Preparation and Characterization of Ag Nanoshell on SiO2 Spheres via Electroless Plating Technique in Acidic Conditions

Kan-Sen Chou,Yu-Chieh Lu

DOI: https://doi.org/10.1109/ICONN.2006.340546

2006-01-01

Abstract:Nanoshells composed of close-packed silver nanocrystals have been fabricated on silica spheres by electroless plating technique. By controlling the solution's pH in acidic condition during the synthesis of SiO2-Ag core-shell particles, the homogeneous deposition resulted in thin and uniform silver shells. The deposition process was carried out in two steps: the first step was the modification of silica surface with the adsorption of 3-(2-Aminoethylamino) propyltrimethoxysilane (APTS), and the second step was the deposition of silver by reacting AgNO3, dextrose and acetic acid. The reaction was performed at high temperature to accelerate the deposition process. The resulting silica-silver core-shell colloids were characterized with XRD, high-resolution TEM and SEM, and UV-visible spectroscopy. It was found that the core-shell structures, such as shell thickness and shell continuity, influenced significantly the absorption spectra. Moreover, the thin shell at about 3nm was very sensitive to the temperature, and the core-shell structure collapsed after 200 C treatment for 30 minutes probably due to the coalescence between adjacent Ag particles. When heating temperature was over than 300 C the Ag particles began to move and leave the SiO2 surface, causing the corlour of particles to fade gradually