Abstract:Al0.5CrCoFeNi high entropy alloy was prepared by vacuum arc melting in a high-purity argon atmosphere. The oxidation experiments were performed at the temperatures of 800, 900, 1000 and 1100 degrees C for 100 h, and the corresponding oxidation kinetics curves have been tested. The structure and morphology of oxide layer have been studied by adopting the analytical methods, such as XRD and SEM. The results show that oxide films forming at 800 degrees C and 900 degrees C were complete and compact, and have excellent oxidation resistance. However, the oxide films forming at 1000 degrees C and 1100 degrees C become much thicker and have a large number of cracks and holes, which result into poor oxidation resistance. Interface reactions played a mast role at the early stage of oxidation, but with the growing of oxide films, diffusion process played an important role increasingly, and became the control factor for continue oxidizing. Then, one or multiple kinds of alloy elements oxide precipitated on the surface, and formed inner spinel oxide of NiCr2O4, CoCr2O4 and Fe(Cr,Al)(2)O-4. During the high temperature oxidation process, N-2 will react with Al to generate AIN particles. The further oxidizing has made AIN particles oxidized again and N-2 escaped. Finally, the holes with the AIN particles shape have appeared.

High-temperature oxidation behavior of minor Hf doped NiAl alloy in dry and humid atmospheres

Thermal Oxidation Behaviour of Ti6Al7Nb and Ti6Al4V Alloys

Long-term oxidation behavior for Ni-5Al coating in Air-H 2 O at 650 °C

Oxidation behavior of high Hf nickel-based superalloy in air at 900, 1000 and 1100°C

Effect of Hf Addition on Initial Microstructure of (ni, Pt)Al Coating and Inhibiting the Detrimental Sulfur During High Temperature Exposure at 1150 °C

Effect of Y-doping on the microstructural evolution and oxidation resistance of NiAlHf coatings at 1200 °C

Effect of Al content on the oxidation behavior of NiCoCrAlYHf alloys at 1100°C

Effect of Hf as oxygen vacancy formation inhibitor on the oxidation behavior of Ni-28 W alloy

Co-doping Effect of Hf and Y on Improving Cyclic Oxidation Behavior of (ni,pt)al Coating at 1150 °C

High-Temperature Oxidation Behavior of FeCoCrNi+(Cu/Al)-Based High-Entropy Alloys in Humid Air

Influence of water vapour on the oxidation behaviour of TiAl based multielement alloys

Mechanical Properties and Oxidation Characteristics of TiNiAl(Nb) Intermetallics

A comparative study on the oxidation behavior of Y-, Hf- and YHf-doped NiCoCrAl alloys: effect of reactive elements

Microstructure and oxidation behavior of the Y/Ta/Hf co-doped AlCoCrFeNi high-entropy alloys in air at 1100 °C

Effect of Al content on the oxidation behavior of Y/Hf-doped AlCoCrFeNi high-entropy alloy

Synergistic Effect of Pt and Hf on the Early-Stage Oxidation Behaviour of NiAl Coating at 1000°C

Effect of Al2O3 scales from pre-oxidation on the microstructural evolution and phase transition of NiAlHf coatings at 1200 °C

Unveiling the precipitation-induced high-temperature oxidation behavior in a Ni-Al-Y alloy

Effect of aluminum addition on microstructure, mechanical properties and high temperature tribological properties of nickel-rich NiTi alloy

Oxidation behavior of NiAl nanoparticles prepared by hydrogen plasma–metal reaction

High Temperature Oxidation Behavior of Al0.5CrCoFeNi High Entropy Alloy