Abstract:As a wide band-gap semiconductor，SnO2 films have attracted much attention due to their novel optical and electronic properties. It has been reported that the physical properties can be quite different when the size of SnO2 is reduced to nanometer scale due to the large surface-to-volume ratio and the quantum size effects，which may be applied in many kinds of devices, such as solar cells sensors. etc. It is interesting to study the synthesis of SnO2 nanoparticles and their physics properties. In the present work，a soft chemical technique was used to prepare SnO2 nanoparticles with uniform size and good crystallization in alkalescent solution. The surfactant was added during the preparation process to control the growth and agglomeration of crystal precipitates in the solution. X-ray diffraction spectra and transmission electron microscopy were used to characterize the structures of SnO2 nanoparticles before and after thermal annealing. It was found that the nanocrystalline SnO2 particles can be formed by the present technique and the size is about 4 nm with good crystallinity. With changing the preparation parameters，the size of nanocrystalline SnO2 particles is changed. Post thermal annealing at various temperatures （400—1000 ℃） can promote the crystallization and the size of formed particles was increased with increasing annealing temperature. Optical absorption spectra were used to see the change of the optical properties for samples prepared under different conditions. It was found that the optical band gap is enlarged in nanocrystalline SnO2 particles compared with its bulk counterpart, which can be attributed to the quantum confinement effect. The red-shift of the optical band gap with the particle size supported the quantum size effect. A broad photoluminescence band in the range of 350—750 nm can be detected in the annealed samples and the intensity was significantly enhanced after the thermal annealing. The luminescence peak energy was kept at 390 nm which was independent of the particle size. This luminescence band can be ascribed to the luminescence center associated with the oxygen vacancies on the SnO2 particle surface.

Synthesis and optical properties of SnO2 nanorods

Zn-Cu-codoped SnO2 Nanoparticles: Structural, Optical, and Ferromagnetic Behaviors

Structural, Luminescent, and NO2 Sensing Properties of SnO2-core/V2O5-shell Nanorods

Synthesis and characterization of SnO2 nanorods

Sub-2 Nm SnO2 Nanocrystals: A Reduction/oxidation Chemical Reaction Synthesis and Optical Properties

Growth Process, Photoluminescence Property and Photocatalytic Activity of SnO<sub>2</sub> Nanorods

Synthesis and Growth Mechanism Study of SnO2 Micro/nanomaterials

Layer-by-layer synthesis of γ-Fe2O3@SnO2@C porous core-shell nanorods with high reversible capacity in lithium-ion batteries.

Large-scale synthesis of rutile SnO2 nanorods

Synthesis and Characterization of Rutile SnO2 Nanorods

Synthesis,structures and Luminescence Properties of SnO2 Nanoparticles

Structural and Luminescent Properties of ZnO Nanorods and ZnO/ZnS Nanocomposites

Preparation and Characterization of SnO2 Nanorods by Thermal Decomposition of SnC2O4 Precursor

Preparation of SnO2 nanorods by annealing SnO2 powder in NaCl flux

Hydrothermal synthesis of SnO2 nanoflower arrays and their optical properties

Low‐dose inhaled budesonide once or twice daily for 27 months in children with mild asthma

Production of SnO2 nanorods by redox reaction

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Li2SnO3 branched nano- and microstructures with intense and broadband white-light emission

Synthesis And Magnetic Properties Of Zn1-Xcoxo Nanorods

Single Crystalline SnO2 Nanowires Obtained from Heat-Treated SnO2 and C Mixture and Their Electrochemical Properties