Abstract:Two kinds of adsorbates—L-ascorbic acid and NaOH were used separately to investigate the effects of adsorbate distribution between ethanol bulk phase and the phase of water-rich layer adsorbed by the surface of SiO2 particles on the preparation of silver nanoparticles on SiO2 particles. When the adsorbate L-ascorbic acid was used, L-ascorbic distributes mainly in the ethanol bulk phase and thus the Ag particle generating reaction will take place in the ethanol bulk phase with the generated Ag particle size of about 18 nm. When the adsorbate NaOH was used, NaOH distributes mainly in the phase of water-rich layer adsorbed on the surface of SiO2 particles and thus the Ag particles generate in the water-rich adsorption layer with particle size of only about 5.4 nm. Since the NaOH concentration effects its distribution between the two phases of ethanol bulk phase and water-rich adsorption layer, the further experiments with changing NaOH concentration in the reaction system from 0.0170 to 0.404 g·L-1 were conducted. Results show that when concentration of NaOH in the system was increased from 0.0170 to 0.135 g·L-1, the NaOH concentration in the water-rich adsorption layer increases with the increase of NaOH concentration in the system gradually, which causes the generation of Ag grains gradually centralizes in the adsorption layer with the grain size decreases from 8 nm to 5 nm, and the Ag particles generated cover the SiO2 more uniformly. When NaOH concentration in the system was increased from 0.135 to 0.404 g·L-1, the amount of NaOH in the system is over the maximum NaOH capacity that can be contained in the water-rich adsorption layer and thus the NaOH concentration in ethanol bulk phase will increase to the limit, above which, the Ag generating reaction rate in it will accelerate more quickly than that in the water-rich adsorption layer, which causes the main generation zone of silver nanoparticles moves from water-rich adsorption layer to ethanol bulk phase gradually, and at the same time, the generated Ag grain size will increase from 5 nm to 12 nm.

The Formation Mechanism of Ag/SBA-15 Nanocomposites Prepared Via In-Situ Ph-Adjusting Method.

In Situ Formation of Silver Nanoparticles Hosted in Mesoporous Sba-15

Studies on Preparation of Ag/SiO2 Nanocomposite and Its Electrical Properties

Synthesis of Ag/SiO2 nanocomposite material by adsorption phase nanoreactor technique

Effect of adsorption layer on preparation process of Ag/SiO2 nanocomposite materials

Preparation of CuO-Ag/SiO2 nano-composites via adsorption phase reaction technique

Effect of Interphase Distribution of Reactants in Binary Liquids on Preparation of Silver Nanoparticles on Silica Particles

Effect of pH on the structural characteristics of in situ synthesized Ni-incorporated SBA-15 magnetic composites

Synthesis of Heteroatom Substituted SBA-15 by the “pH-Adjusting” Method

Synthesis of the Supported Au Polystyrene/poly (acrylic acid) Composite Microspheres and Their pH Regulated Performance

Morphology and Composition Controlled Synthesis of Flower-Like Silver Nanostructures.

Sol-gel Preparation of Ag-silica Nanocomposite with High Electrical Conductivity

Characterization of sonochemically prepared silver–silica monolithic mesoporous nanocomposite

Preparation and Characterization of Ag Nanoparticles Embedded in Hierarchically Porous Monolithic Silica

Al/SBA-15 Mesoporous Material: A Study of pH Influence over Aluminum Insertion into the Framework

Growth of PbS architectural nanostructures catalyzed by silver nanocrystal seeds

Synthesis, Characterization and Optical Properties of CdS Nanoparticles Confined in SBA-15

In Situ Coating Metal Oxide on SBA-15 in One-Pot Synthesis

In Situ Preparation and Inhibitory Activity of Hydroxyapatite/Silver Nanocomposite

Controllable Synthesis of Mesoporous SBA-15 Using H2SO4