Abstract:ZrB2-20 vol.% SiC-10 vol.% h-BN (particles) ceramic composites (ZSB) were fabricated by hot pressing under inert gas protected. ZSB samples with mean size 75 × 55 × 40 mm(3) were heated using current heating method and then cooled down to low temperature by circulating water. ZSB samples repeatedly went through thermal shock with 10-50 times under various conditions, respectively. Diverse effects on residual strength of ZSB at different experiment conditions (temperatures, thermal shock times, and heating rates) were investigated. The test results indicated that the residual strength of specimen materials all reached the maximum while the temperature was 1600 °C and thermal shock number was less than 50 times. Because ZSB samples could not stand the extremely serious hyperoxidation at very high temperature (1800 °C), the residual strength of samples decreased sharply. At 1600 °C, when the thermal shock times was 20, ZSB samples' residual strength reached the maximum, but it decreased to the lowest point while the thermal shock times was 30. So we argued that the sensitive thermal shock number was 30. Finally, we analyzed the influences on samples residual strength generated by different heating rates at the same temperature and thermal shock number; the results showed that when heating rate was equal to cooling rate, the residual strength of specimen materials reached the maximum.

Effect of high temperature heat treatment on ZrB2-SiC composites added with Yb2O3

Microstructural evolution of ZrB2–MoSi2 composites during heat treatment

Effect of sintering temperature and holding time on the microstructure and mechanical properties of ZrB2–SiCw composites

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride

Effects of ZrB2 on Mechanical Properties of Al2O3-ZrB2-SiC Composite Ceramics at Room Temperature

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Secondary crystalline phases and mechanical properties of heat-treated Si3N4

High-performance B4C-YB4 composites fabricated with Y2O3 additive via hot-pressing sintering

Effect of repeated thermal shock on mechanical properties of ZrB2-SiC-BN ceramic composites

Mechanical Properties of Short Carbon Fiber Reinforced ZrB2–SiC Ceramic Matrix Composites

High temperature oxidation resistance of hot-pressed h-BN/ZrO 2 composites

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Effect of Carbon Impurities on Hot-Pressed Zrb2-Sic Ceramics

Effect of thermal treatment at high temperature on phase stability and transformation of Yb2O3 and Y2O3 co-doped ZrO2 ceramics

High‐temperature tensile strength and fracture behavior of ZrB2‐SiC‐graphite composite

The fiber structure evolution and performance changes of SiC–ZrC fibers after 1600 °C heat treatment

Effect of SiC Content on the Ablation and Oxidation Behavior of ZrB2-Based Ultra High Temperature Ceramic Composites

Comparison of ZrB2–SiC Ceramics with Yb2O3 Additive Prepared by Hot Pressing and Spark Plasma Sintering

High-Temperature Oxidation Resistance of ZrB2-SiC Ceramic Composites Prepared by Reactive Hot Pressing

Effect of heat treatment on the microstructure and ablation performance of C/C–SiC composites containing ZrSi 2 –Si

High-temperature deformation of ZrB2 ceramics with WC additive in four-point bending