Abstract:A structured nanoparticle support was prepared by using diol as precipitant to recrystallize nano-sized MgCl2 on the surface of SiO2.TiCl4 was immobilized on the surface of the resulting structured nanoparticle support,forming structured nanoparticle Ziegler-Natta cataylst.The resulting catalyst was used to catalyze the slurry-phase polymerization of ethylene.Polyethylene produced was characterized with scanning electron microscopy(SEM),differential scanning calorimetry(DSC) and particle size analysis.In order to obtain the proper catalyst,the influence of diol/MgCl2 ratio on support morphology,catalysis features of structured nanoparticle catalyst and characteristics of products were investigated.Results showed that the structured nanoparticle Ziegler-Natta catalyst was an excellent catalyst for producing ultra high molecular weight polyethylene(UHMWPE) because of its special particle morphology.Polymerization activity and molecular weight of products were both sensitive to the temperature.At the optimum temperature,polymerization activity could reach as high as 1261 kg PE·(molTi)-1·h-1·10-5Pa-1 and molecular weight of product could reach as high as 5.87×106.UHMWPE produced with structured nanoparticle Ziegler-Natta catalyst had a high crystallinity degree which could reach 49.5%.It also performed a uniform spherical morphology with an average particle size of 68~69 μm and moreover the distribution of particle size was very narrow.These were all beneficial to the processing of UHMWPE.

The preparation of nanosized polyethylene particles via carbon sphere nanotemplates

PREPARATION OF ULTRA HIGH MOLECULAR WEIGHT POLYETHYLENE USING STRUCTURED NANOPARTICAL ZIEGLER-NATTA CATALYSTS

ETHYLENE POLYMERIZATION WITH CORE-SHELL ZIEGLER-NATTA HYBRID CATALYSTS

Ethylene polymerization with metallocene/late transition metal combined catalysts

The Preparation and Characterization of Carbon Nanosphere/Polyethylene Composites

Advanced Catalyst Technology for Broad/Bimodal Polyethylene, Achieved by Polymer-Coated Particles Supporting Hybrid Catalyst

A new route for preparing magnetic polyolefins with well dispersed nanometer magnetic particles in polymer matrix using supported Fe3O4/AlR3/TiCl4 nanometer magnetic Ziegler-Natta catalyst

Preparation and Characterization of Novel Polyethylene Supported Metallocene Catalysts

Preparation of nanosheet polyethylene with heterogeneous metallocene catalyst and formation mechanism of nanosheet polyethylene.

PREPARATION OF NOVEL POLYETHYLENE-graft-POLY(4-VINYLPYRIDINE)-SUPPORTED METALLOCENE CATALYSTS FOR ETHYLENE POLYMERIZATION

Preparation of Nanopolyethylene Wire with Carbon Nanotubes‐supported Cp2ZrCl2 Catalyst

Nano-Dispersed Ziegler-Natta Catalysts for 1 μm-Sized Ultra-High Molecular Weight Polyethylene Particles

Preparation of nano-polyethylene fibres using Cp2ZrCl2/carbon nanotube catalytic system

Preparation of Regular Polyethylene Hollow Spheres with Supported Z-N Catalysts

Particle Morphology and Morphogenesis of Nascent Polyethylene Produced with a Spherical MgCl2‐supported Ziegler–Natta Catalyst in Slurry Process

MCM-41 and SBA-15 supported Cp2ZrCl2 catalysts for the preparation of nano-polyethylene fibres via in situ ethylene extrusion polymerization

Preparation Of Nano-Polyethylene Fibers By Sba-15-Supported Half-Sandwich Titanium(Iv) Aryloxy Catalyst

Preparation of Nano-polyethylene Fibers by SBA-15-supported Half-sandwich Titanium(Ⅳ) Aryloxy Catalyst

Combination of 8‐aminoquinoline Nickel Dichloride and Cp2ZrCl2 Catalysts for Ethylene Polymerization

Preparation of nano-polyethylene fibres using TiCl4/MCM-41 catalytic system

Research in Morphology of Polypropylene Grafting Maleic Anhydride /sio2 Supported Titanium Catalysts and Polyethylene