Abstract:During service, hot-section components of aircraft engines are subjected to high-temperature gas impacts and erosion. To ensure their normal operation, thermal barrier coatings (TBCs) are applied to their surfaces for thermal protection. However, due to long-term exposure in a thermal-mechanical coupled environment, thermally grown oxides (TGOs) form within the TBCs on these components. As service time increases, the thickness of the TGO increases and, if conditions and stresses exceed critical values cracking and spallation of the TGO will occur. Therefore, studying the microstructural characteristics of TBCs on hot-end components during service is crucial for enhancing the lifespan and performance of aircraft engines. In this study, transmission electron microscopy (TEM) samples containing the interface between TGO and bond coat, as well as interface between TGO and ceramic top coat, were prepared using focused ion beam (FIB) technique. The microstructure characteristics of TBCs during thermal cycling was investigated based on high-resolution transmission electron microscopy (HRTEM) technique. The results reveal a number of microstructural features within the TBC, including nanotwins, stacking faults with different orientations, and nano-sized LPSO phase. In addition, it is revealed that in the presence of Y the TGO formed has an amorphous Al-rich structure whereas where Y is not present a fully crystalline Al 2 O 3 forms. It is postulated that a crystalline-to-amorphous transition occurs in the ceramic topcoat induced by high stress concentration at the interface.

In situ microstructure characterization of ZrO2 coating at high temperature

Microcracks characterization for thermal barrier coatings at high temperature

High Performance Nanostructured ZrO2 Based Thermal Barrier Coatings Deposited by High Efficiency Supersonic Plasma Spraying

Microstructure and thermal behaviour of plasma sprayed zirconia/alumina composite coating

Study of Failure Mechanisms of Thermal Barrier Coatings by Plasma Spraying

Microstructure characteristics and deformation-induced crystalline-to-amorphous phase transformation in thermal barrier coatings during thermal cycling

Experimental Study of the Thermally Grown Oxide and Interface of Thermal Barrier Coatings Using TEM In-Situ Heating

High Temperature Oxidation and Insulation Behavior of Plasma-Sprayed Nanostructured Thermal Barrier Coatings

Atmospheric plasma sprayed thick thermal barrier coatings: Microstructure, thermal shock behaviors and failure mechanism

Thermal shock resistance and failure analysis of La2(Zr0.75Ce0.25)2O7-based TBCs produced by atmospheric plasma spraying

Microstructural and Mechanical Properties of Thermal Barrier Coating at 1400°C Treatment

In-situ synthesized nanostructured t-ZrO2/La2(Zr0.75Ce0.25)2O7 composite thermal barrier coatings

Microstructure and Thermal Properties of Plasma Sprayed Thermal Barrier Coatings from Nanostructured YSZ

Microstructural Design and Properties of Supersonic Suspension Plasma Sprayed Thermal Barrier Coatings

High Temperature In-Situ Synchrotron X-Ray Diffraction Technique of Thermal Barrier Coatings under Thermal Gradient and Mechanical Loads

Oxidation Damage of APS Thermal Barrier Coatings under High Temperature

Multi-scale Phenomena and Structures Observed in Fabrication of Thermal Barrier Coatings by Using Plasma Spraying

Thermophysical properties and thermal cycling behavior of plasma sprayed thick thermal barrier coatings

Microstructure characterization and thermal conductivity analysis of plasma sprayed ZrO 2 coatings

Effect of Microstructure on the Thermal Conductivity of Plasma Sprayed Y2O3 Stabilized Zirconia (8% YSZ)

Effect of spraying ceramic powder pore structure on thermophysical properties of plasma-sprayed thermal barrier coatings