Two pyrazine derivatives as inhibitors of the cold rolled steel corrosion in hydrochloric acid solution

Shuduan Deng,Xianghong Li,Hui Fu

DOI: https://doi.org/10.1016/j.corsci.2010.11.019

IF: 7.72

2011-01-01

Corrosion Science

Abstract:The inhibition effect of two pyrazine derivatives of 2-aminopyrazine (AP) and 2-amino-5-bromopyrazine (ABP) on the corrosion of cold rolled steel (CRS) in 1.0 M hydrochloric acid (HCl) was studied by weight loss, potentiodynamic polarization curves, and electrochemical impedance spectroscopy (EIS) methods. The results show that both AP and ABP are good inhibitors, and inhibition efficiency follows the order: ABP > AP. The adsorption of each inhibitor on CRS surface obeys Langmuir adsorption isotherm. Potentiodynamic polarization curves show that two pyrazine derivatives act as mixed-type inhibitors. EIS spectra exhibit one capacitive loop and confirm the inhibitive ability. Keywords A. Steel B. EIS B. Polarization B. Weight loss C. Acid inhibition 1 Introduction The use of inhibitors is one of the most practical methods for protecting materials against corrosion, especially in acidic media [1] . Most well-known acid inhibitors are organic compounds containing nitrogen, sulfur, and oxygen atoms. Among them, N-heterocyclic compounds are considered to be the most effective corrosion inhibitors [2] . Up to now, various N-heterocyclic compounds are reported as good corrosion inhibitors for iron or steel in acidic media, such as imidazoline derivatives [3–5] , 1,2,3-triazole derivatives [6] , 1,2,4-triazole derivatives [2,7–19] , benzotriazole [20–23] , pyrrole [24] , pyridine derivatives [25–27] , pyrazole derivatives [28–31] , bipyrazole derivatives [32–34] , pyrimidine derivatives [35] , pyridazine derivatives [36–39] , indole derivatives [40–42] , benzimidazole derivatives [43–47] , quinoline derivatives [48] , purine derivatives [49–51] and tetrazole derivatives [52–58] . It is generally accepted that N-heterocyclic compounds exert their inhibition via adsorption on the metal surface through N heteroatom, as well as those with triple or conjugated double bonds or aromatic rings in their molecular structures. Furthermore, the adsorption of inhibitor on steel/solution interface is influenced by the chemical structures of the inhibitors, the nature and charged surface of metal, the distribution of charge over the whole inhibitor molecule and the type of aggressive media. As another typical kind of N-heterocyclic compound, pyrazine derivatives whose molecules possess the pyrazine ring with two N heteroatoms could also be seemed as good potential inhibitors. However, data regarding the use of pyrazine derivatives as corrosion inhibitors are very poor. Hammouti et al. [59,60] investigated the inhibition of diethyl pyrazine-2,3-dicarboxylate on the corrosion of steel in 0.5 M H 2 SO 4 , and its maximum inhibition efficiency ( E ) was about 82% at 1 × 10 −2 M. As ordinary pyrazine derivatives, 2-aminopyrazine (AP, C 4 H 5 N 3 ) and 2-amino-5-bromopyrazine (ABP, C 4 H 4 N 3 Br) have good solubility in water, and can be seemed as the good potential inhibitors owing to two N atoms in pyrazine ring and one substitution—NH 2 group. Up to now, to our best of knowledge, both AP and ABP have not yet been investigated as corrosion inhibitors. By considering the remarks mentioned above, in the present work, the inhibition effect of AP and ABP on the corrosion of cold rolled steel (CRS) in 1.0 M hydrochloric acid (HCl) solution was studied for the first time using weight loss, potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS) methods. The adsorption mode of inhibitor on steel surface and the adsorption free energy Δ G 0 was obtained. Meanwhile, the difference in inhibition performance between AP and ABP is discussed. A probable inhibitive mechanism is presented to explain the results. 2 Experimental 2.1 Materials Tests were performed on a cold rolled steel (CRS) of the following composition (wt.%): 0.07% C, 0.3% Mn, 0.022% P, 0.010% S, 0.01% Si, 0.030% Al, and the remainder Fe. 2.2 Inhibitors The pyrazine derivatives of 2-aminopyrazine (AP) and 2-amino-5-bromopyrazine (ABP) were obtained from Shanghai Chemical Reagent Company of China. Fig. 1 shows the molecular structures of AP and ABP. 2.3 Solutions The aggressive solution of 1.0 M HCl was prepared by dilution of AR grade 37% HCl with distilled water. The concentration range employed for AP or ABP was 0.1–1.0 mM (1.0 × 10 −4 —1.0 × 10 −3 M). 2.4 Weight loss measurements The CRS sheets of 2.5 cm × 2.0 cm × 0.06 cm were abraded by a series of emery paper (grade 320–500–800) and then washed with distilled water, degreased with acetone, and finally dried at room temperature. The samples were stored dry for about 12 h before the start of immersion in test solution. After weighing accurately by digital balance with sensitivity of ±0.1 mg, the specimens were immersed in beaker containing 250 ml 1.0 M HCl without and with different concentrations of inhibitor using glass hooks and rods. The temperature was controlled at 25 ± 0.1 °C using a water thermostat. All the aggressive acid solutions were open to air. After immersion for 24 h, the specimens were taken out, washed with bristle brush under running water to remove the corrosion product, dried with a hot air stream, and re-weighed accurately. In order to get good reproducibility, experiments were carried out in triplicate. The average weight loss of three parallel CRS sheets was obtained. The corrosion rate ( v ) is calculated by the following equation [56] : (1) v = W St where W is the average weight loss of three parallel CRS sheets, S the total area of one CRS specimen, and t is immersion time. With the corrosion rate calculated, the inhibition efficiency ( E w ) is determined as follows: (2) E w % = v 0 - v v 0 × 100 where v 0 and v are the values of corrosion rate without and with inhibitor, respectively. 2.5 Electrochemical measurements Electrochemical experiments were carried out in the conventional three-electrode cell with a platinum counter electrode (CE) and a saturated calomel electrode (SCE) coupled to a fine Luggin capillary as the reference electrode. In order to minimize ohmic contribution, the Luggin capillary was placed close to working electrode (WE) which was in the form of a square CRS embedded in PVC holder using epoxy resin so that the flat surface was only surface in the electrode. The working surface area was 1.0 cm × 1.0 cm, abraded with emery paper (grade 320–500–800) on test face, rinsed with distilled water, degreased with acetone, and dried with a cold air stream. Before measurement the electrode was immersed in test solution at open circuit potential (OCP) for 2 h to be sufficient to attain a stable state. All electrochemical measurements were carried out at 25 °C using PARSTAT 2273 advanced electrochemical system (Princeton Applied Research). Each experiment was repeated at least three times to check the reproducibility. The potential of potentiodynamic polarization curves was increased at 0.5 mV s −1 and started from a potential of −250 mV to +250 mV vs. OCP. Inhibition efficiency ( E p %) is defined as: (3) E p % = i corr - i corr(inh) i corr × 100 where i corr and i corr(inh) represent corrosion current density values without and with inhibitor, respectively. Electrochemical impedance spectroscopy (EIS) was carried out after 2 h of immersion time at OCP in the frequency range of 10 mHz–100 kHz using a 10 mV peak-to-peak voltage excitation. Inhibition efficiency ( E R %) is defined as: (4) E R % = R t(inh) - R t(0) R t(inh) × 100 where R t(0) and R t(inh) are charge transfer resistance values in the absence and presence of inhibitor, respectively. 3 Results and discussion 3.1 Weight loss measurements 3.1.1 Effect of AP and ABP on corrosion rate The weight loss method of monitoring corrosion rate and inhibition efficiency is useful because of its good reliability [61] . For the present study, the reproducibility of results obtained for both corrosion rate and percentage inhibition efficiency values for triplicate determination was very precise (within range of ±5%). Table 1 shows the results for the corrosion rate ( v ) of cold rolled steel (CRS) in 1.0 M HCl at 25 °C in the absence and presence of AP or ABP. The corrosion rate decreases as the concentration of the inhibitor increases due to the fact that the adsorption coverage increases, which shields the CRS surface efficiently from the medium [62] . In the presence of 1.0 mM AP or ABP, the corrosion rate values are decreased to 0.75 and 0.28 g m −2 h −1 , respectively. At any given inhibitor concentration, the corrosion rate follows the order: v (ABP) < v (AP), which indicates that ABP exhibits better inhibitive performance than AP. 3.1.2 Effect of AP and ABP on inhibition efficiency Values of inhibition efficiency obtained from the weight loss ( E w ) for AP and ABP at different concentrations in 1.0 M HCl solution at 25 °C are shown in Fig. 2 . When the concentration of inhibitor is less than 0.50 mM, E w increases sharply with an increase in concentration, while a further increase causes no appreciable change in performance, and reaches up to a limiting value. The maximum E w values are 95.1% (AP) and 97.4% (ABP) at 1.0 mM (1.0 × 10 −3 M). The inhibition is estimated to be 80.8% for AP, and 88.3% for ABP even at very low concentration (0.1 mM); and at 0.5 mM concentration the protection is higher than 90% for AP, and 96% for ABP, which indicates that both AP and ABP are very good inhibitors for steel in 1.0 M HCl. At the same inhibitor concentration, E w values follow the order: E w (ABP) > E w (AP). 3.1.3 Adsorption isotherm and standard adsorption free energy Basic information on the interaction between inhibitor and metal surface can be provided by the adsorption isotherm. Attempts were made to fit experimental data to various isotherms including Frumkin, Langmuir, Temkin, Freundlich, Bockris–Swinkels, and Flory–Huggins isotherms. By far the results were best fitted by Langmuir adsorption isotherm equation [56] : (5) c θ = 1 K + c where c is the concentration of inhibitor, K the adsorption equilibrium constant, and θ is the surface coverage calculated as follows [56] : (6) θ = v 0 - v v 0 Plots of c / θ against c yield straight lines as shown in Fig. 3 , and the linear regression parameters are listed in Table 2 . Both linear correlation coefficient ( r ) and slope are very close to 1, indicating the adsorption of both inhibitors on steel surface obeys the Langmuir adsorption isotherm. Inspection of Table 2 reveals that K of ABP is higher than that of AP, which confirms that ABP exhibits a stronger tendency to adsorb on steel surface than AP. The adsorption equilibrium constant ( K ) is related to the standard free energy of adsorption (Δ G 0 ) as shown the following equation [63] : (7) K = 1 55.5 exp - Δ G 0 RT where R is the gas constant (8.314 J K −1 mol −1 ), T the absolute temperature ( K ), and the value 55.5 is the concentration of water in solution expressed in M [63] . The Δ G 0 values are also given in Table 2 . The negative values of Δ G 0 indicate that the adsorption of inhibitor molecule on steel surface is a spontaneous process. Generally, values of Δ G 0 up to −20 kJ mol −1 are consistent with the electrostatic interaction between the charged molecules and the charged metal (physical adsorption) while those more negative than −40 kJ mol −1 involve sharing or transfer of electrons from the inhibitor molecules to the metal surface to form a co-ordinate type of bond (chemisorption) [64] . In the present study, the value of Δ G 0 is found to be within the range from −40 to −20 kJ mol −1 ; probably means that the adsorption of either AP or ABP on CRS surface involves both physical adsorption and chemical adsorption. 3.2 Potentiodynamic polarization studies Potentiodynamic polarization curves for CRS in 1.0 M HCl containing AP and ABP at 25 °C are shown in Figs. 4 and 5 , respectively. In both cases, addition of either compound causes a remarkable decrease in the corrosion rate i.e., shifts the both anodic and cathodic curves to lower current densities. In other words, both cathodic and anodic reactions of CRS electrode are drastically inhibited. The electrochemical corrosion parameters including corrosion current densities ( i corr ), corrosion potential ( E corr ), cathodic Tafel slope ( b c ), anodic Tafel slope ( b a ), and corresponding inhibition efficiency ( E p ) are listed in Table 3 . It is apparent that i corr decreases considerably in the presence of each inhibitor, and decreases with increasing the inhibitor concentration. Correspondingly, E p increases with the inhibitor concentration, due to the increase in the blocked fraction of the electrode surface by adsorption. E p of 0.50 mM inhibitor reaches up to a maximum of 92.8% for AP; and 95.5% for ABP. Inspection of Table 3 reveals that both AP and ABP are good inhibitors in 1.0 M HCl, and E p follows the order: ABP > AP. The presence of AP or ABP does not prominently shift the corrosion potential, which indicates both studied pyrazine derivatives act as mixed-type inhibitors [65] . Furthermore, in the presence of either compound, the slight change of both b c and b a indicates that the corrosion mechanism of steel does not change. These results indicate that these inhibitors act by simple blocking the available surface area [65] . In the other words, these inhibitors decrease the surface area for corrosion without affecting the mechanism of corrosion and only cause inactivation of a part of the metal surface with respect to the corrosive medium. 3.3 Electrochemical impedance spectroscopy (EIS) Figs. 6 and 7 represent the Nyquist diagrams for CRS in 1.0 M HCl in the presence of AP and ABP at 25 °C, respectively. Clearly, all the impedance spectra exhibit one single depressed semicircle, which indicates that the corrosion of steel is mainly controlled by a charge transfer process, and usually related to the charge transfer of the corrosion process and double layer behavior. In the presence of both inhibitors, comparing with blank solution, the shape is maintained throughout all tested concentrations, indicating that almost no change in the corrosion mechanism occurs due to the inhibitor addition [66] . These capacitive loops are not perfect semicircles which can be attributed to the frequency dispersion effect as a result of the roughness and inhomogeneousness of electrode surface [67] . Furthermore, the diameter of the capacitive loop in the presence of inhibitor is bigger than that in the absence of inhibitor (blank solution) and increases with the inhibitor concentration. This indicates that the impedance of inhibited substrate increases with the inhibitor concentration. The EIS results are simulated by the equivalent circuit shown in Fig. 8 to pure electric models that could verify or rule out mechanism models and enable the calculation of numerical values corresponding to the physical and/or chemical properties of the electrochemical system under investigation [68] . The circuit employed allows the identification of both solution resistance ( R s ) and charge transfer resistance ( R t ). It is worth mentioning that the double layer capacitance ( C dl ) value is affected by imperfections of the surface, and that this effect is simulated via a constant phase element (CPE) [69] . The CPE is composed of a component Q dl and a coefficient a. The parameter a quantifies different physical phenomena like surface inhomogeneousness resulting from surface roughness, inhibitor adsorption, porous layer formation, etc. Therefore, the capacitance is deduced from the following relation [70] : (8) C dl = Q dl × ( 2 π f max ) a - 1 where f max represents the frequency at which imaginary value reaches a maximum on the Nyquist plot. The electrochemical parameters of R t , C dl and E R are calculated by ZSimpWin software and presented in Table 4 . Inspection of Table 4 reveals that R t value increases prominently while C dl reduces with the concentration of inhibitor. A large charge transfer resistance is associated with a slower corroding system. In contrast, better protection provided by an inhibitor can be associated with a decrease in capacitance of the metal. At any given inhibitor concentration, R t (AP) < R t (AP), while C dl (AP) > C dl (ABP). These results imply that ABP shows better inhibition than AP. The decrease in C dl in comparing with that in blank solution (without inhibitor), which can result from a decrease in local dielectric constant and/or an increase in the thickness of the electrical double layer, suggests that the inhibitor molecules function by adsorption at the metal/solution interface [70] . E R increases with the concentration of inhibitor, and follows the order: E R (ABP) > E R (AP). The maximum E R values are 93.0% and 96.0% for AP and ABP, respectively. These results again confirm that both AP and ABP exhibit good inhibitive performance for CRS in hydrochloric acid solution, and it is more efficient to inhibit the corrosion of steel for ABP than AP. Inhibition efficiencies obtained from weight loss ( E w ), potentiodynamic polarization curves ( E p ) and EIS ( E R ) are in good reasonably agreement. 3.4 Explanation for inhibition The inhibition mechanism can be proposed from the adsorption of inhibitor on steel surface. In general, owing to the complex nature of adsorption and inhibition of a given inhibitor, it is impossible for single adsorption mode between inhibitor and metal surface. In the present system, based on the chemical structures of AP and ABP, they have many active sites for the adsorption process. Thus, five types of adsorption may take place in the inhibiting phenomena involving AP and ABP molecules on steel surface as follows: (i) Owing to neutral N atoms in AP and ABP, they can be protonated in the acid solution as following: (9) AP+ x H + ↔ [ APH x ] x + (10) ABP+ x H + ↔ [ ABPH x ] x + Thus, in acidic solutions, the pyrazine derivatives studied exist as [APH x ] x + and [ABPH x ] x + . The charge of the metal surface can be determined from the value of E corr − E q=0 (zero charge potential) [71] . The E q=0 of iron is −530 mV vs. SCE in HCl [72] . In the present system, the value of E corr obtained in 1.0 M HCl is −444.1 mV vs. SCE. So the steel surface charges positive charge in HCl solution because of E corr − E q=0 (zero charge potential) > 0. Since Cl − could be specifically adsorbed, they create an excess negative charge towards the solution and favor more adsorption of the cations [73] , [APH x ] x + and [ABPH x ] x + may adsorb on the negatively charged metal surface. In other words, there may be a synergism between Cl − and protonated inhibitor. (i) Besides to the physical adsorption, AP and ABP may be adsorbed on the metal surface via the chemisorption mechanism, involving to the coordinate bonds that may be formed between the lone electrons pairs of the unprotonated N atoms and the empty orbital of Fe atoms which enhanced the combination intension between the inhibitor molecule and electrode surface. (ii) It is well known that the key adsorption centre of N-heterocyclic compound is N-heterocyclic ring. AP and ABP have plentiful π -electrons owing to pyrazine ring, they can be also adsorbed on the metal surface on the basis of donor–acceptor interactions between π -electrons of the pyrazine rings and vacant d-orbitals of Fe. Once the amino group—NH 2 (donor group) is added, the electron density on the pyrazine ring is increased, and subsequently, it results into the increased adsorbability. (iii) Due to the chelating action of pyrazine, some metal complexes of Fe 2+ —pyrazine compounds [74,75] have been widely prepared. Thus, [APH x ] x + and [ABPH x ] x + may combine with freshly generated Fe 2+ ions on steel surface forming metal inhibitor complexes: (11) Fe → Fe 2 + + 2 e (12) [ APH x ] x + + Fe 2 + ↔ [ APH x - Fe ] ( x + 2 ) + (13) [ ABPH x ] x + + Fe 2 + ↔ [ ABPH x - Fe ] ( x + 2 ) + These complexes might get adsorbed onto steel surface by the van der Waals force to form a blocking barrier to keep CRS from corrosion. (i) A combination of the above. The inhibition efficiency of ABP is higher than that of AP. The results indicate that the substitution Br atom on pyrazine ring of compound ABP increases the inhibition performance in comparison with unsubstituted AP. Similar conclusion is also reported for Schiff bases as corrosion inhibitors in hydrochloric acid [76] . According to the molecular structure of ABP, the substitution Br is negatively charged centre, so it could adsorb on the positively charged steel surface through the electrostatic attraction, and then donate its lone electron pair to the unfilled orbit of Fe atom. Similar views have also been put forward by Hackerman and Kaesche for substitution halides in aromatic amine [77] . In other words, the substitution Br of ABP is the additional centre of adsorption, which causes more adsorption centers and corresponding better inhibition performance than AP. Furthermore, according to some quantum chemical calculations of pyrazine derivations [78,79] , it can be concluded that the additional substitution Br of ABP would also increases the electron density of pyrazine ring, which can facilitate its adsorption on the metal surface so it has higher inhibition efficiency than AP. 4 Conclusions (1) Two pyrazine derivatives of AP and ABP acts as good inhibitors for the corrosion of CRS in 1.0 M HCl solution. Inhibition efficiency ( E w ) increases with the inhibitor concentration, and the maximum E w values are 95.1% (AP) and 97.4% (ABP) at 1.0 mM. Inhibition performance of ABP is always higher than that of AP. (2) For either ABP or AP, the adsorption is a spontaneous process and obeys Langmuir adsorption isotherm. The parameter of adsorption free energy (Δ G 0 ) indicates that the adsorption of inhibitor involves both physical adsorption and chemical adsorption. (3) Both ABP and AP act as mixed-type inhibitors in 1.0 M HCl. EIS spectra exhibit one capacitive loop, and the presence of each inhibitor enhances R t values while reduces C dl values. (4) The adsorption of ABP and AP involves electrostatic attraction between Cl − and protonated inhibitor molecules, sharing electrons between the N atoms and Fe, donor–acceptor interactions between π -electrons of pyrazine rings and vacant d-orbitals of Fe, adsorption of the complexes of [APH x –Fe] ( x +2)+ and [ABPH x –Fe] ( x+ 2)+ . (5) The substitution Br of ABP is the additional centre of adsorption and increases the electron density of pyrazine ring, which can facilitate its adsorption on the metal surface so it has higher inhibition efficiency than AP. Acknowledgements This study was carried out in the scope of research project funded by Key Construction Course of Chemical Engineering for Forest Products of Southwest Forestry University ( XKX200907 ), Applied Fundamental Research Foundation of Yunnan Province ( 2009CD072 ) and Educational Department of Yunnan Province ( 09C0181 ). References [1] G. Trabanelli Inhibitors an old remedy for a new challenge Corrosion 47 1991 410 419 [2] F. Bentiss M. Traisnel L. Gengembre M. Lagrenée Inhibition of acidic corrosion of mild steel by 3, 5-diphenyl-4H–1, 2, 4-triazole Appl. Surf. Sci. 161 2000 194 202 [3] J. Cruz R. Martínez J. Genesca E. García-Ochoa Experimental and theoretical study of 1-(2-ethylamino)-2-methylimidazoline as an inhibitor of carbon steel corrosion in acid media J. Electroanal. Chem. 566 2004 111 121 [4] M.H. Wahdan G.K. Gomma Effect of copper cation on electrochemical behaviour of steel in presence of imidazole in acid medium Mater. Chem. Phys. 47 1997 176 183 [5] G. Bereket E. Hür C. Öğretir Quantum chemical studies on some imidazole derivatives as corrosion inhibitors for iron in acidic medium J. Mol. Struct. (Theochem) 578 2002 79 88 [6] A.M.S. Abdennaby A.I. Abdulhady S.T. Abu-Oribi H. Saricimen The inhibition action of 1 (benzyl)1-H-4, 5-dibenzoyl -1, 2, 3-triazole on mild steel in hydrochloric acid media Corros. Sci. 38 1996 1791 1800 [7] S.L. Granese B.M. Rosales C. Oviedo J.O. Zerbino The inhibition action of heterocyclic nitrogen organic compounds on Fe and steel in HCl media Corros. Sci. 33 1992 1439 1453 [8] F. Bentiss M. Traisnel L. Gengembre M. Lagrenée A new triazole derivative as inhibitor of the acid corrosion of mild steel: electrochemical studies, weight loss determination, SEM and XPS Appl. Surf. Sci. 152 1999 237 249 [9] L. Wang Inhibition of mild steel corrosion in phosphoric acid solution by triazole derivatives Corros. Sci. 48 2006 608 616 [10] M.A. Quraishi H.K. Sharma 4-Amino-3-butyl-5-mercapto-1, 2, 4-triazole: a new corrosion inhibitor for mild steel in sulphuric acid Mater. Chem. Phys. 78 2002 18 21 [11] E. García-Ochoa J. Genesca Understanding the inhibiting properties of 3-amino-1, 2, 4-triazole from fractal analysis Surf. Coat. Tech. 184 2004 322 330 [12] W.H. Li Q. He S.T. Zhang C.L. Pei B.R. Hou Some new triazole derivatives as inhibitors for mild steel corrosion in acidic medium J. Appl. Electrochem. 38 2008 289 295 [13] H.L. Wang R.B. Liu J. Xin Inhibiting effects of some mercapto–triazole derivatives on the corrosion of mild steel in 1.0 M HCl medium Corros. Sci. 46 2004 2455 2466 [14] F. Bentiss M. Traisnel H. Vezin M. Lagrenée Linear resistance model of the inhibition mechanism of steel in HCl by triazole and oxadiazole derivatives: structure–activity correlations Corros. Sci. 45 2003 371 380 [15] M. Lebrini M. Traisnel M. Lagrenée B. Mernari F. Bentiss Inhibitive properties, adsorption and a theoretical study of 3, 5-bis(n-pyridyl)-4-amino-1, 2, 4-triazoles as corrosion inhibitors for mild steel in perchloric acid Corros. Sci. 50 2008 473 479 [16] F. Bentiss M. Lagrenee M. Traisnel J.C. Hornez The corrosion inhibition of mild steel in acidic media by a new triazole derivative Corros. Sci. 41 1999 789 803 [17] W.H. Li X. Zhao F.Q. Liu B.R. Hou Investigation on inhibition behavior of S-triazole–triazole derivatives in acidic solution Corros. Sci. 50 2008 3261 3266 [18] F. Bentiss C. Jama B. Mernari H. El Attari L. El Kadi M. Lebrini M. Traisnel M. Lagrenée Corrosion control of mild steel using 3, 5-bis(4-methoxyphenyl)-4-amino-1, 2, 4-triazole in normal hydrochloric acid medium Corros. Sci. 51 2009 1628 1635 [19] Z.H. Tao S.T. Zhang W.H. Li B.R. Hou Corrosion inhibition of mild steel in acidic solution by some oxo-triazole derivatives Corros. Sci. 51 2009 2588 2595 [20] G.K. Gomma Corrosion inhibition of steel by benzotriazole in sulphuric acid Mater. Chem. Phys. 55 1998 235 240 [21] A. Bellaouchou B. Kabkab A. Guenbour A. Ben Bachir Corrosion inhibition under heat transfer of 9042 stainless steel in phosphoric acid by benzotriazole Prog. Org. Coat. 41 2001 121 127 [22] P. Cao R. Gu Z. Tian Electrochemical and surface enhanced Raman spectroscopy studies on inhibition of iron corrosion by benzotriazole Langmuir 18 2002 7609 7615 [23] Q. Qu S.A. Jiang W. Bai L. Li Effect of ethylenediamine tetraacetic acid disodium on the corrosion of cold rolled steel in the presence of benzotriazole in hydrochloric acid Electrochim. Acta 52 2007 6811 6820 [24] R.M. Hudson T.J. Bulter C.J. Warning The effect of pyrrole-halide mixtures in inhibiting the dissolution of low-carbon steel in sulphuric acid Corros. Sci. 17 1977 571 581 [25] M. Bouklah A. Ouassini B. Hammouti A. El Idrissi Corrosion inhibition of steel in 0.5 M H 2 SO 4 by [(2-pyridin-4-ylethyl) thio] acetic acid Appl. Surf. Sci. 250 2005 50 56 [26] M. Lashkari M.R. Arshadi DFT studies of pyridine corrosion inhibitors in electrical double layer: solvent, substrate, and electric field effects Chem. Phys. 299 2004 131 137 [27] M.A. Veloz I.G. Martinz Effect of some pyridine derivatives on the corrosion behavior of carbon steel in an environmental like NACE TM0177 Corrosion 62 2006 283 292 [28] A. Ouchrif M. Zegmout B. Hammouti S. El-Kadiri A. Ramdani 1, 3-Bis(3-hyroxymethyl-5-methyl-1-pyrazole) propane as corrosion inhibitor for steel in 0.5 M H 2 SO 4 solution Appl. Surf. Sci. 252 2005 339 344 [29] G.K. Gomma Corrosion of low-carbon steel in sulphuric acid solution in the presence of pyrazole–halides mixture Mater. Chem. Phys. 55 1998 241 246 [30] M. Abdallah M.M. El-Naggar Cu +2 cation + 3, 5-dimethyl pyrazole mixture as a corrosion inhibitor for carbon steel in sulfuric acid solution Mater. Chem. Phys. 71 2001 291 298 [31] M. Abdallah Corrosion behaviour of 304 stainless steel in sulphuric acid solutions and its inhibition by some substituted pyrazolones Mater. Chem. Phys. 82 2003 786 792 [32] A. Chetouani B. Hammouti T. Benhadda M. Daoudi Inhibitive action of bipyrazolic type organic compounds towards corrosion of pure iron in acidic media Appl. Surf. Sci. 249 2005 375 385 [33] M. Elayyachy M. Elkodadi A. Aouniti A. Ramdani B. Hammouti F. Malek A. Elidrissi New bipyrazole derivatives as corrosion inhibitors for steel in hydrochloric acid solutions Mater. Chem. Phys. 93 2005 281 285 [34] K. Tebbji A. Aouniti M. Benkaddour H. Oudda I. Bouabdallah B. Hammouti A. Ramdani New bipyrazolic derivatives as corrosion inhibitors of steel in 1 M HCl Prog. Org. Coat. 54 2005 170 174 [35] S.A. Abd El-Maksoud The influence of some arylazobenzoyl acetonitrile derivatives on the behaviour of carbon steel in acidic media Appl. Surf. Sci. 206 2003 129 136 [36] A. Chetouani A. Aouniti B. Hammouti N. Benchat T. Benhadda S. Kertit Corrosion inhibitors for iron in hydrochloride acid solution by newly synthesised pyridazine derivatives Corros. Sci. 45 2003 1675 1684 [37] M. Bouklah N. Benchat A. Aouniti B. Hammouti M. Benkaddour M. Lagrenée H. Vezin F. Bentiss Effect of the substitution of an oxygen atom by sulphur in a pyridazinic molecule towards inhibition of corrosion of steel in 0.5 M H 2 SO 4 medium Prog. Org. Coat. 51 2005 118 124 [38] A. Chetouani B. Hammouti A. Aouniti N. Benchat T. Benhadda New synthesised pyridazine derivatives as effective inhibitors for the corrosion of pure iron in HCl medium Prog. Org. Coat. 45 2002 373 378 [39] M. Bouklah N. Benchat B. Hammouti A. Aouniti Thermodynamic characterization of steel corrosion and inhibitor adsorption of pyridazine compounds in 0.5 M H 2 SO 4 Mater. Lett. 60 2006 1901 1905 [40] G. Moretti G. Quartarone A. Tassan A. Zingales 5-amino and 5-chloro-indole as mild steel corrosion inhibitors in 1N sulphuric acid Electrochim. Acta 41 1996 1971 1980 [41] M. Düdükcü B. Yazici M. Erbil The effect of indole on the corrosion behaviour of stainless steel Mater. Chem. Phys. 87 2004 138 141 [42] A.A. Ismail S.H. Sanad A.A. El-Meligi Inhibiting effect of indole and some of its derivatives on corrosion of C-steel in HCl J. Mater. Sci. Technol. 16 2000 397 400 [43] L. Wang Evaluation of 2-mercaptobenzimidazole as corrosion inhibitor for mild steel in phosphoric acid Corros. Sci. 43 2001 2281 2289 [44] A. Popova M. Christov T. Deligeorigiev Influence of the molecular structure on the inhibitor properties of benzimidazole derivatives on mild steel corrosion in 1 M hydrochloric acid Corrosion 59 2003 756 764 [45] A. Popova M. Christov S. Raicheva E. Sokolova Adsorption and inhibitive properties of benzimidazole derivatives in acid mild steel corrosion Corros. Sci. 46 2004 1333 1350 [46] K.F. Khaled The inhibition of benzimidazole derivatives on corrosion of iron in1 M HCl solutions Electrochim. Acta 48 2003 2493 2503 [47] M.H. Wahdan The synergistic inhibition effect and thermodynamic properties of 2-mercaptobenzimidazol and some selected cations as a mixed inhibitor for pickling of mild steel in acid solution Mater. Chem. Phys. 49 1997 135 140 [48] L.B. Tang X.M. Li Y.S. Si G.N. Mu G.H. Liu The synergistic inhibition between 8-hydroxyquinoline and chloride ion for the corrosion of cold rolled steel in 0.5 M sulfuric acid Mater. Chem. Phys. 95 2006 29 38 [49] Y. Yan W.H. Li L.K. Cai B.R. Hou Electrochemical and quantum chemical study of purines as corrosion inhibitors for mild steel in 1 M HCl solution Electrochim. Acta 53 2008 5953 5960 [50] X.H. Li S.D. Deng H. Fu T.H. Li Adsorption and inhibition of 6-benzylaminopurine on cold rolled steel in 1.0 M HCl Electrochim. Acta 54 2009 4089 4098 [51] X.H. Li S.D. Deng H. Fu G.N. Mu Inhibition effect of 6-benzylaminopurine on the corrosion of cold rolled steel in H 2 SO 4 solution Corros. Sci. 51 2009 620 634 [52] S. Kertit B. Hammouti Corrosion inhibition of iron 1 M HCl by 1-phenyl-5-mercapto-1, 2, 3, 4-tetrazole Appl. Surf. Sci. 93 1996 59 66 [53] E. Bensajjay S. Alehyen M. El Achouri S. Kertit Corrosion inhibition of steel by 1-phenyl-5-mercapto 1, 2, 3, 4-tetrazole in acidic environments (0.5 M H 2 SO 4 and 1/3 M H 3 PO 4 ) Anti-Corros. Meth. Mater. 50 2003 402 409 [54] P. Morales-Gil G. Negrón-Silva M. Romero-Romoa C. Ángeles-Chávez M. Palomar-Pardavé Corrosion inhibition of pipeline steel grade API 5L X52 immersed in 1 M H 2 SO 4 aqueous solution using heterocyclic organic molecules Electrochim. Acta 49 2004 4733 4741 [55] X.H. Li S.D. Deng H. Fu Corrosion inhibition of red tetrazolium for cold rolled steel in hydrochloric acid media Chin. J. Appl. Chem. 26 2009 1075 1079 (in Chinese) [56] X.H. Li S.D. Deng H. Fu Synergism between red tetrazolium and uracil on the corrosion of cold rolled steel in H 2 SO 4 solution Corros. Sci. 51 2009 1344 1355 [57] X.H. Li S.D. Deng H. Fu Synergistic inhibition effect of red tetrazolium and uracil on the corrosion of cold rolled steel in H 3 PO 4 solution: weight loss, electrochemical, and AFM approaches Mater. Chem. Phys. 115 2009 815 824 [58] X.H. Li S.D. Deng H. Fu Blue tetrazolium as a novel corrosion inhibitor for cold rolled steel in hydrochloric acid solution Corros. Sci. 52 2010 2786 2792 [59] M. Bouklah A. Attayibat S. Kertit A. Ramdani B. Hammouti A pyrazine derivative as corrosion inhibitor for steel in sulphuric acid solution Appl. Surf. Sci. 242 2005 399 406 [60] M. Kissi M. Bouklah B. Hammouti M. Benkaddour Establishment of equivalent circuits from electrochemical impedance spectroscopy study of corrosion inhibition of steel by pyrazine in sulphuric acidic solution Appl. Surf. Sci. 252 2005 4190 4197 [61] I.B. Obot N.O. Obi-Egbedi Adsorption properties and inhibition of mild steel corrosion in sulphuric acid solution by ketoconazole: experimental and theoretical investigation Corros. Sci. 52 2010 198 204 [62] X.H. Li G.N. Mu Tween-40 as corrosion inhibitor for cold rolled steel in sulphuric acid: weight loss study, electrochemical characterization, and AFM Appl. Surf. Sci. 252 2005 1254 1265 [63] E. Cano J.L. Polo A. La Iglesia J.M. Bastidas A study on the adsorption of benzotriazole on copper in hydrochloric acid using the inflection point of the isotherm Adsorption 10 2004 219 225 [64] F. Bentiss M. Lebrini M. Lagrenée Thermodynamic characterization of metal dissolution and inhibitor adsorption processes in mild steel/2, 5-bis(n-thienyl)-1, 3, 4-thiadiazoles/hydrochloric acid system Corros. Sci. 47 2005 2915 2931 [65] C. Cao On electrochemical techniques for interface inhibitor research Corros. Sci. 38 1996 2073 2082 [66] N. Labjar M. Lebrini F. Bentiss N.E. Chihib S. El Hajjaji C. Jama Corrosion inhibition of carbon steel and antibacterial properties of aminotris-(methylnephosnic) acid Mater. Chem. Phys. 119 2010 330 336 [67] M. Lebrini M. Lagrenée H. Vezin M. Traisnel F. Bentiss Experimental and theoretical study for corrosion inhibition of mild steel in normal hydrochloric acid solution by some new macrocyclic polyether compounds Corros. Sci. 49 2007 2254 2269 [68] A.R.S. Priya V.S. Muralidharam A. Subramania Development of novel acidizing inhibitors for carbon steel corrosion in 15% boiling hydrochloric acid Corrosion 64 2008 541 552 [69] P. Bommersbach C. Alemany-Dumont J.P. Millet B. Normand Hydrodynamic effect on the behaviour of a corrosion inhibitor film: characterization by electrochemical impedance spectroscopy Electrochim. Acta 51 2006 4011 4018 [70] M. Lagrenée B. Mernari M. Bouanis M. Traisnel F. Bentiss Study of the mechanism and inhibiting efficiency of 3, 5-bis(4-metylthiophenyl)-4H–1, 2, 4-triazole on mild steel corrosion in acidic media Corros. Sci. 44 2002 573 588 [71] D.P. Schweinsberg V. Ashworth The inhibition of the corrosion of pure iron in 0.5 M sulphuric acid by n -alkyl quaternary ammonium iodides Corros. Sci. 28 1988 539 545 [72] G. Banerjee S.N. Malhotra Contribution to adsorption of aromatic amines on mild steel surface from HCl solutions by impedance, UV, and Raman spectroscopy Corrosion 48 1992 10 15 [73] F. Bentiss M. Traisnel M. Lagrenée The substituted 1, 3, 4-oxadiazoles: a new class of corrosion inhibitors of mild steel in acidic media Corros. Sci. 42 2000 127 146 [74] C.A. Kilner M.A. Halcrow An iron(II) complex of 2, 6-di(pyrazol-1-yl)pyrazine that crystallises in three forms, two of which exhibit an unusual angular Jahn–Teller distortion Polyhedron 25 2006 235 240 [75] L. Beaufort F. Benvenuti A.F. Noels Iron(II)–ethylene polymerization catalysts bearing 2, 6-bis(imino)pyrazine ligands: part I. Synthesis and characterization J. Mol. Catal. A-Chem. 260 2006 210 214 [76] A. Yurt S. Ulutas H. Dal Electrochemical and theoretical investigation on the corrosion of aluminium in acidic solution containing some Schiff bases Appl. Surf. Sci. 253 2006 919 925 [77] N. Hackerman H. Kaesche Corrosion inhibition by organic amines J. Electrochem. Soc. 105 1958 191 198 [78] B. Hong Y.Q. Qiu DFT study on electronic structures pyrazine derivatives with donor and acceptor group J. Mol. Sci. 20 2004 54 58 (in Chinese) [79] Y.Q. Qiu H.Y. Yu Z.M. Su L. Zhao R.S. Wang Y.L. Zhu Theoretical studies on electronic spectrum and third-order nonlinear optical properties of centrosymmetric pyrazine derivatives Chem. J. Chine. Univ. 25 2004 2335 2338 (in Chinese)