Abstract:The thermal oxidation of molten SnCl2 leads to the formation of SnO2 nanocrystals of less than 50 nm in diameter at 600 degrees C. These nanoparticles grow to large crystals with sizes of up to 10 um by increasing the heat-treatment temperature to 800 degrees C. The excessive growth of SnO2 crystals can be prevented by the introduction of polyethylene terephthalate (PET) and inorganic salts, through which SnO2@carbon nanocomposites could be prepared in a fast and clean way. Increasing the heat-treatment temperature from 600 to 800 degrees C leads to the enhancement of the crystalline quality of SnO2 present in the nanocomposites, while the excessive crystal growth at high temperatures is prevented. A large number of highly-crystalline SnO2 nanocrystals with sizes of less than 5 nm embedded in carbon substrate could be detected in the nanocomposite material prepared at 800 degrees C. The prepared sample exhibits an interesting combination of dye adsorption, with the capacity of 63 Mg-dye/g(nano-composite), as well as photocatalytic performance under normal sunlight irradiation toward the removal of methylene blue. This article suggests a clean and fast strategy for the preparation of highly crystalline SnO2 amorphous carbon nanocomposites.

Preparation of SnO2 nanorods by annealing SnO2 powder in NaCl flux

Large-scale synthesis of rutile SnO2 nanorods

Synthesis and characterization of SnO2 nanorods

Production of SnO2 nanorods by redox reaction

Synthesis and Characterization of Rutile SnO2 Nanorods

Synthesis of ZnS nanorods by annealing precursor ZnS nanoparticles in NaCl flux

Preparation and Characterization of SnO2 Nanorods by Thermal Decomposition of SnC2O4 Precursor

Growth Process, Photoluminescence Property and Photocatalytic Activity of SnO<sub>2</sub> Nanorods

Sub-2 Nm SnO2 Nanocrystals: A Reduction/oxidation Chemical Reaction Synthesis and Optical Properties

Hydrothermal Synthesis of Rutile-structured SnO_2 Nanorod Crystals

Synthesis of NiO nanorods by a novel simple precursor thermal decomposition approach

Fast and Clean Preparation of Highly Crystalline SnO2 Nanoparticles Incorporated in Amorphous Carbon, and Its Dye Removal Performance

A simple and novel route for the preparation of ZnO nanorods

Preparation and photoluminescence of ZnO nanorods

Low-Temperature Fabrication of Highly Crystalline SnO2 Nanorods

Synthesis and Raman Scattering Study of Rutile Sno2 Nanowires

Growth of SnO2 nanowires with uniform branched structures

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Preparation and characterization of NiO nanorods by thermal decomposition of NiC2O4 precursor

Preparation and characterization of ZnO nanorods

Nanostructured ZnO: from Monodisperse Nanoparticles to Nanorods