Abstract:The highly filled isotropic polyurethane (PU) elastomer with a magnetorheological (MR) effect was prepared through an in situ polycondensation method. The carbonyl iron particles were treated by coupling agents and then the dispersions of polyol/carbonyl iron particles was prepared by a ball milling process. The dispersion problem of magnetizable particles at a high content in PU matrix was tried to overcome by the combination of surface modification, ball milling, and in situ polymerization. The microstructure and properties of the composite were examined in detail. With increasing the content of carbonyl iron particles, the degree of phase separation of PU increased and the glass transition temperature (T-g) of PU soft segment decreased. Highly filled carbonyl iron particles led to the decrease in the thermal stability of PU matrix, especially in the heating air atmosphere. The MR effect appeared when the content of carbonyl iron particles was higher than 50 wt %, and became relatively pronounced at a 70 wt % of carbonyl iron content. The mechanical properties of PU MR elastomers were deteriorated significantly at a high content of carbonyl iron. Surface modification of carbonyl iron particles can improve the mechanical properties to some extent; however, it was also found that surface modification led to a decrease in the MR effect because of the improved interfacial adhesion. The MR test showed that the maximum absolute MR effect and relative MR effect of PU composite were similar to 0.31 MPa and similar to 8.1% at 1 Hz and 400 mT with 70 wt % of carbonyl iron, respectively. (C) 2009 Wiley Periodicals, Inc. J Appl Polym Sci 114: 901-910, 2009

Smart Polyurethane Foam with Magnetic Field Controlled Modulus and Anisotropic Compression Property

Anisotropic polyurethane magnetorheological elastomer prepared through in situ polycondensation under a magnetic field

Preparation and characterization of isotropic polyurethane magnetorheological elastomer through in situ polymerization

Improving the Magnetorheological Properties of Polyurethane Magnetorheological Elastomer Through Plasticization

Effect of the Carbonyl Iron Particles on Acoustic Absorption Properties of Magnetic Polyurethane Foam

Stretchable Polyurethane Sponge Reinforced Magnetorheological Material with Enhanced Mechanical Properties

Study on the properties of magnetorheological gel based on polyurethane

A high-performance magnetorheological material: Preparation, characterization and magnetic-mechanic coupling properties

Study on characteristic parameters identification and low frequency sound absorption performance of polyurethane foam filled with carbonyl iron particles

New magnetorheological elastomers based on polyurethane/Si-rubber hybrid

MAGNETORHEOLOGICAL ELASTOMERS BASED ON POLYURETHANE/<font>SI</font>-RUBBER HYBRID

Micro topography and low frequency sound absorption performance of magnetic polyurethane foam

Influence of Polyurethane Properties on Mechanical Performances of Magnetorheological Elastomers

Polystyrene/magnetite Hybrid Foams Prepared Via 60 Co Γ-Ray Radiation of High Internal Phase Emulsions

Poly(methyl Methacrylate)‐coated Carbonyl Iron Particles and Their Magnetorheological Characteristics

olymer composite with excellent shear sti ff ening performance and magnetorheological e ff ect

The effect of external magnetic fields on the pore structure of polyurethane foams loaded with magnetic microparticles

Physically crosslinked poly(vinyl alcohol) hydrogels with magnetic field controlled modulus

Magnetically-sensitive Shape Memory Polyurethane Composites Crosslinked with Multi-Walled Carbon Nanotubes

Soft Magnetorheological Polymer Gels with Controllable Rheological Properties

Influence of particles size and concentration of carbonyl iron powder on magnetorheological properties of silicone rubber-based magnetorheological elastomer