Abstract:ZnO nanorods were grown on ITO substrates with different concentration of electrolyte by electrodeposition method. Microstructure, surface topography, photoluminescence Spectra, Raman spectra and water contact angle of the thin films were measured. The XRD results show all samples are hexagonal wurtzite and the intensity of diffraction peaks at (002) preferred orientation are strengthen as electrolyte concentration increase from 0.005 to 0.03 M. As the concentration increases, the average diameter, density and inclination of the ZnO nanorods increased. Room temperature photoluminescence spectras of the ZnO nanorods show a narrow UV band centering at about 377 nm and broad visible emissions around 600 nm and the UV peak intensity revealed a remarkable decreased. Raman spectras exhibit three peaks which are located at 439 cm(-1), 562 cm(-1) and 1095 cm(-1). All samples change from hydrophobicity to hydrophilic after one hour ultraviolet (UV) irradiation. (C) The Author(s) 2015. Published by ECS. This is an open access article distributed under the terms of the Creative Commons Attribution Non-Commercial No Derivatives 4.0 License (CC BY-NC-ND, http://creativecommons.org/licenses/by-nc-nd/4.0/), which permits non-commercial reuse, distribution, and reproduction in any medium, provided the original work is not changed in any way and is properly cited. For permission for commercial reuse, please email: oa@electrochem.org. All rights reserved.

Production of SnO2 nanorods by redox reaction

Preparation of SnO2 nanorods by annealing SnO2 powder in NaCl flux

Synthesis and characterization of SnO2 nanorods

Large-scale synthesis of rutile SnO2 nanorods

Facile synthesis of Zn 1−x Cu x O nanorods with a very broad visible band

Effects of Electrodeposition Electrolyte Concentration on Microstructure, Optical Properties and Wettability of ZnO Nanorods

Sub-2 Nm SnO2 Nanocrystals: A Reduction/oxidation Chemical Reaction Synthesis and Optical Properties

Synthesis and Characterization of Rutile SnO2 Nanorods

Synthesis and Growth Mechanism Study of SnO2 Micro/nanomaterials

Preparation and Characterization of SnO2 Nanorods by Thermal Decomposition of SnC2O4 Precursor

Preparation and photoluminescence of ZnO nanorods

Growth Process, Photoluminescence Property and Photocatalytic Activity of SnO<sub>2</sub> Nanorods

Synthesis of NiO nanorods by a novel simple precursor thermal decomposition approach

A simple and novel route for the preparation of ZnO nanorods

Low-Temperature Fabrication of Highly Crystalline SnO2 Nanorods

Synthesis and Characterization of Zirconia Nanorods

Nanostructured ZnO: from Monodisperse Nanoparticles to Nanorods

Preparation and characterization of ZnO nanorods

Synthesis of ZnS nanorods by annealing precursor ZnS nanoparticles in NaCl flux

Preparation and characterization of bat-like ZnO micro- and nanorods by adjusting oxygen flux

[The Study on the Growth Process of ZnO Nanorods].