Abstract:In recent years, high-mobility GaSb nanowires have received tremendous attention for high-performance p-type transistors; however, due to the difficulty in achieving thin and uniform nanowires (NWs), there is limited report until now addressing their diameter-dependent properties and their hole mobility limit in this important one-dimensional material system, where all these are essential information for the deployment of GaSb NWs in various applications. Here, by employing the newly developed surfactant-assisted chemical vapor deposition, high-quality and uniform GaSb NWs with controllable diameters, spanning from 16 to 70 nm, are successfully prepared, enabling the direct assessment of their growth orientation and hole mobility as a function of diameter while elucidating the role of sulfur surfactant and the interplay between surface and interface energies of NWs on their electrical properties. The sulfur passivation is found to efficiently stabilize the high-energy NW sidewalls of (111) and (311) in order to yield the thin NWs (i.e., and , whereas the thick NWs (i.e., u003e40 nm in diameters) would grow along the most energy-favorable close-packed planes with the orientation of , supported by the approximate atomic models. Importantly, through the reliable control of sulfur passivation, growth orientation and surface roughness, GaSb NWs with the peak hole mobility of similar to 400 cm(2)Vs(-1) for the diameter of 48 nm, approaching the theoretical limit under the hole concentration of similar to 2.2 x 10(18) cm(-3), can be achieved for the first time. All these indicate their promising potency for utilizations in different technological domains.

Synthesis, Properties, and Top-Gated Metal–oxide–semiconductor Field-Effect Transistors of P-Type GaSb Nanowires

Approaching the Hole Mobility Limit of GaSb Nanowires

Complementary Metal Oxide Semiconductor-Compatible, High-Mobility, ⟨111⟩-Oriented GaSb Nanowires Enabled by Vapor–Solid–Solid Chemical Vapor Deposition

P-Type Zns:N Nanowires: Low-Temperature Solvothermal Doping and Optoelectronic Properties

Antimony‐Rich GaAs x Sb 1− x Nanowires Passivated by Organic Sulfides for High‐Performance Transistors and Near‐Infrared Photodetectors

P-Type Znte:Ga Nanowires: Controlled Doping And Optoelectronic Device Application

Gasb Nanowire Single-Hole Transistor

Stoichiometric effect on electrical and near-infrared photodetection properties of full-composition-range GaAs1−xSbx nanowires

From powder to nanowire: A simple and environmentally friendly strategy for optical and electrical GaN nanowire films

Enhanced thermoelectric figure of merit in thin GaAs nanowires.

Tunable N‐type Conductivity and Transport Properties of Ga‐doped ZnO Nanowire Arrays

Controllable Ga/Ga 2 O 3 Nanowire Growth at High Temperatures Enabled by Au and Pd Quantum Dot Catalysts

Towards low-dimensional hole systems in Be-doped GaAs nanowires

Substrate-Free Chemical Vapor Deposition of Large-Scale III-V Nanowires for High-Performance Transistors and Broad-Spectrum Photodetectors

Synthesis of High Quality N-Type Cds Nanobelts and Their Applications in Nanodevices

One Dimensional Ternary Cu–Bi–S Based Semiconductor Nanowires: Synthesis, Optical and Electrical Properties

Ambipolar Transport in Narrow Bandgap Semiconductor InSb Nanowires

Room temperature device performance of electrodeposited InSb nanowire field effect transistors

Synthesis of high quality p-type Zn3P2 nanowires and their application in MISFETs

Gallium Nitride Nanowire Nanodevices

Doping Dependent Crystal Structures and Optoelectronic Properties of N-Type Cdse:Ga Nanowries