Influence of milling time on the synthesis, microstructure and mechanical properties of ZrB2SiCZrO2f ceramic composites

Jia Lin,Xinghong Zhang,Wenbo Han,Di Sun
DOI: https://doi.org/10.1016/j.ceramint.2012.11.003
IF: 5.532
2013-01-01
Ceramics International
Abstract:Zirconium diboride toughened by silicon carbide and zirconia fiber (ZrB2SiCZrO2f) was prepared by using planetary ball mill and the effect of milling time was investigated. The results showed that both the length of fiber and particle size of ZrB2SiC-matrix were reduced as the ball milling time increased. When milling time varied from 8h to 12h, the accumulated fibers and agglomerated particles were observed. The production of a homogeneous ceramic could be successfully achieved by using a combination of 20h milling time and hot-pressing at 1850°C for 60min under a uniaxial load of 30MPa. The optimal flexural strength and fracture toughness of the hot-pressed ZrB2SiCZrO2f ceramics reached 1084MPa and 6.8MPam1/2, respectively. The main toughening mechanisms were fiber debonding, fiber pull-out and transformation toughening. The results indicated that the ball milling technique was proposed as a potential and simple method to obtain usable quantities of ZrB2SiCZrO2f ceramic.
What problem does this paper attempt to address?