of Carbon Fiber-Reinforced PEEK–titanium Laminates

Numerical simulation and experiment validation of variable stiffness composite laminates with open holes under unidirectional tension

A 3D finite element model to simulate progressive damage in unidirectional- and woven-fibre thermoplastic discontinuous-long-fibre composites

Characterization of progressive damage behaviour and failure mechanism of carbon fibre reinforced DP590 laminates

Progressive Fatigue Modelling of Open-Hole Glass-Fibre Epoxy Laminates

Progressive fracture analysis of the open-hole composite laminates: experiment and simulation

Deformation and Fracture Mechanisms of Automated Fiber Placement Pre-Preg Laminates under Out-of-plane Tensile Loading

A New Stress-Based Formulation for Modeling Notched Fiber-Reinforced Laminates

Progressive Failure Analysis of Carbon Fiber/epoxy Composite Laminates Using Continuum Damage Mechanics

Progressive Damage and Failure Modeling in Fiber-Reinforced Laminated Composites Containing a Hole

Mechanical response and critical failure mechanism characterization of notched carbon fiber reinforced polymer laminate subjected to tensile loading

Collaborative Model in Brain-Computer Integration

Experimental and numerical studies of the open hole tensile strength of drilled‐ and molded‐hole unidirectional laminates

A comparative study on failure mechanisms of open-hole and filled-hole composite laminates: Experiment and numerical simulation

Finite Element Method of a Progressive Intralaminar and Interlaminar Damage Model for Woven Fibre Laminated Composites under Low Velocity Impact

A progressive damage model for carbon fiber-reinforced polymer laminates subjected to fastener pull-through failure

A New Three-Dimensional Progressive Damage Model for Fiber-Reinforced Polymer Laminates and Its Applications to Large Open-Hole Panels

Progressive damage modelling and fatigue life prediction of Plain-weave composite laminates with Low-velocity impact damage