Study on Synthesis of Linear Poly (P-Phenylene Sulfide) Resin with High Molecular Weight ( HMW PPS) and Recycling of Solvent and Additive
MENG Xiao,CHEN Yong,SUN Xiao-yi,JIANG Wen-wei,YANG Qin,LUO Qin
DOI: https://doi.org/10.3969/j.issn.0253-4320.2012.02.009
2012-01-01
Abstract:Uniform design was applied to study the synthesis of linear poly(p-phenylene sulfide) resin with high molecular weight(HMW PPS).The effects of reaction temperature,reaction time,the molar ratio of reaction monomers,the amount of solvent and catalyst on the yield of HMW PPS were investigated.The optimal reaction conditions were found by using multiple regression analysis based on the data obtained from uniform design experiments.The optimized conditions are as follows:210.9℃ and 2.8 hours of reaction temperature and reaction time,respectively,in the early stage,270℃ and 2.5 hours of reaction temperature and reaction time,respectively,in the late stage,1.1∶1 of molar ratio of Na2S·9H2O and para-dichlorobenzene,550 mL ∶1 mol of ratio of NMP and para-dichlorobenzene,and 20 g ∶1 mol of the additive and para-dichlorobenzene.The molecular weight of the obtained HMW PPS is close to 60 000.The product yield is up to 93.7%.Both the solvent and the catalyst can be reused without complex recovering process.After several times of recycling,the yield of the product is still up to 91.2%.The obtained product is characterized by thermal analysis,IR and element analysis.