Abstract:Two kinds of adsorbates—L-ascorbic acid and NaOH were used separately to investigate the effects of adsorbate distribution between ethanol bulk phase and the phase of water-rich layer adsorbed by the surface of SiO2 particles on the preparation of silver nanoparticles on SiO2 particles. When the adsorbate L-ascorbic acid was used, L-ascorbic distributes mainly in the ethanol bulk phase and thus the Ag particle generating reaction will take place in the ethanol bulk phase with the generated Ag particle size of about 18 nm. When the adsorbate NaOH was used, NaOH distributes mainly in the phase of water-rich layer adsorbed on the surface of SiO2 particles and thus the Ag particles generate in the water-rich adsorption layer with particle size of only about 5.4 nm. Since the NaOH concentration effects its distribution between the two phases of ethanol bulk phase and water-rich adsorption layer, the further experiments with changing NaOH concentration in the reaction system from 0.0170 to 0.404 g·L-1 were conducted. Results show that when concentration of NaOH in the system was increased from 0.0170 to 0.135 g·L-1, the NaOH concentration in the water-rich adsorption layer increases with the increase of NaOH concentration in the system gradually, which causes the generation of Ag grains gradually centralizes in the adsorption layer with the grain size decreases from 8 nm to 5 nm, and the Ag particles generated cover the SiO2 more uniformly. When NaOH concentration in the system was increased from 0.135 to 0.404 g·L-1, the amount of NaOH in the system is over the maximum NaOH capacity that can be contained in the water-rich adsorption layer and thus the NaOH concentration in ethanol bulk phase will increase to the limit, above which, the Ag generating reaction rate in it will accelerate more quickly than that in the water-rich adsorption layer, which causes the main generation zone of silver nanoparticles moves from water-rich adsorption layer to ethanol bulk phase gradually, and at the same time, the generated Ag grain size will increase from 5 nm to 12 nm.

Characterization of sonochemically prepared silver–silica monolithic mesoporous nanocomposite

Synthesis of Ag/SiO2 nanocomposite material by adsorption phase nanoreactor technique

STUDY OF PREPARATION AND PROPERTIES OF NANO-SCALE AgI- POROUS SiO2 COMPOSITES

Preparation and Characterization of Ag Nanoparticles Embedded in Hierarchically Porous Monolithic Silica

Studies on Preparation of Ag/SiO2 Nanocomposite and Its Electrical Properties

Preparation of CuO-Ag/SiO2 nano-composites via adsorption phase reaction technique

Effect of adsorption layer on preparation process of Ag/SiO2 nanocomposite materials

Fabrication and characterization of silver core and porous silica shell nanocomposite particles

Effect of Interphase Distribution of Reactants in Binary Liquids on Preparation of Silver Nanoparticles on Silica Particles

Sol-gel Preparation of Ag-silica Nanocomposite with High Electrical Conductivity

Preparation and Characterization of Ag Nanoshell on SiO2 Spheres via Electroless Plating Technique in Acidic Conditions

Preparation and Characterization of Ag Nanoshell on SiO/sub 2/ Spheres via Electroless Plating Technique in Acidic Conditions

Facile Preparation of Silver Nanoparticles Homogeneously Immobilized in Hierarchically Monolithic Silica Using Ethylene Glycol As Reductant

Preparation of Silver Nanoshells on Silica Particles by a Simple Two-step Process

Synthesis and Characterization of Silica–silver Core–shell Composite Particles with Uniform Thin Silver Layers

Toward Monodispersed Silver Nanoparticles with Unusual Thermal Stability.

Indirect Fabrication of Ag Nanoparticle-Immobilized Hollow Silica Composite Particles and Their Catalysis

The preparation of silver nanoparticles on silica microspheres as SERS substrates

Facile Fabrication Method And Characterization Of Hollow Ag/Sio2 Double-Shelled Spheres

Novel preparation and near-infrared photoluminescence of uniform core-shell silver sulfide nanoparticle@mesoporous silica nanospheres