Three pyrazine derivatives as corrosion inhibitors for steel in 1.0M H2SO4 solution
Xianghong Li,Shuduan Deng,Hui Fu
DOI: https://doi.org/10.1016/j.corsci.2011.05.068
IF: 7.72
2011-01-01
Corrosion Science
Abstract:The inhibition effect of three pyrazine derivatives of 2-methylpyrazine (MP), 2-aminopyrazine (AP) and 2-amino-5-bromopyrazine (ABP) on the corrosion of cold rolled steel (CRS) in 1.0 M H 2 SO 4 solution was studied by weight loss, potentiodynamic polarization curves and electrochemical impedance spectroscopy (EIS) methods. The results show that all pyrazine compounds are good inhibitors, and inhibition efficiency follows the order: ABP > AP > MP. The adsorption of each inhibitor on CRS surface obeys Langmuir adsorption isotherm. For all these pyrazine derivatives, they act as mixed-type inhibitors. The probable inhibitive mechanism is proposed from the viewpoint of adsorption theory. Keywords A. Steel B. EIS B. Polarization B. Weight loss C. Acid inhibition 1 Introduction Using inhibitors is one of the most practical methods for protecting metals against corrosion, especially in acidic media [1] . Among numerous inhibitors, N-heterocyclic compounds are considered to be the most effective corrosion inhibitors [2] . Up to now, various N-heterocyclic compounds are reported as good corrosion inhibitors for steel in acidic media, such as imidazoline derivatives [3,4] , 1,2,3-triazole derivatives [5] , 1,2,4-triazole derivatives [2,6–18] , benzotriazole [19,20] , pyrrole [21] , pyridine derivatives [22] , pyrazole derivatives [23–25] , bipyrazole derivatives [26,27] , pyrimidine derivatives [28] , pyridazine derivatives [29–31] , indole derivatives [32,33] , benzimidazole derivatives [34–38] , quinoline derivatives [39] , purine derivatives [40–42] and tetrazole derivatives [43–49] . Generally, N-heterocyclic compounds exert their inhibition by adsorption on the metal surface through N heteroatom, as well as those with triple or conjugated double bonds or aromatic rings in their molecular structures. Furthermore, the adsorption of inhibitor on steel/solution interface is influenced by the chemical structure of inhibitor, the nature and charged surface of metal, the distribution of charge over the whole inhibitor molecule and the type of aggressive media. As another important kind of N-heterocyclic compound, pyrazine derivatives whose molecules possess the pyrazine ring with two N heteroatoms could also be seemed as good potential inhibitors. However, data regarding the use of pyrazine derivatives as corrosion inhibitors is very scarce. Hammouti et al. [50,51] studied the inhibition effect of diethyl pyrazine-2,3-dicarboxylate on the corrosion of steel in 0.5 M H 2 SO 4 , and its maximum inhibition efficiency ( E ) was about 82% at 0.01 M. As ordinary pyrazine derivatives, 2-methylpyrazine (MP, C 5 H 6 N 2 ), 2-aminopyrazine (AP, C 4 H 5 N 3 ) and 2-amino-5-bromopyrazine (ABP, C 4 H 4 N 3 Br) have good solubility in water, and are widely used as intermediates for the preparation of drugs. According to our recent work [52] , the pyrazine derivatives of AP and ABP act as good corrosion inhibitors on the corrosion of steel in 1.0 M HCl, which incite us to further extend the corrosion inhibition by pyrazine derivatives for steel in H 2 SO 4 solution. In a continuation of our program, the inhibition effect of three pyrazine derivatives (MP, AP and ABP) on the corrosion of cold rolled steel (CRS) in 1.0 M H 2 SO 4 solution was studied using weight loss, potentiodynamic polarization curves and electrochemical impedance spectroscopy (EIS) methods. The adsorption isotherm of inhibitor on steel surface and the standard adsorption free energy (Δ G 0 ) are obtained. Meanwhile, the difference in inhibition performance among MP, AP and ABP is discussed to gain some insight into the effect of three selected pyrazine compounds related to their chemical structures. A probable inhibitive mechanism is presented to explain the results. 2 Experimental 2.1 Materials Tests were performed on a cold rolled steel (CRS) of the following composition (wt.%): 0.07% C, 0.3% Mn, 0.022% P, 0.010% S, 0.01% Si, 0.030% Al, and the remainder Fe. 2.2 Inhibitors Three pyrazine derivatives of 2-methylpyrazine (MP), 2-aminopyrazine (AP) and 2-amino-5-bromopyrazine (ABP) were obtained from Shanghai Chemical Reagent Company of China. Fig. 1 shows the molecular structures of MP, AP and ABP. 2.3 Solutions The aggressive solution of 1.0 M H 2 SO 4 was prepared by dilution of AR grade 98% H 2 SO 4 with distilled water. The concentration range of inhibitors is 0.2–5.0 mM. 2.4 Weight loss measurements The CRS sheets of 2.5 cm × 2.0 cm × 0.06 cm were abraded by a series of emery paper (grade 320-500-800) and then washed with distilled water, degreased with acetone, and finally dried at room temperature. After weighing using digital balance with sensitivity of ±0.1 mgt, the specimens were immersed in beakers containing 250 ml 1.0 M H 2 SO 4 without and with various concentrations of inhibitor using glass hooks and rods. The temperature was controlled at 25 ± 0.1 °C using a water thermostat. All the aggressive acid solutions were open to air. After immersion for 6 h, the specimens were taken out, washed with bristle brush under running water to remove the corrosion product, dried with a hot air stream, and re-weighed accurately. In order to get good reproducibility, experiments were carried out in duplicate. The average weight loss of two parallel CRS sheets was obtained. The corrosion rate ( ν ) is calculated using the following equation: (1) ν = W St where W is the average weight loss of two parallel CRS sheets, S the total area of one CRS specimen, and t is immersion time. With the corrosion rate calculated, the inhibition efficiency ( E w ) is determined as follows: (2) E w % = ν 0 − ν ν 0 × 100 where ν 0 and ν are the values of corrosion rate without and with inhibitor, respectively. 2.5 Electrochemical measurements Electrochemical experiments were carried out in the conventional three-electrode cell with a platinum counter electrode (CE) and a saturated calomel electrode (SCE) coupled to a fine Luggin capillary as the reference electrode. In order to minimize ohmic contribution, the Luggin capillary was placed close to the working electrode (WE) which was in the form of a square CRS embedded in PVC holder using epoxy resin so that the flat surface was only surface in the electrode. The working surface area was 1.0 cm × 1.0 cm, and prepared as described above (Section 2.4 ). Before measurement the electrode was immersed in test solution at open circuit potential (OCP) for 2 h to be sufficient to attain a stable state. All electrochemical measurements were carried out at 25 °C using PARSTAT 2273 advanced electrochemical system (Princeton Applied Research). The potential of potentiodynamic polarization curves was increased at 0.5 mV s −1 and started from a potential of −250–+250 mV versus OCP. Inhibition efficiency ( E p %) is defined as: (3) E p % = i corr ( 0 ) − i corr ( inh ) i corr ( 0 ) × 100 where i corr(0) and i corr(inh) represent corrosion current density values without and with inhibitor, respectively. Electrochemical impedance spectroscopy (EIS) was carried out after 2 h of immersion time at OCP in the frequency range of 10 mHz–100 kHz using a 10 mV peak-to-peak voltage excitation. Inhibition efficiency ( E R %) is estimated using the relation: (4) E R % = R t ( inh ) − R t ( 0 ) R t ( inh ) × 100 where R t(0) and R t(inh) are the charge transfer resistance values in the absence and presence of inhibitor, respectively. 3 Results and discussion 3.1 Weight loss measurements 3.1.1 Effect of pyrazine derivatives on corrosion rate Fig. 2 illustrates the corrosion rate of CRS in 1.0 M H 2 SO 4 at 25 °C in the presence of different concentrations of pyrazine derivatives. The corrosion rate reduces after addition of the selected three pyrazine derivatives, and decreases with the inhibitor concentration due to the fact that the adsorption coverage increases, which shields the CRS surface efficiently from the medium. In the absence of inhibitor, the corrosion rate is 21.34 g m −2 h −1 . While in the presence of 5.0 mM inhibitor, the corrosion rate values are reduced to 4.36, 3.40 and 2.14 g m −2 h −1 , for MP, AP and ABP, respectively. At any given inhibitor concentration, the corrosion rate follows the order: ν (ABP) < ν (AP) < ν (MP), which indicates that ABP exhibits the best inhibitive performance among three pyrazine compounds. 3.1.2 Effect of pyrazine derivatives on inhibition efficiency Fig. 3 represents inhibition efficiency values obtained from the weight loss ( E w ) in 1.0 M H 2 SO 4 solutions in the presence of various concentrations of MP, AP and ABP at 25 °C. Clearly, E w increases with an increase in the inhibitor concentration. It should be noted that when the concentration of inhibitor reaches about 3.0 mM, E w reaches certain value and change slightly with a further increase in the inhibitor concentration. At 5.0 mM, the maximum E w is 79.6% for MP; 84.3% for AP; and 90.1% for ABP, which indicates all pyrazine compounds act as good corrosion inhibitors for CRS in 1.0 M H 2 SO 4 . E w values of the examined pyrazine derivatives follow the order: ABP > AP > MP. 3.1.3 Adsorption isotherm and standard adsorption free energy Basic information on the adsorption of inhibitor on metal surface can be provided by adsorption isotherm. Several isotherms including Frumkin, Langmuir, Temkin, Freundlich, Bockris–Swinkels and Flory–Huggins isotherms are employed to fit the experimental data. It is found that the adsorption of studied inhibitors on steel surface obeys the Langmuir adsorption isotherm equation [52] : (5) c θ = 1 K + c where c is the concentration of inhibitor, K the adsorption equilibrium constant, and θ is the surface coverage and expressed by the ration E w %/100. Plots of c/θ against c yield straight lines as shown in Fig. 4 , and the corresponding linear regression parameters are listed in Table 1 . Both linear correlation coefficient ( r ) and slope are close to 1, indicating the adsorption of three pyrazine inhibitors on steel surface obeys Langmuir adsorption isotherm. Also, K follows the order: ABP > AP > MP. Generally, large value of K means better inhibition performance of a given inhibitor. This is in good agreement with the values of E w obtained from Fig. 3 . The adsorption equilibrium constant ( K ) is related to the standard adsorption free energy (Δ G 0 ) as shown the following equation [53] : (6) K = 1 55.5 exp − Δ G ° RT where R is the gas constant (8.314 J K −1 mol −1 ), T the absolute temperature (K), and the value 55.5 is the concentration of water in the solution expressed in M [53] . The Δ G 0 values are also presented in Table 1 . Furthermore, values of Δ G 0 up to −20 kJ mol −1 are consistent with the electrostatic interaction between the charged molecules and the charged metal (physisorption) while those more negative than −40 kJ mol −1 involve sharing or transfer of electrons from the inhibitor molecules to the metal surface to form a co-ordinate type of bond (chemisorption) [54] . In the present study, the value of Δ G 0 is found to be within the range from −40 to −20 kJ mol −1 ; probably means that the adsorption of each pyrazine inhibitor on the steel surface contains both physical adsorption and chemical adsorption. 3.2 Potentiodynamic polarization curves Potentiodynamic polarization curves of CRS in 1.0 M H 2 SO 4 containing MP, AP and ABP at 25 °C are shown in Figs. 5–7 , respectively. In all cases, addition of each compound causes a remarkable decrease in the corrosion rate i.e., shifts the both anodic and cathodic curves to lower current densities. In other words, both cathodic and anodic reactions of CRS electrode are drastically inhibited by the pyrazine compounds. It should be noted that in anodic domain, it is difficult to recognize the linear Tafel regions. Accordingly, the corrosion current density values are estimated accurately by extrapolating the cathodic linear region back to the corrosion potential. Similar fitting method has also been widely used [55,56] . The electrochemical corrosion parameters including corrosion current densities ( i corr ), corrosion potential ( E corr ), cathodic Tafel slope ( b c ) and corresponding inhibition efficiency ( E p ) are given in Table 2 . It is apparent that i corr decreases considerably in the presence of each inhibitor, and decreases with increasing the inhibitor concentration. Correspondingly, E p increases with the inhibitor concentration, due to the increase in the blocked fraction of the electrode surface by adsorption. E p of 5.0 mM inhibitor reaches up to a maximum of 81.2% for MP; 85.4% for AP; and 91.7% for ABP, which again confirms that all three pyrazine derivatives are good inhibitors in 1.0 M H 2 SO 4 , and E p follows the order: ABP > AP > MP. The presence of MP, AP or ABP does not prominently shift the corrosion potential, which indicates all studied pyrazine derivatives act as mixed-type inhibitors [57] . Furthermore, in the presence of each inhibitor, the slight change of b c indicates that the cathodic corrosion mechanism of steel does not change. 3.3 Electrochemical impedance spectroscopy (EIS) Figs. 8–10 represent the Nyquist diagrams for CRS in 1.0 M H 2 SO 4 in the presence of MP, AP and ABP at 25 °C, respectively. Clearly, the impedance spectra exhibit a large capacitive loop at high frequencies followed by a small inductive loop at low frequency values. In the presence of each inhibitor, comparing with blank solution, the shape is maintained throughout all tested concentrations, indicating that almost no change in the corrosion mechanism occurs due to the inhibitor addition [58] . The capacitive loop indicates that the corrosion of steel is mainly controlled by a charge transfer process, and usually related to the charge transfer of the corrosion process and double layer behavior. On the other hand, the inductive loop may be attributed to the relaxation process obtained by adsorption species like FeSO 4 [59] or inhibitor species [60] on the electrode surface. The diameter of the capacitive loop in the presence of inhibitor is bigger than that in the absence of inhibitor (blank solution) and increases with the inhibitor concentration. This indicates that the impedance of inhibited substrate increases with the inhibitor concentration. Noticeably, these capacitive loops are not perfect semicircles which can be attributed to the frequency dispersion effect as a result of the roughness and inhomogeneousness of the electrode surface [61] . Accordingly, the capacitive loops at high frequencies are simulated by the equivalent circuit shown in Fig. 11 [62] . The circuit employed allows the identification of both solution resistance ( R s ) and charge transfer resistance ( R t ). It is worth mentioning that the double layer capacitance ( C dl ) value is affected by imperfections of the surface, and that this effect is simulated via a constant phase element (CPE) [63] . The CPE is composed of a component Q dl and a coefficient a which quantifies different physical phenomena like surface inhomogeneousness resulting from surface roughness, inhibitor adsorption, porous layer formation, etc. The capacitance can be calculated from the following equation [20,59] : (7) C dl = Q dl × ( 2 π f max ) a − 1 where f max represents the frequency at which the imaginary value reaches a maximum on the Nyquist plot. The electrochemical parameters of a , R t , C dl and E R are calculated by ZSimpWin software and presented in Table 3 . In H 2 SO 4 solutions the value of a increases in presence of inhibitors on steel surface, and increases with the inhibitor concentration except for 3.0 mM AP. For example, the value of a increases from 0.76 to 0.94 in the presence of 5.0 mM ABP. These results indicate that the steel surface has become smoother due to formation of a non-porous and dense monolayer of inhibiting film. Clearly, R t value increases prominently while C dl reduces with the concentration of inhibitor. A large charge transfer resistance is associated with a slower corroding system. At any given inhibitor concentration, R t (MP) < R t (AP) < R t (ABP), which confirms that ABP shows the best inhibitive performance among three pyrazine compounds. The decrease in C dl in comparing with that in blank solution (without inhibitor), which can result from a decrease in local dielectric constant and/or an increase in the thickness of the electrical double layer, suggests that the inhibitor molecules function by adsorption at the metal/solution interface [59] . E R increases with the concentration of inhibitor, and follows the order: E R (ABP) > E R (AP) > E R (MP). The maximum E R values are 83.3%, 85.3% and 89.8% for MP, AP and ABP, respectively. These results again confirm that all pyrazine derivatives exhibit good inhibitive performance for CRS in H 2 SO 4 solution. Inhibition efficiencies obtained from weight loss ( E w ), potentiodynamic polarization curves ( E p ) and EIS ( E R ) are in good reasonably agreement. 3.4 Explanation for inhibition The inhibition mechanism can be proposed from the adsorption of inhibitor on steel surface. In general, owing to the complex nature of adsorption and inhibition of a given inhibitor, it is impossible for single adsorption mode between inhibitor and metal surface. In the present system, based on the chemical structures of three pyrazine compounds, they are many adsorption active sites on steel surface. Thus, five types of adsorption may take place in the inhibiting phenomena as follows: (i) Owing to neutral N atoms in MP, AP and ABP, they can be protonated in the acid solution as following: (8) MP + x H + ↔ [ MPH x ] x + (9) AP + x H + ↔ [ APH x ] x + (10) ABP + x H + ↔ [ ABPH x ] x + Thus, in acidic solutions, the pyrazine derivatives exist as [MPH x ] x + , [APH x ] x + and [ABPH x ] x + . The charge of the metal surface can be determined from the value of E corr − E q = 0 (zero charge potential) [64] . The E q = 0 of iron is −550 mV vs. SCE in H 2 SO 4 [65] . In the present system, the value of E corr obtained in 1.0 M H 2 SO 4 is −463 mV vs. SCE. So the steel surface charges positive charge in H 2 SO 4 solution because of E corr − E q = 0 > 0. Since SO 4 2− could adsorb on the metal surface [66] , they create an excess negative charge towards the solution and favor more adsorption of the cations. [MPH x ] x + , [APH x ] x+ and [ABPH x ] x+ may adsorb on the negatively charged metal surface. In other words, there may be a synergism between adsorbed SO 4 2− and protonated inhibitor [49] . (ii) Besides to the physical adsorption, MP, AP and ABP may be adsorbed on the metal surface via the chemisorption mechanism, involving to the coordinate bonds that may be formed between the lone electrons pairs of the unprotonated N atoms and the empty orbital of Fe atoms which strengthens the combination intension between the inhibitor molecule and electrode surface. (iii) It is generally accepted that the key adsorption center of N-heterocyclic compound is N-heterocyclic ring. MP, AP and ABP have plentiful π-electrons owing to pyrazine ring, they can be also adsorbed on the metal surface on the basis of donor–acceptor interactions between π-electrons of the pyrazine ring and vacant d-orbitals of Fe. (iv) Due to the chelating action of pyrazine, some metal complexes of Fe 2+ —pyrazine compounds [67,68] have been widely prepared. Thus, [APH x ] x + and [ABPH x ] x + may combine with freshly generated Fe 2+ ions on steel surface forming metal inhibitor complexes: (11) Fe → Fe 2 + + 2 e (12) [ APH x ] x + + Fe 2 + ↔ [ APH x – Fe ] ( x + 2 ) + (13) [ APH x ] x + + Fe 2 + ↔ [ APH x – Fe ] ( x + 2 ) + (14) [ ABPH x ] x + + Fe 2 + ↔ [ ABPH x – Fe ] ( x + 2 ) + These complexes might adsorb onto steel surface through the van der Waals force to form a blocking barrier to keep CRS from corrosion. (v) A combination of the above. All the experimental methods show that the inhibition efficiency of three pyrazine compounds follows the order: ABP > AP > MP. It is well known that if the substitution donor group is added, the electron density on the pyrazine ring is increased, and subsequently, it results into the increased adsorbability. The donor ability of substitution group follows the order: –NH 2 > –CH 3 . Accordingly, AP or ABP exhibits higher inhibition performance than MP. The inhibition efficiency of ABP is higher than that of AP. The results indicate that the substitution Br atom on pyrazine ring of compound ABP increases the inhibition performance in comparison with unsubstituted AP. Similar conclusion is also reported for Schiff bases as corrosion inhibitors in HCl [55] . According to the molecular structure of ABP, the substitution Br is negatively charged center, so it could adsorb on the positively charged steel surface through the electrostatic attraction, and then donate its lone electron pair to the unfilled orbit of Fe atom. Similar views have also been put forward by Hackerman and Kaesche for substitution halides in aromatic amine [69] . In other words, the substitution Br of ABP is the additional center of adsorption, which causes stronger affinity for the metal surface and corresponding better inhibition performance than AP. Furthermore, according to some quantum chemical calculations of pyrazine derivations [70,71] , it can be concluded that the additional substitution Br of ABP would also increases the electron density of pyrazine ring and the delocalization of electron density in the molecule, which can facilitate its adsorption on the metal surface so it has higher inhibition efficiency than AP. 4 Conclusions (1) Three pyrazine derivatives of MP, AP and ABP act as good inhibitors for the corrosion of CRS in 1.0 M H 2 SO 4 solution. Inhibition efficiency ( E w ) increases with the inhibitor concentration, and the maximum E w values are 79.6% (AP), 84.3% (AP) and 90.1% (ABP) at 5.0 mM. (2) For each pyrazine inhibitor, the adsorption is a spontaneous process and obeys Langmuir adsorption isotherm. The parameter of adsorption free energy (Δ G 0 ) indicates that the adsorption of inhibitor involves both physisorption and chemisorption. (3) All pyrazine compounds act as mixed-type inhibitors in 1.0 M H 2 SO 4 . EIS spectra exhibit a large capacitive loop at high frequencies followed by a small inductive loop at low frequency values, and the presence of each inhibitor increases R t values while reduces C dl values. (4) The inhibition efficiency of three pyrazine inhibitors follows the order: ABP > AP > MP. Acknowledgements The electrochemical measurements were carried out on PARSTAT 2273 advanced electrochemical system (Princeton Applied Research) provided by the Advanced Science Instrument Sharing Center of Southwest Forestry University. References [1] G. Trabanelli Inhibitors an old remedy for a new challenge Corrosion 47 1991 410 419 [2] F. Bentiss M. Traisnel L. Gengembre M. Lagrenée Inhibition of acidic corrosion of mild steel by 3,5-diphenyl-4 H -1,2,4-triazole Appl. Surf. Sci. 161 2000 194 202 [3] J. Cruz R. Martínez J. Genesca E. García-Ochoa Experimental and theoretical study of 1-(2-ethylamino)-2-methylimidazoline as an inhibitor of carbon steel corrosion in acid media J. Electroanal. Chem. 566 2004 111 121 [4] M.H. Wahdan G.K. Gomma Effect of copper cation on electrochemical behaviour of steel in presence of imidazole in acid medium Mater. Chem. Phys. 47 1997 176 183 [5] A.M.S. Abdennaby A.I. Abdulhady S.T. Abu-Oribi H. Saricimen The inhibition action of 1 (benzyl)1-H-4,5-dibenzoyl -1,2,3-triazole on mild steel in hydrochloric acid media Corros. Sci. 38 1996 1791 1800 [6] S.L. Granese B.M. Rosales C. Oviedo J.O. Zerbino The inhibition action of heterocyclic nitrogen organic compounds on Fe and steel in HCl media Corros. Sci. 33 1992 1439 1453 [7] F. Bentiss M. Traisnel L. Gengembre M. Lagrenée A new triazole derivative as inhibitor of the acid corrosion of mild steel: electrochemical studies, weight loss determination, SEM and XPS Appl. Surf. Sci. 152 1999 237 249 [8] L. Wang Inhibition of mild steel corrosion in phosphoric acid solution by triazole derivatives Corros. Sci. 48 2006 608 616 [9] M.A. Quraishi H.K. Sharma 4-Amino-3-butyl-5-mercapto-1,2,4-triazole: a new corrosion inhibitor for mild steel in sulphuric acid Mater. Chem. Phys. 78 2002 18 21 [10] E. García-Ochoa J. Genesca Understanding the inhibiting properties of 3-amino-1,2,4-triazole from fractal analysis Surf. Coat. Tech. 184 2004 322 330 [11] W.H. Li Q. He S.T. Zhang C.L. Pei B.R. Hou Some new triazole derivatives as inhibitors for mild steel corrosion in acidic medium J. Appl. Electrochem. 38 2008 289 295 [12] H.L. Wang R.B. Liu J. Xin Inhibiting effects of some mercapto-triazole derivatives on the corrosion of mild steel in 1. 0 M HCl medium Corros. Sci. 46 2004 2455 2466 [13] F. Bentiss M. Traisnel H. Vezin M. Lagrenée Linear resistance model of the inhibition mechanism of steel in HCl by triazole and oxadiazole derivatives: structure–activity correlations Corros. Sci. 45 2003 371 380 [14] M. Lebrini M. Traisnel M. Lagrenée B. Mernari F. Bentiss Inhibitive properties, adsorption and a theoretical study of 3,5-bis( n -pyridyl)-4-amino-1,2,4-triazoles as corrosion inhibitors for mild steel in perchloric acid Corros. Sci. 50 2008 473 479 [15] F. Bentiss M. Lagrenee M. Traisnel J.C. Hornez The corrosion inhibition of mild steel in acidic media by a new triazole derivative Corros. Sci. 41 1999 789 803 [16] W.H. Li X. Zhao F.Q. Liu B.R. Hou Investigation on inhibition behavior of S-triazole–triazole derivatives in acidic solution Corros. Sci. 50 2008 3261 3266 [17] F. Bentiss C. Jama B. Mernari H. El Attari L. El Kadi M. Lebrini M. Traisnel M. Lagrenée Corrosion control of mild steel using 3,5-bis(4-methoxyphenyl)-4-amino-1,2,4-triazole in normal hydrochloric acid medium Corros. Sci. 51 2009 1628 1635 [18] Z.H. Tao S.T. Zhang W.H. Li B.R. Hou Corrosion inhibition of mild steel in acidic solution by some oxo-triazole derivatives Corros. Sci. 51 2009 2588 2595 [19] G.K. Gomma Corrosion inhibition of steel by benzotriazole in sulphuric acid Mater. Chem. Phys. 55 1998 235 240 [20] Q. Qu S.A. Jiang W. Bai L. Li Effect of ethylenediamine tetraacetic acid disodium on the corrosion of cold rolled steel in the presence of benzotriazole in hydrochloric acid Electrochim. Acta 52 2007 6811 6820 [21] R.M. Hudson T.J. Bulter C.J. Warning The effect of pyrrole-halide mixtures in inhibiting the dissolution of low-carbon steel in sulphuric acid Corros. Sci. 17 1977 571 581 [22] M. Bouklah A. Ouassini B. Hammouti A. El Idrissi Corrosion inhibition of steel in 0. 5 M H2 SO4 by [(2-pyridin-4-ylethyl) thio] acetic acid Appl. Surf. Sci. 250 2005 50 56 [23] A. Ouchrif M. Zegmout B. Hammouti S. El-Kadiri A. Ramdani 1,3-Bis(3-hyroxymethyl-5-methyl-1-pyrazole) propane as corrosion inhibitor for steel in 0. 5 M H2 SO4 solution Appl. Surf. Sci. 252 2005 339 344 [24] G.K. Gomma Corrosion of low-carbon steel in sulphuric acid solution in the presence of pyrazole-halides mixture Mater. Chem. Phys. 55 1998 241 246 [25] M. Abdallah M.M. El-Naggar Cu +2 cation + 3,5-dimethyl pyrazole mixture as a corrosion inhibitor for carbon steel in sulfuric acid solution Mater. Chem. Phys. 71 2001 291 298 [26] M. Elayyachy M. Elkodadi A. Aouniti A. Ramdani B. Hammouti F. Malek A. Elidrissi New bipyrazole derivatives as corrosion inhibitors for steel in hydrochloric acid solutions Mater. Chem. Phys. 93 2005 281 285 [27] K. Tebbji A. Aouniti M. Benkaddour H. Oudda I. Bouabdallah B. Hammouti A. Ramdani New bipyrazolic derivatives as corrosion inhibitors of steel in 1 M HCl Prog. Org. Coat. 54 2005 170 174 [28] F. Zucchi G. Trabanelli G. Brunoro C. Monticelli G. Rocchini Corrosion inhibition of carbon and low-alloy steel in sulfuric acid solutions by 2-mercaptopyrimidine derivatives Mater. Corros. 44 1993 264 268 [29] A. Chetouani A. Aouniti B. Hammouti N. Benchat T. Benhadda S. Kertit Corrosion inhibitors for iron in hydrochloride acid solution by newly synthesised pyridazine derivatives Corros. Sci. 45 2003 1675 1684 [30] M. Bouklah N. Benchat A. Aouniti B. Hammouti M. Benkaddour M. Lagrenée H. Vezin F. Bentiss Effect of the substitution of an oxygen atom by sulphur in a pyridazinic molecule towards inhibition of corrosion of steel in 0.5M H2 SO4 medium Prog. Org. Coat. 51 2005 118 124 [31] M. Bouklah N. Benchat B. Hammouti A. Aouniti Thermodynamic characterization of steel corrosion inhibitor adsorption of pyridazine compounds in 0.5 M H2SO4 Mater. Lett. 60 2006 1901 1905 [32] G. Moretti G. Quartarone A. Tassan A. Zingales 5-amino and 5-chloro-indole as mild steel corrosion inhibitors in 1N sulphuric acid Electrochim. Acta 41 1996 1971 1980 [33] A.A. Ismail S.H. Sanad A.A. El-Meligi Inhibiting effect of indole and some of its derivatives on corrosion of C-steel in HCl J. Mater. Sci. Technol. 16 2000 397 400 [34] L. Wang Evaluation of 2-mercaptobenzimidazole as corrosion inhibitor for mild steel in phosphoric acid Corros. Sci. 43 2001 2281 2289 [35] A. Popova M. Christov T. Deligeorigiev Influence of the Molecular Structure on the inhibitor properties of benzimidazole derivatives on mild steel corrosion in 1 M hydrochloric acid Corrosion 59 2003 756 764 [36] A. Popova M. Christov S. Raicheva E. Sokolova Adsorption and inhibitive properties of benzimidazole derivatives in acid mild steel corrosion Corros. Sci. 46 2004 1333 1350 [37] K.F. Khaled The inhibition of benzimidazole derivatives on corrosion of iron in1 M HCl solutions Electrochim. Acta 48 2003 2493 2503 [38] M.H. Wahdan The synergistic inhibition effect and thermodynamic properties of 2-mercaptobenzimidazol and some selected cations as a mixed inhibitor for pickling of mild steel in acid solution Mater. Chem. Phys. 49 1997 135 140 [39] L.B. Tang X.M. Li Y.S. Si G.N. Mu G.H. Liu The synergistic inhibition between 8-hydroxyquinoline chloride ion for the corrosion of cold rolled steel in 0.5 M sulfuric acid Mater. Chem. Phys. 95 2006 29 38 [40] Y. Yan W.H. Li L.K. Cai B.R. Hou Electrochemical and quantum chemical study of purines as corrosion inhibitors for mild steel in 1M HCl solution Electrochim. Acta 53 2008 5953 5960 [41] X.H. Li S.D. Deng H. Fu T.H. Li Adsorption inhibition of 6-benzylaminopurine on cold rolled steel in 1.0 M HCl Electrochim. Acta 54 2009 4089 4098 [42] X.H. Li S.D. Deng H. Fu G.N. Mu Inhibition effect of 6-benzylaminopurine on the corrosion of cold rolled steel in H 2 SO 4 solution Corros. Sci. 51 2009 620 634 [43] E. Bensajjay S. Alehyen M. El Achouri S. Kertit Corrosion inhibition of steel by 1-phenyl-5-mercapto 1.2,3,4-tetrazole in acidic environments (0.5 M H 2 SO 4 1/3 M H 3 PO 4 ) Anti-Corros. Meth. Mater. 50 2003 402 409 [44] P. Morales-Gil G. Negrón-Silva M. Romero-Romoa C. Ángeles-Chávez M. Palomar-Pardavé Corrosion inhibition of pipeline steel grade API 5L X52 immersed in 1 M H 2 SO 4 aqueous solution using heterocyclic organic molecules Electrochim. Acta 49 2004 4733 4741 [45] X.H. Li S.D. Deng H. Fu Corrosion inhibition of red tetrazolium for cold rolled steel in hydrochloric acid media Chin. J. Appl. Chem. 26 2009 1075 1079 in Chinese [46] X.H. Li S.D. Deng H. Fu Synergism between red tetrazolium and uracil on the corrosion of cold rolled steel in H 2 SO 4 solution Corros. Sci. 51 2009 1344 1355 [47] X.H. Li S.D. Deng H. Fu Synergistic inhibition effect of red tetrazolium and uracil on the corrosion of cold rolled steel in H 3 PO 4 solution: weight loss, electrochemical, and AFM approaches Mater. Chem. Phys. 115 2009 815 824 [48] X.H. Li S.D. Deng H. Fu Blue tetrazolium as a novel corrosion inhibitor for cold rolled steel in hydrochloric acid solution Corros. Sci. 52 2010 2786 2792 [49] S.D. Deng X.H. Li H. Fu Nitrotetrazolium blue chloride as a novel corrosion inhibitor of steel in sulfuric acid solution Corros. Sci. 52 2010 3840 3846 [50] M. Bouklah A. Attayibat S. Kertit A. Ramdani B. Hammouti A pyrazine derivative as corrosion inhibitor for steel in sulphuric acid solution Appl. Surf. Sci. 242 2005 399 406 [51] M. Kissi M. Bouklah B. Hammouti M. Benkaddour. Establishment of equivalent circuits from electrochemical impedance spectroscopy study of corrosion inhibition of steel by pyrazine in sulphuric acidic solution Appl. Surf. Sci. 252 2005 4190 4197 [52] S.D. Deng X.H. Li H. Fu Two pyrazine derivatives as inhibitors of the cold rolled steel corrosion in hydrochloric acid solution Corros. Sci. 53 2011 822 828 [53] E. Cano J.L. Polo A. La Iglesia J.M. Bastidas A study on the adsorption of benzotriazole on copper in hydrochloric acid using the inflection point of the isotherm Adsorption 10 2004 219 225 [54] F. Bentiss M. Lebrini M. Lagrenée Thermodynamic characterization of metal dissolution and inhibitor adsorption processes in mild steel/2,5-bis(n-thienyl)-1,3,4-thiadiazoles/hydrochloric acid system Corros. Sci. 47 2005 2915 2931 [55] A. Yurt S. Ulutas H. Dal Electrochemical and theoretical investigation on the corrosion of aluminium in acidic solution containing some Schiff bases Appl. Surf. Sci. 253 2006 919 925 [56] P.C. Okafor Y.G. Zheng Synergistic inhibition behaviour of methylbenzyl quaternary imidazoline derivative and iodine ions on mild steel in H2SO4 solutions Corros. Sci. 51 2009 850 859 [57] C. Cao On electrochemical techniques for interface inhibitor research Corros. Sci. 38 1996 2073 2082 [58] N. Labjar M. Lebrini F. Bentiss N.E. Chihib S. El Hajjaji C. Jama Corrosion inhibition of carbon steel and antibacterial properties of aminotris-(methylnephosnic) acid Mater. Chem. Phys. 119 2010 330 336 [59] M. Lagrenée B. Mernari M. Bouanis M. Traisnel F. Bentiss Study of the mechanism and inhibiting efficiency of 3,5-bis(4-metylthiophenyl)-4H-1,2,4-triazole on mild steel corrosion in acidic media Corros. Sci. 44 2002 573 588 [60] A.K. Singh M.A. Quraishi Effect of Cefazolin on the corrosion of mild steel in HCl solution Corros. Sci. 52 2010 152 160 [61] M. Lebrini M. Lagrenée H. Vezin M. Traisnel F. Bentiss Experimental and theoretical study for corrosion inhibition of mild steel in normal hydrochloric acid solution by some new macrocyclic polyether compounds Corros. Sci. 49 2007 2254 2269 [62] A.R.S. Priya V.S. Muralidharam A. Subramania Development of novel acidizing inhibitors for carbon steel corrosion in 15% boiling hydrochloric acid Corrosion 64 2008 541 552 [63] P. Bommersbach C. Alemany-Dumont J.P. Millet B. Normand Hydrodynamic effect on the behaviour of a corrosion inhibitor film: Characterization by electrochemical impedance spectroscopy Electrochim. Acta 51 2006 4011 4018 [64] D.P. Schweinsberg V. Ashworth The inhibition of the corrosion of pure iron in 0.5 M sulphuric acid by n -alkyl quaternary ammonium iodides Corros. Sci. 28 1988 539 545 [65] S.C. Roy S.K. Roy S.C. Sircar Critique of inhibitor evaluation by polarization measurement Br. Corro. J. 32 1988 102 104 [66] F. Bentiss M. Traisnel M. Lagrenée The substituted 1,3,4-oxadiazoles: a new class of corrosion inhibitors of mild steel in acidic media Corros. Sci. 42 2000 127 146 [67] C.A. Kilner M.A. Halcrow An iron(II) complex of 26-di(pyrazol-1-yl)pyrazine that crystallises in three forms, two of which exhibit an unusual angular Jahn–Teller distortion Polyhedron 25 2006 235 240 [68] L. Beaufort F. Benvenuti A.F. Noels Iron(II)–ethylene polymerization catalysts bearing 2,6-bis(imino)pyrazine ligands: part I. Synthesis and characterization J. Mol. Catal. A-Chem. 260 2006 210 214 [69] N. Hackerman H. Kaesche Corrosion inhibition by organic amines J. Electrochem. Soc. 105 1958 191 198 [70] B. Hong Y.Q. Qiu DFT study on electronic structures pyrazine derivatives with donor and acceptor group J. Molecu. Sci. 20 2004 54 58 in Chinese [71] Y.Q. Qiu H.Y. Yu Z.M. Su L. Zhao R.S. Wang Y.L. Zhu Teheoretial studies on electronic spectrum and third-order nonlinear optical properties of centrosymmetric pyrazine derivatives Chem. J. Chine. Univ. 25 2004 2335 2338 in Chinese