Abstract:Abstract Due to the high conductivity and stability of silver, silver ink has been widely used in the field of printed electronics. However, since mechanical strain would cause the contact between key particles to be broken. Recently, higher requirements have been put on the bending resistance of silver paste. In this experiment, by preparing Ag NPs: Ag Flakes composite materials of 20:80 and 30:70 respectively, a new method for preparing stable modified flake silver powder is proposed, and the attachment and growth methods of Ag NPs reduced on micron flake silver powder is discussed. Flake silver powder, dispersant and reducing agent are added to the silver-ammonia complex, and the nano-silver particles are reduced on the flake silver powder by controlling the reaction conditions. When Ag + : Ag Flakes in the solution is 30:70, there is a clear interface between the silver particles and the silver flakes, and the size distribution range is between 10 and 100 nm; when Ag + : Ag Flakes is 20:80, the distance between the nano-silver particles and the silver plate crystal plane is about 0.222 nm and 0.260 nm, these spacings represent the (1–12) and (004) planes of Ag, respectively. The reduced silver particles grow on the surface of the silver sheet, the size is about 5 ∼ 60 nm, and form a sheet-point combination of shaped silver powder, which can be used to make conductive silver paste with cost and performance competitiveness. The reaction can be completed at room temperature (5 ∼ 25 °C) and atmospheric pressure (80 ∼ 100 kPa), the operation is simple, the reaction time is short, and it has a positive effect on the commercial production of printable highly conductive silver paste.

Acrylamide And Lactic Acid-Based Sol-Gel Process For The Preparation Of Silver And Nickel Nanoparticles Under A N-2 Protecting Atmosphere

Lactic Acid Based Sol–gel Process of Ag Nanoparticles and Crystalline Phase Control of Ni Particles in Aqueous Sol–gel Process

Synthesis of iron–nickel nanoparticles via a nonaqueous organometallic route

Sol–gel process of carbon-supported nickel nanoparticles using different solvents and protecting atmospheres

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

Non-aqueous sol–gel preparation of carbon-supported nickel nanoparticles

Preparation of Nickel and Ni3Sn Nanoparticles Via Extension of Conventional Citric Acid and Ethylene Diamine Tetraacetic Acid Mediated Sol–gel Method

Electrochemical synthesis of silver oxide nanowires, microplatelets and application as SERS substrate precursors

Non‐Aqueous Sol–Gel Approach Towards the Controllable Synthesis of Nickel Nanospheres, Nanowires, and Nanoflowers

Preparation of Silver Nanoshells on Silica Particles by a Simple Two-step Process

Pure Face-Centered-cubic (fcc) and Hexagonal-Close-packed (hcp) Nickel Phases Obtained in Air Atmosphere Sol–gel Process and Fcc Nickel Phase Obtained in N2 Protected Sol–gel Process

Chemical Synthesis of Monodisperse Fe-Ni Nanoparticles Via A Diffusion-Based Approach

Preparation and study of polyacryamide-stabilized silver nanoparticles through a one-pot process.

A Facile Synthetic Route to Aqueous Dispersions of Silver Nanoparticles

Morphology and Composition Controlled Synthesis of Flower-Like Silver Nanostructures.

Preparation and magnetic properties of nickel nanoparticles via the thermal decomposition of nickel organometallic precursor in alkylamines

Study on the Preparation of Spherical Nanosilver Particles Using Ammonium Citrate and Polyvinyl Alcohol as Surfactants

A Novel Sol–gel Process to Facilely Synthesize Ni3Fe Nanoalloy Nanoparticles Supported with Carbon and Silica

Elucidation of the capillarity-promoted sintering of silver nanoparticles produced by a spark ablation vapor source

Study on the mechanism of forming silver nanoparticles on micron-scale flake silver powder

Preparation and Size Control of Silver Nanoparticles by A Thermal Method