Al/SBA-15 Mesoporous Material: A Study of pH Influence over Aluminum Insertion into the Framework

Francisco Gustavo Hayala Silveira Pinto,Vinícius Patrício da Silva Caldeira,Jhonny Villarroel-Rocha,Karim Sapag,Sibele Berenice Castellã Pergher,Anne Gabriella Dias Santos

DOI: https://doi.org/10.3390/nano14020208

IF: 5.3

2024-01-17

Nanomaterials

Abstract:Herein, ordered mesoporous materials like SBA-15 and Al/SBA-15 were prepared using the pH adjustment method. Thus, these materials were developed in different pH of synthesis, from the pH adjustment method using a KCl/HCl solution and varying the Si/Al molar ratio (5, 25, and 75). All the ordered mesoporous materials were characterized by FRX, 27Al NMR, SEM, XRD, N2 adsorption/desorption, and CO2 adsorption. From the applied method, it was possible to obtain SBA-15 and Al/SBA-15 with high mesoscopic ordering based on the XRD patterns, independent of the pH employed. From the chemical composition, the insertion of higher amounts of Al into the synthesis caused a progressive improvement in the structural and textural properties of the ordered mesoporous materials. Thus, the chosen synthesis conditions can lead to different aluminum coordination (tetrahedral and octahedral), which gives these materials a greater potential to be applied. The presence of Al in high amounts provides material with the ability to form micropores. Finally, the proposed method proved to be innovative; low-cost; less aggressive to the environment, with efficient insertion of aluminum in the framework of SBA-15 mesoporous material; and practical, based on only one step.

materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology,chemistry

What problem does this paper attempt to address?

The paper attempts to address the issue of efficiently incorporating aluminum (Al) into SBA-15 mesoporous materials. Specifically, the researchers aim to optimize the insertion of aluminum into the SBA-15 framework by adjusting the pH value during the synthesis process, thereby enhancing the material's structure and performance. The main focus areas include:

1. **Efficiency of Aluminum Insertion**: By controlling the pH value, the researchers hope to improve the efficiency of aluminum insertion into the SBA-15 framework. In highly acidic environments, aluminum ions tend to dissociate, making insertion difficult.

2. **Structure and Performance of the Material**: The researchers aim to evaluate the impact of aluminum insertion on the structure and performance of SBA-15 materials under different Si/Al molar ratios and pH conditions, particularly focusing on properties such as orderliness, specific surface area, and pore distribution.

3. **Coordination Environment of Aluminum**: The researchers also intend to analyze the coordination environment (tetrahedral and octahedral) of aluminum in the SBA-15 framework using techniques such as nuclear magnetic resonance (27Al MAS NMR) to understand the effect of different pH values on the mode of aluminum insertion.

4. **Application Potential**: The ultimate goal is to develop a simple, low-cost, and environmentally friendly synthesis method that endows SBA-15 materials with higher acidic sites and better catalytic performance, thereby expanding their applications in fields such as catalysis and adsorption.

Through these studies, the paper aims to provide new synthesis strategies and scientific basis for preparing high-performance Al/SBA-15 mesoporous materials.