Abstract:The electrochemical behaviour of different Pb-Ag (0.5, 0.6 and 0.7%) anodes during zinc electro winning has been studied in acid zinc sulphate electrolyte containing Mn2+ at 38 °C, and 50 mA/cm2 by electrochemical noise measurements “ENM” using the zero resistance ammeter set-up (ZRA). During 16 h decay period after 24 h of electrolysis, Pb-0.5% Ag anode had the highest corrosion rate among the three anodes, followed by Pb-0.6%Ag anode and Pb-0.7% Ag anode. It can be observed that at the end of 16 h decay, the 0.7% Ag lead anode had the lowest potential (the most active) followed by 0.6% and 0.5% Ag lead anodes. Also, 0.5% Ag lead anode had the longest first plateau as compared to 0.6% and 0.7% Ag lead anodes. This plateau had higher corrosion rate “1/Rn”, higher slope of ratio “Sr” than that in its following decay period. In addition, at the end of 16 h potential decay, the potential-time record shows that Pb-0.7% Ag anode had several high amplitude and high frequency oscillations with several peak transients; while Pb-0.5% Ag anode had more frequent repetition of fluctuations with smoother potential. Moreover, at the end of 16 h decay, it was also obtained that the absolute magnitudes of the slopes of potential of power spectral densities (PSD) of 0.7% Ag lead anode are also lower than that of 0.5% Ag lead anode. Finally, it can be admitted that 0.5% Ag-Pb anode has more corrosion rate during polarization and this is shown by important plateau at the average value of 1.61 V/SHE for the longest time (45 min); while 0.7% Ag lead anode showed more active galvanic cells at the end of decay (11-16 h) that can correspond to more localized corrosion because of more abundant silver containing phases. Keywords: Corrosion rates, electrochemical noise measurements, Pb-Ag alloy anodes, plateau, potential decay.

Influence of Fluoride and Chromium(Vi) Ions on Corrosion Mechanisms of Pb-3wt% Sn-0.5wt%Ag Anode

Studies of the Surface Reaction Mechanisms of Pb-3 Wt%sn-0.5 Wt%ag Anode in CrO3Solutions

Effects of fluoride and chloride ions on anodic layer and corrosion behavior of Pb-Ag anode

Influence of Fluoride Ion on the Performance of Pb-Ag Anode During Long-Term Galvanostatic Electrolysis

Effect of the Sn-Ag Addition on the Internal Stress Change and Electrochemical Properties of Lead-Based Anodes

Study on Corrosion Process of Lead Alloy Anode in Plating Solution of Tin Free Steel

Influence of Micro-alloyed Pb and Chromate on the Corrosion Behavior of High Voltage Anode Aluminum Foil

Influence of Mn2+ on the Performance of Pb-Ag Anodes in Fluoride/chloride-Containing H2SO4 Solutions

Anodic Passivation of Pb-Ag-Nd Anode in Fluoride-Containing H 2 SO 4 Solution

Influence of Alloy Element Addition on the Nucleation Mechanism of the Lead Alloy Surface and Its Oxide Film Properties

Corrosion Behavior of Lead Alloy Anodes for Copper Electrowinning

Anodic Behavior of Pb-Ag-Ca-Sr Alloy in Zinc Electrowinning

Influence of Fe Ions on Anode Performance and the Mechanism of Action during Copper Electrowinning Process

Study Of The Effect Of The Initial Nucleation Mechanism Of Lead Anode Oxidation Film On Internal Stress In Chromic Acid Electrolyte

Electrochemical Performances of Al/Pb-Ag-Sn Anode for Zinc Electrowinning

Effect of Ag Content and beta-PbO2 Plating on the Properties of Al/Pb-Ag Alloy

Influences of Temperature, H2SO4 Concentration and Sn Content on Corrosion Behaviors of PbSn Alloy in Sulfuric Acid Solution

Influence of Silver Content on Corrosion Resistance of Lead Anodes During Potential Decay by Electrochemical Noise Measurements

Effect of Trace Sn on Corrosion Behaviors of High Voltage Anode Aluminum Foil

Effect of Mn2+ on the anodic film and corrosion behavior of Pb-Ca-Sn alloy anode in copper electrowinning

Effect of Sn Content on the Properties of Passive Film on PbSn Alloy in Sulfuric Acid Solution