Abstract:Mesoporous carbon materials with ultra-thin carbon pore walls and highly dispersed Ni nanoparticles have been successfully prepared by using two different SBA-15 silicas as hard templates and 2,3-dihydroxynaphthalene (DHN) as a carbon precursor. The nickel precursor was a concentrated nickel nitrate hexahydrate [Ni(NO3)(2)center dot 6H(2)O] solution in 2-propanol, which was added to the carbon-silica nanocomposite prior to thermal treatment. The samples studied were analyzed by thermogravimetry (TG), nitrogen adsorption at -196 degrees C, powder X-ray diffraction (XRD), Raman spectroscopy, scanning and transmission electron microscopy (STEM), and in situ electron diffraction X-ray spectroscopy (EDX). While TG analysis revealed carbon contents lower than 30 wt.-%, nitrogen adsorption provided information about the homogeneity of the carbon thin film deposited onto the mesopore walls of the ordered silica templates SBA-15. The templates, carbon-silica nanocomposites, and carbon inverse replicas with nickel nanoparticles exhibit uniform pores, high surface areas, and large pore volumes. Partially graphitic carbon was identified by the presence of a characteristic G band in the Raman spectra, whereas the diffraction peak attributed to the stacking of graphene planes was not observed by powder XRD. The presence of ordered domains in the carbon materials studied was confirmed by small angle XRD and STEM imaging. In addition, the STEM images revealed that the nickel nanoparticles are uniform in size, ca. 3 nm, and are homogeneously dispersed on the tubular carbon walls. A few larger clusters of nickel, ca. 60 nm, present on the external surface, were identified by powder XRD as metallic Ni. The in situ EDX revealed that the small nanoparticles are largely composed of Ni with traces of NiO. Similar nanoparticle dispersions have been reported only for Ni-containing multiwalled carbon nanotubes (CNTs), whereas previously reported ordered mesoporous carbon materials, CMK-3, possess larger Ni/NiO nanoparticles. ((C) Wiley-VCH Verlag GmbH & Co. KGaA, 69451 Weinheim, Germany, 2009)

Non-aqueous sol–gel preparation of carbon-supported nickel nanoparticles

Sol–gel process of carbon-supported nickel nanoparticles using different solvents and protecting atmospheres

Sol-Gel Preparation, Characterization and Hydrogenation Property of Silica Supported Ni Catalyst

Synthesis of iron–nickel nanoparticles via a nonaqueous organometallic route

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

Preparation and magnetic properties of nickel nanoparticles via the thermal decomposition of nickel organometallic precursor in alkylamines

Preparation of Nickel and Ni3Sn Nanoparticles Via Extension of Conventional Citric Acid and Ethylene Diamine Tetraacetic Acid Mediated Sol–gel Method

Lactic Acid Based Sol–gel Process of Ag Nanoparticles and Crystalline Phase Control of Ni Particles in Aqueous Sol–gel Process

Non‐Aqueous Sol–Gel Approach Towards the Controllable Synthesis of Nickel Nanospheres, Nanowires, and Nanoflowers

A Novel Sol–gel Process to Facilely Synthesize Ni3Fe Nanoalloy Nanoparticles Supported with Carbon and Silica

Acrylamide And Lactic Acid-Based Sol-Gel Process For The Preparation Of Silver And Nickel Nanoparticles Under A N-2 Protecting Atmosphere

Facile synthesis of nickel nanoparticles supported on carbon and silica matrix via a novel silica sol–gel process

Sol-gel preparation and characterization of NiCo and Ni3Fe nanoalloys

Pure Face-Centered-cubic (fcc) and Hexagonal-Close-packed (hcp) Nickel Phases Obtained in Air Atmosphere Sol–gel Process and Fcc Nickel Phase Obtained in N2 Protected Sol–gel Process

Mesoporous Carbon Materials with Ultra‐Thin Pore Walls and Highly Dispersed Nickel Nanoparticles

Preparation of hexagonal close-packed nickel nanoparticles via a thermal decomposition approach using nickel acetate tetrahydrate as a precursor

Synthesis of NiO nanowires by a sol-gel process

Sol–gel preparation of crystalline Ni 12 P 5 /N-doped carbon and amorphous Ni–P–C catalysts and their high catalytic performances toward hydrogenation reduction reaction of 4-nitrophenol

Unsupported and silica-supported nickel nanoparticles: synthesis and application in catalysis

Controllable Synthesis of Hexagonal Close-Packed Nickel Nanoparticles under High Nickel Concentration and Its Catalytic Properties

In Situ Thermal Atomization to Convert Supported Nickel Nanoparticles into Surface‐Bound Nickel Single‐Atom Catalysts